Compressive strength evaluation of thin occlusal veneers from different CAD/CAM materials, before and after acidic saliva exposure

Compressive Strength Testing of Glass-Fibre-Reinforced Tooth Crown Tissues After Endodontic Treatment

The objective of this study was to compare the effects of using short and continuous fibres for repairing compression-induced tooth crown damage. Human teeth were used for the study. They were upper medial incisors and maxillary first premolars lost due to periodontal causes. The teeth were divided into two groups with Hahnenkratt and short glass fibres. Teeth compressive strength tests were carried out. Then micro-CT imaging of the teeth and their fractures obtained after compression was performed. The teeth restored with Hahnenkratt's glass fibre posts showed higher compressive strength than the teeth restored using the EverX Posterior material. The tooth's most weakened and sensitive point after endodontic treatment was the cervical area of the tooth. All cracks were parallel to the root canal.

Influence of Storing Composite Filling Materials in a Low-pH Artificial Saliva on Their Mechanical Properties-An In Vitro Study

Restorative composites are subjected to various influences in the oral cavity environment, such as high or low temperatures, the mechanical force generated during mastication, colonization of various microorganisms, and low pH, which may result from ingested food and the influence of microbial flora. This study aimed to investigate the effect of a recently developed commercial artificial saliva (pH = 4, highly acidic) on 17 commercially available restorative materials. After polymerization, the samples were stored in an artificial solution for 3 and 60 days and subjected to crushing resistance and flexural strength tests. The surface additions of the materials were examined in terms of the shapes and sizes of the fillers and elemental composition. When stored in an acidic environment, the resistance of the composite materials was reduced by 2-12%. Larger compressive and flexural strength resistance values were observed for composites that could be bonded to microfilled materials (invented before 2000). This may result from the filler structure taking an irregular form, which results in a faster hydrolysis of silane bonds. All composite materials meet the standard requirements when stored for a long period in an acidic environment. However, storage of the materials in an acid environment has a destructive impact on the materials' properties.

The Biological Activity of Fragmented Computer-Aided Design/Manufacturing Dental Materials before and after Exposure to Acidic Environment

Three ceramic and composite computer-aided design/computer-aided manufacturing (CAD/CAM) materials from different manufacturers (Cerasmart (CS)-nanoceramic resin; Straumann Nice (SN)-glass ceramic and Tetric CAD (TC)-composite resin) were tested to investigate the biocompatibility and sustainability on human fibroblasts and keratinocytes cells. Each type of CAD/CAM blocks restorative materials with fine and rough surfaces was exposed to an acidic environment for one month. After that, various powders were obtained by milling. In parallel, powders were also prepared from each restorative material, which were not exposed to the acidic environment. The cytotoxic effects were investigated by means of MTT and LDH assays, as well as nitric oxide production on two human normal cell lines, namely, fibroblasts (BJ) and keratinocytes (HaCaT). In addition, the degree of adhesion of fibroblast cells to each CAD/CAM material was evaluated by scanning electron microscopy (SEM). The results showed that the two samples that were exposed to an acidic environment (CS and SN) induced a reduction of mitochondrial activity and plasma membrane damage as regards the fibroblast cells. A similar effect was observed in TC_fine-exposed material, which seemed to induce necrosis at the tested concentration of 1 mg/mL. No oxidative stress was observed in fibroblasts and keratinocytes treated with the CAD/CAM materials. Regarding the adhesion degree, it was found that the fibroblasts adhere to all the occlusal veneers tested, with the mention that the CS and SN materials have a weaker adhesion with fewer cytoplasmic extensions than TC material. With all of this considered, the CAD/CAM restorative materials tested are biocompatible and represent support for the attachment and dispersion of cells.