Oxidative Dehydrogenation of n-Butene to 1,3-Butadiene over Sulfated ZnFe2O4 Catalyst

Oxidative Dehydrogenation of 1-Butene to 1,3-Butadiene Over Metal Ferrite Catalysts

The oxidative dehydrogenation (ODH) of 1-butene to 1,3-butadiene was studied over a series of AFe2O4 catalysts, where A = Zn, Mn, Ni, Cu, Mg and Fe. The catalysts were characterised by XPS, EPR spectroscopy, BET surface area analysis, Raman spectroscopy and XRD. All the ferrites were active for ODH and gave an order of activity after 80 h on-stream of ZnFe2O4 > NiFe2O4 > MnFe2O4 > MgFe2O4 > CuFe2O4 > FeFe2O4. All catalysts lost significant surface area (up to ~ 80%) under reaction conditions of 0.75:1:15 oxygen:1-butene:steam with an overall GHSV of 10,050 h−1 at 693 K. Fe3O4 was unstable under reaction conditions and was converted to Fe2O3, which showed very low activity. Nickel ferrite was the only material that gave carbon dioxide as a significant product, all others were selective to 1,3-butadiene. Zinc ferrite gave a steady-state yield of 1,3-butadiene of ~ 80%. Inversion parameters were determined for the ferrites from XPS and a correlation was obtained between 1,3-butadiene yield and inversion parameter, indicating that Fe3+ in an octahedral hole is a key species in the mechanism of oxidative dehydrogenation. Butene isomerisation and ODH were shown to occur on different sites.

Temperature-induced deactivation mechanism of ZnFe2O4 for oxidative dehydrogenation of 1-butene

This paper describes the observation of an irregular decrease in 1-butene conversion during oxidative dehydrogenation over ZnFe₂O₄ in the production of 1,3-butadiene upon increasing the reaction temperature above 400 °C.