Novel Mn–Cu-Containing CeO2 Nanopolyhedra for the Oxidation of CO and Diesel Soot: Effect of Dopants on the Nanostructure and Catalytic Activity

Hydroxyls on CeO2 Support Promoting CuO/CeO2 Catalyst for Efficient CO Oxidation and NO Reduction by CO

Transition metal catalysts, such as copper oxide, are more attractive alternatives to noble metal catalysts for emission control due to their higher abundance, lower cost, and excellent catalytic activity. In this study, we report the preparation and application of a novel CuO/CeO2 catalyst using a hydroxyl-rich Ce(OH)x support for CO oxidation and NO reduction by CO. Compared to the catalyst prepared from a regular CeO2 support, the new CuO/CeO2 catalyst prepared from the OH-rich Ce(OH)x (CuO/CeO2-OH) showed significantly higher catalytic activity under different testing conditions. The effect of OH species in the CeO2 support on the catalytic performance and physicochemical properties of the CuO/CeO2 catalyst was characterized in detail. It is demonstrated that the abundant OH species enhanced the CuOx dispersion on CeO2, increased the CuOx-CeO2 interfaces and surface defects, promoted the oxygen activation and mobility, and boosted the NO adsorption and dissociation on CuO/CeO2-OH, thus contributing to its superior catalytic activity for both CO oxidation and NO reduction by CO. These results suggest that the OH-rich Ce(OH)x is a superior support for the preparation of highly efficient metal catalysts for different applications.

Mesoporous Hollow Manganese Doped Ceria Nanoparticle for Effectively Prevention of Hepatic Ischemia Reperfusion Injury

Introduction

Hepatic ischemia-reperfusion injury (HIRI) is the main reason for liver dysfunction or failure after liver resection and liver transplantation. As excess accumulation of reactive oxygen species (ROS) is the leading factor, ceria nanoparticle, a cyclic reversible antioxidant, is an excellent candidate for HIRI.

Methods

Manganese doped mesoporous hollow ceria nanoparticles (MnO_x-CeO₂ NPs) were prepared, and the physicochemical characteristics, such as particle size, morphology, microstructure, etc. were elucidated. The in vivo safety and liver targeting effect were examined after i.v. injection. The anti-HIRI was determined by a mouse HIRI model.

Results

MnO_x-CeO₂ NPs with 0.40% Mn doped exhibited the strongest ROS-scavenging capability, which may due to the increased specific surface area and surface oxygen concentration. The nanoparticles accumulated in the liver after i.v. injection and exhibited good biocompatibility. In the HIRI mice model, MnO_x-CeO₂ NPs significantly reduced the serum ALT and AST level, decreased the MDA level and increased the SOD level in the liver, prevent pathological damages in the liver.

Conclusion

MnO_x-CeO₂ NPs were successfully prepared and it could significantly inhibit the HIRI after i.v. injection.

Soot Oxidation over γ-Al2O3-Supported Manganese-Based Binary Catalyst in a Dielectric Barrier Discharge Reactor

In this work, soot oxidation was conducted over a series of Mn-X/γ-Al2O3 (M = Ce, Co and Cu) binary catalysts in a dielectric barrier discharge reactor. The soot conversion in the plasma–catalytic system was in the order of Mn/γ-Al2O3 (57.7%) > Mn-Co/γ-Al2O3 (53.9%) > Mn-Ce/γ-Al2O3 (51.6%) > Mn-Cu/γ-Al2O3 (47.7%) during the 30 min soot oxidation process at 14 W and 150 °C. Meanwhile, the doping of Ce, Co and Cu slightly improved the CO2 selectivity of the process by 4.7% to 10.3% compared to soot oxidation over Mn/γ-Al2O3.It is worth to note that the order of CO2 selectivity was in the opposite order with soot oxidation rate. The effects of discharge power, oxygen content in the carrier gas and reaction temperature on plasma–catalytic soot oxidation was systematically analyzed. The catalyst characterizations, including N2 adsorption–desorption, X-ray diffraction, X-ray photoelectron spectroscopy, temperature-programmed reduction by H2 and temperature-programmed desorption of O2, were conducted to illustrate the reaction mechanisms of plasma–catalytic soot oxidation and reaction pathways.

Cerium-Copper Oxides Synthesized in a Multi-Inlet Vortex Reactor as Effective Nanocatalysts for CO and Ethene Oxidation Reactions

In this study, a set of CuCeOx catalysts was prepared via the coprecipitation method using a Multi-Inlet Vortex Reactor: the Cu wt.% content is 5, 10, 20, 30 and 60. Moreover, pure CeO2 and CuO were synthesized for comparison purposes. The physico-chemical properties of this set of samples were investigated by complementary techniques, e.g., XRD, N2 physisorption at −196 °C, Scanning Electron Microscopy, XPS, FT-IR, Raman spectroscopy and H2-TPR. Then, the CuCeOx catalysts were tested for the CO and ethene oxidation reactions. As a whole, all the prepared samples presented good catalytic performances towards the CO oxidation reaction (1000 ppm CO, 10 vol.% O2/N2): the most promising catalyst was the 20%CuCeOx (complete CO conversion at 125 °C), which exhibited a long-term thermal stability. Similarly, the oxidative activity of the catalysts were evaluated using a gaseous mixture containing 500 ppm C2H4, 10 vol.% O2/N2. Accordingly, for the ethene oxidation reaction, the 20%CuCeOx catalyst evidenced the best catalytic properties. The elevated catalytic activity towards CO and ethene oxidation was mainly ascribed to synergistic interactions between CeO2 and CuO phases, as well as to the high amount of surface-chemisorbed oxygen species and structural defects.

Catalytic Abatement of Volatile Organic Compounds and Soot over Manganese Oxide Catalysts

A set of manganese oxide catalysts was synthesized via two preparation techniques: solution combustion synthesis (Mn₃O₄/Mn₂O₃-SCS and Mn₂O₃-SCS) and sol-gel synthesis (Mn₂O₃-SG550 and Mn₂O₃-SG650). The physicochemical properties of the catalysts were studied by means of N₂-physisorption at −196 °C, X-ray powder diffraction, H₂ temperature-programmed reduction (H₂-TPR), soot-TPR, X-ray photoelectron spectroscopy (XPS) and field-emission scanning electron microscopy (FESEM). The high catalytic performance of the catalysts was verified in the oxidation of Volatile Organic Compounds (VOC) probe molecules (ethene and propene) and carbon soot in a temperature-programmed oxidation setup. The best catalytic performances in soot abatement were observed for the Mn₂O₃-SG550 and the Mn₃O₄/Mn₂O₃-SCS catalysts. The catalytic activity in VOC total oxidation was effectively correlated to the enhanced low-temperature reducibility of the catalysts and the abundant surface O_α-species. Likewise, low-temperature oxidation of soot in tight contact occurred over the Mn₂O₃-SG550 catalyst and was attributed to high amounts of surface O_α-species and better surface reducibility. For the soot oxidation in loose contact, the improved catalytic performance of the Mn₃O₄/Mn₂O₃-SCS catalyst was attributed to the beneficial effects of both the morphological structure that—like a filter—enhanced the capture of soot particles and to a probable high amount of surface acid-sites, which is characteristic of Mn₃O₄ catalysts.

Solvothermal Synthesis Routes to Substituted Cerium Dioxide Materials

We review the solution-based synthesis routes to cerium oxide materials where one or more elements are included in place of a proportion of the cerium, i.e., substitution of cerium is performed. The focus is on the solvothermal method, where reagents are heated above the boiling point of the solvent to induce crystallisation directly from the solution. This yields unusual compositions with crystal morphology often on the nanoscale. Chemical elements from all parts of the periodic table are considered, from transition metals to main group elements and the rare earths, including isovalent and aliovalent cations, and surveyed using the literature published in the past ten years. We illustrate the versatility of this synthesis method to allow the formation of functional materials with applications in contemporary applications such as heterogeneous catalysis, electrodes for solid oxide fuel cells, photocatalysis, luminescence and biomedicine. We pick out emerging trends towards control of crystal habit by use of non-aqueous solvents and solution additives and identify challenges still remaining, including in detailed structural characterisation, the understanding of crystallisation mechanisms and the scale-up of synthesis.

Synergistic Effect of Simultaneous Doping of Ceria Nanorods with Cu and Cr on CO Oxidation and NO Reduction

Ceria particles play a key role in catalytic applications such as automotive three-way catalytic systems in which toxic CO and NO are oxidized and reduced to safe CO2 and N2 , respectively. In this work, we explore the incorporation of Cu and Cr metals as dopants in the crystal structure of ceria nanorods prepared by a single-step hydrothermal synthesis. XRD, Raman and XPS confirm the incorporation of Cu and Cr in the ceria crystal lattices, offering ceria nanorods with a higher concentration of oxygen vacancies. XPS also confirms the presence of Cr and Cu surface species. H2 -TPR and XPS analysis show that the simultaneous Cu and Cr co-doping results in a catalyst with a higher surface Cu concentration and a much-enhanced surface reducibility, in comparison with either undoped or singly doped (Cu or Cr) ceria nanorods. While single Cu doping enhances catalytic CO oxidation and Cr doping improves catalytic NO reduction, co-doping with both Cu and Cr enhances the benefits of both dopants in a synergistic manner employing roughly a quarter of dopant weight.

Defects Engineering on Ceria and C-C Coupling Reactions Using [Au11(PPh3)7I3] Nanocluster: A Combined Experimental and Theoretical Study

Ligand protected atom-precise gold-based catalysts have been utilized in many essential chemical processes, but their mechanism and the fate of the catalyst during reaction are still unrevealed. Atom-precise cluster without ligands are thus highly desirable to maximize atom efficiency, but making these in solution phase is challenging. In this scenario, catalysts with dispersion on oxide support are highly desirable to understand the role of metal core during catalytic reaction. Here, we report the synthesis of Au₁₁(PPh₃)₇I₃ cluster that consists of an incomplete icosahedron core. During its impregnation process on CeO₂ support, all of the ligands were removed from the kernel and the Au₁₁ kernel fits into the defects of ceria (embedded onto the oxygen vacancy of ceria (111) plane). This Au₁₁@CeO₂ has high atom efficiency and catalytic activity for Ullmann-type C-C homocoupling reactions for electron rich substrates. Density functional theory calculations showed that hexagonal arrangements of Au₁₁ kernel on (111) plane of CeO₂ is the most stable one. Theoretical calculations also proved that the atop gold atom has more favorable interaction with phenyl iodide than the second layer gold atoms of the Au₁₁@CeO₂. This demonstrated that the present catalyst mimics the single-atom catalyst-like behavior in facilitating the coupling reactions.

Cerium–Copper–Manganese Oxides Synthesized via Solution Combustion Synthesis (SCS) for Total Oxidation of VOCs

Abstract

A set of cerium–manganese–copper oxide catalysts with various foreign metal contents was prepared via the solution combustion synthesis (SCS). The catalysts were characterized by complementary techniques such as N2 physisorption at − 196 °C, X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), H2-temperature-programmed reduction (H2-TPR), O2-temperature-programmed desorption (O2-TPD) and X-ray photoelectron spectroscopy (XPS). Their catalytic activity was tested towards the VOC oxidation using ethylene and propylene as probe molecules. As a whole, it has been observed that the Ce55Mn45 sample (Mn 45 at.%), containing MnOx clusters interacting with the ceria phase, was the most active catalyst for propylene oxidation, exhibiting a complete conversion at 250 °C. On the other hand, the ternary oxide catalyst (Ce55Mn22.5Cu22.5 with Mn = 22.5 at.% and Cu = 22.5 at.%) has exhibited the best results for the oxidation of ethylene. These findings suggest that the co-presence of different active phases on the catalytic surface may have a beneficial (multiplicative) role on the whole reactivity. Finally, the most active powder catalysts were wash-coated in a SiC monolith and tested in a bench-scale reactor. As a whole, the catalyzed monoliths performed the complete oxidation of either ethylene or propylene at lower temperatures (550 and 450 °C, respectively) than those required to thermally decompose these molecules.

Graphic Abstract

Catalytic Behaviour of Flame-Made CuO-CeO2 Nanocatalysts in Efficient CO Oxidation

CuO-CeO2 nanocatalysts with varying CuO contents (1, 5, 9, 14 and 17 wt %) were prepared by one-step flame spray pyrolysis (FSP) and applied to CO oxidation. The influences of CuO content on the as-prepared catalysts were systematically characterized by X-ray diffraction (XRD), N2 adsorption-desorption at −196 °C, field emission scanning electron microscopy (FESEM), high-resolution transmission electron microscopy (HRTEM), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), and hydrogen-temperature programmed reduction (H2-TPR). A superior CO oxidation activity was observed for the 14 wt % CuO-CeO2 catalyst, with 90% CO conversion at 98 °C at space velocity (60,000 mL × g−1 × h−1), which was attributed to abundant surface defects (lattice distortion, Ce3+, and oxygen vacancies) and high reducibility supported by strong synergistic interaction. In addition, the catalyst also displayed excellent stability and resistance to water vapor. Significantly, in situ diffuse reflectance infrared Fourier transform spectroscopy (in situ DRIFTS) showed that in the CO catalytic oxidation process, the strong synergistic interaction led readily to dehydroxylation and CO adsorption on Cu+ at low temperature. Furthermore, in the feed of water vapor, although there was an adverse effect on the access of CO adsorption, there was also a positive effect on the formation of fewer carbon intermediates. All these results showed the potential of highly active and water vapor-resistive CuO-CeO2 catalysts prepared by FSP.

In situ Raman analyses of the soot oxidation reaction over nanostructured ceria-based catalysts

To reduce the emissions of internal combustion engines, ceria-based catalysts have been widely investigated as possible alternatives to the more expensive noble metals. In the present work, a set of four different ceria-based materials was prepared via hydrothermal synthesis, studying the effect of Cu and Mn as dopants both in binary and ternary oxides. In situ Raman analyses were carried out to monitor the behaviour of defect sites throughout thermal cycles and during the soot oxidation reaction. Despite ceria doped with 5% of Cu featured the highest specific surface area, reducibility and amount of intrinsic and extrinsic defects, a poor soot oxidation activity was observed through the standard activity tests. This result was confirmed by the calculation of soot conversion curves obtained through a newly proposed procedure, starting from the Raman spectra collected during the in situ tests. Moreover, Raman analyses highlighted that new defectiveness was produced on the Cu-doped catalyst at high temperature, especially after soot conversion, while a slight increase of the defect band and a total reversibility were observed in case of the ternary oxide and pure/Mn-doped ceria, respectively. The major increment was related to the extrinsic defects component; tests carried out in different atmospheres suggested the assignment of this feature to vacancy-free sites containing oxidized doping cations. Its increase at the end of the tests can be an evidence of peroxides and superoxides deactivation on catalysts presenting excessive oxygen vacancy concentrations. Instead, ceria doped with 5% of Mn exhibited the best soot oxidation activity, thanks to an intermediate density of oxygen vacancies and to its well-defined morphology.

Synergetic effect over flame-made manganese doped CuO-CeO2 nanocatalyst for enhanced CO oxidation performance

CuO-CeO2 nanocatalysts with different amounts of Mn dopping (Mn/Cu molar ratios of 0.5 : 5, 1 : 5 and 1.5 : 5) were synthesized by flame spray pyrolysis (FSP) method and tested in the catalytic oxidation of CO. The physicochemical properties of the synthesised samples were characterized systematically, including using X-ray diffraction (XRD), Raman spectroscopy, field-emission scanning electron microscopy (FESEM), Brunauer-Emmett-Teller (BET), X-ray photoelectron spectroscopy (XPS), oxygen-temperature programmed desorption (O2-TPD), hydrogen-temperature programmed reduction (H2-TPR) and in situ diffuse reflectance infrared Fourier transform spectroscopy (in situ DRIFTS). The results showed that the 1Mn-Cu-Ce sample (Mn/Cu molar ratio of 1 : 5) exhibited superior catalytic activity for CO oxidation, with the temperature of 90% CO oxidation at 131 °C at a high space velocity (SV = 60 000 mL g-1 h-1), which was 56 °C lower than that of the Cu-Ce sample. In addition, the 1Mn-Cu-Ce sample displays excellent stability with prolonged time on CO stream and the resistance to water vapor. The significantly enhanced activity was correlated with strong synergetic effect, leading to fine textual properties, abundant chemically adsorbed oxygen and high lattice oxygen mobility, which further induced more Cu+ species and less formation of carbon intermediates during the CO oxidation process detected by in situ DRIFTS analysis. This work will provide in-depth understanding of the synergetic effect on CO oxidation performances over Mn doped CuO-CeO2 composite catalysts through FSP method.