Formation of calcium phosphates on titanium implants with four different bioactive surface preparations. An in vitro study

Osteogenesis-inducing calcium phosphate nanoparticle precursors applied to titanium surfaces

This study investigated the effects of the morphology and physicochemical properties of calcium phosphate (CaP) nanoparticles on osteogenesis. Two types of CaP nanoparticles were compared, namely amorphous calcium phosphate (ACP) nano-spheres (diameter: 9-13 nm) and poorly crystalline apatite (PCA) nano-needles (30-50 nm × 2-4 nm) that closely resemble bone apatite. CaP particles were spin-coated onto titanium discs and implants; they were evaluated in cultured mouse calvarial osteoblasts, as well as after implantation in rabbit femurs. A significant dependence of CaP coatings was observed in osteoblast-related gene expression (Runx2, Col1a1 and Spp1). Specifically, the PCA group presented an up-regulation of the osteospecific genes, while the ACP group suppressed the Runx2 and Col1a1 expression when compared to blank titanium substrates. Both the ACP and PCA groups presented a more than three-fold increase of calcium deposition, as suggested by Alizarin red staining. The removal torque results implied a slight tendency in favour of the PCA group. Different forms of CaP nanostructures presented different biologic differences; the obtained information can be used to optimize surface coatings on biomaterials.

Cell response of anodized nanotubes on titanium and titanium alloys

Titanium and titanium alloy implants that have been demonstrated to be more biocompatible than other metallic implant materials, such as Co-Cr alloys and stainless steels, must also be accepted by bone cells, bonding with and growing on them to prevent loosening. Highly ordered nanoporous arrays of titanium dioxide that form on titanium surface by anodic oxidation are receiving increasing research interest due to their effectiveness in promoting osseointegration. The response of bone cells to implant materials depends on the topography, physicochemistry, mechanics, and electronics of the implant surface and this influences cell behavior, such as adhesion, proliferation, shape, migration, survival, and differentiation; for example the existing anions on the surface of a titanium implant make it negative and this affects the interaction with negative fibronectin (FN). Although optimal nanosize of reproducible titania nanotubes has not been reported due to different protocols used in studies, cell response was more sensitive to titania nanotubes with nanometer diameter and interspace. By annealing, amorphous TiO2 nanotubes change to a crystalline form and become more hydrophilic, resulting in an encouraging effect on cell behavior. The crystalline size and thickness of the bone-like apatite that forms on the titania nanotubes after implantation are also affected by the diameter and shape. This review describes how changes in nanotube morphologies, such as the tube diameter, the thickness of the nanotube layer, and the crystalline structure, influence the response of cells.

Local bisphosphonate release versus hydroxyapatite coating for stainless steel screw fixation in rat tibiae

Implant fixation in bone can be improved by a coating that delivers bisphosphonates locally, or by a hydroxyapatite (HA) coating. In this study, we compared these different types of coatings. For mechanical testing, 30 rats were assigned into three groups, and similar screws were implanted bilaterally in the proximal tibiae. The rats received screws that were either uncoated, coated with nano-crystalline hydroxyapatite or coated with a bisphosphonate releasing protein matrix. After 4 weeks, one screw was subjected to pull-out testing, and the contra-lateral one to torsion testing. For morphology, 30 rats were assigned to similar treatment groups, but received only one screw each. Bisphosphonates enhanced the pull-out force by 41% (P = 0.02) compared to controls, HA increased the pull-out force although not significantly. Conversely, HA increased the maximal torque by 64% (P = 0.02). Morphometry showed higher bone volume around bisphosphonate screws in comparison to HA-coated screws (P < 0.001) and controls (P < 0.001). The results suggest that bisphosphonates improve fixation by increasing the amount of surrounding bone, whereas HA mainly improves bone to implant attachment.

Laminin Coating Promotes Calcium Phosphate Precipitation on Titanium Discs in vitro

Objectives

The objective of this study was to investigate the effect of a laminin coating on calcium phosphate precipitation on three potentially bioactive titanium surfaces in simulated body fluid.

Material and Methods

Blasted titanium discs were prepared by alkali and heat treatment (AH), anodic oxidation (AO) or hydroxyapatite coating (HA) and subsequently coated with laminin. A laminin coated blasted surface (B) served as a positive control while a blasted non coated (B-) served as a negative control. Surface morphology was examined by Scanning Electron Microscopy (SEM). The analysis of the precipitated calcium and phosphorous was performed by Energy Dispersive X-ray Spectroscopy (EDX).

Results

The thickness of the laminin coating was estimated at 26 Å by ellipsometry. Interferometry revealed that the coating process did not affect any of the tested topographical parameters on µm level when comparing B to B-. After 2 weeks of incubation in SBF, the alkali-heat treated discs displayed the highest calcium phosphate deposition and the B group showed higher levels of calcium phosphate than the B- group.

Conclusions

Our results suggest that laminin may have the potential to be used as a coating agent in order to enhance the osseoinductive performance of biomaterial surfaces, with the protein molecules possibly functioning as nucleation centres for apatite formation. Nevertheless, in vivo studies are required in order to clarify the longevity of the coating and its performance in the complex biological environment.