In vitro corrosion resistance of Lotus-type porous Ni-free stainless steels

Metal Ion Emission and Corrosion Resistance of 3D-Printed Dental Alloy

Background: Prosthetic rehabilitation requires application of materials with different chemical, mechanical and biological properties which must provide longevity, esthetics, and safe use. Corrosion resistance and metal ion emission are the major factors defining biocompatibility of base dental alloys. Digitalization in Dentistry leads to development of new materials suitable for CAD/CAM technologies. Cobalt-chromium powder alloys are used for additive manufacturing of PFM crowns. The aim of this study is to evaluate corrosion resistance and metal ion emission of Cobalt-chromium dental alloy for 3D printing. Materials and methods: 35 metal copings were designed using digital files of intraoral scans of 35 patients. CoCr dental alloy EOS CobaltChrome SP2 (EOS, Germany) was used to produce the copings by DMLS (direct laser metal sintering). Tests for presence of free Cobalt ions were conducted at several stages of the production process. Open circuit potential measurements were conducted 2 hours, 24 hours, and 7 days after placing the copings in artificial saliva. Metal ion emission was assessed by inductively coupled plasma mass spectrometry (ICP–MS) after 24 hour- and 7 day-period of stay in the solution. Results: Tests for free Cobalt ions were positive at all stages during production of the metal copings. Eocp measurements showed high corrosion resistance which increased in time. ICP-MS showed significantly higher amount of cobalt and chromium ions after 7-day period of stay compared to 24-hour period. Conclusion: Studied alloy showed high corrosion resistance at in vitro conditions. Detected ion emission requires further investigations on the biological properties.

Biological behaviour of human umbilical artery smooth muscle cell grown on nickel-free and nickel-containing stainless steel for stent implantation

To evaluate the clinical potential of high nitrogen nickel-free austenitic stainless steel (HNNF SS), we have compared the cellular and molecular responses of human umbilical artery smooth muscle cells (HUASMCs) to HNNF SS and 316L SS (nickel-containing austenitic 316L stainless steel). CCK-8 analysis and flow cytometric analysis were used to assess the cellular responses (proliferation, apoptosis, and cell cycle), and quantitative real-time PCR (qRT-PCR) was used to analyze the gene expression profiles of HUASMCs exposed to HNNF SS and 316L SS, respectively. CCK-8 analysis demonstrated that HUASMCs cultured on HNNF SS proliferated more slowly than those on 316L SS. Flow cytometric analysis revealed that HNNF SS could activate more cellular apoptosis. The qRT-PCR results showed that the genes regulating cell apoptosis and autophagy were up-regulated on HNNF SS. Thus, HNNF SS could reduce the HUASMC proliferation in comparison to 316L SS. The findings furnish valuable information for developing new biomedical materials for stent implantation.

Reduction of in-stent restenosis risk on nickel-free stainless steel by regulating cell apoptosis and cell cycle

High nitrogen nickel-free austenitic stainless steel (HNNF SS) is one of the biomaterials developed recently for circumventing the in-stent restenosis (ISR) in coronary stent applications. To understand the ISR-resistance mechanism, we have conducted a comparative study of cellular and molecular responses of human umbilical vein endothelial cells (HUVECs) to HNNF SS and 316L SS (nickel-containing austenitic 316L stainless steel) which is the stent material used currently. CCK-8 analysis and flow cytometric analysis were used to assess the cellular responses (proliferation, apoptosis, and cell cycle), and quantitative real-time PCR (qRT-PCR) was used to analyze the gene expression profile of HUVECs exposed to HNNF SS and 316L SS, respectively. Flow cytometry analysis revealed that 316L SS could activate the cellular apoptosis more efficiently and initiate an earlier entry into the S-phase of cell cycle than HNNF SS. At the molecular level, qRT-PCR results showed that the genes regulating cell apoptosis and autophagy were overexpressed on 316L SS. Further examination indicated that nickel released from 316L SS triggered the cell apoptosis via Fas-Caspase8-Caspase3 exogenous pathway. These molecular mechanisms of HUVECs present a good model for elucidating the observed cellular responses. The findings in this study furnish valuable information for understanding the mechanism of ISR-resistance on the cellular and molecular basis as well as for developing new biomedical materials for stent applications.

The effect of some fluids on surface oxidation and amount of released iron of stainless steel endodontic files

Endodontic files come in contact with blood, infected pulp tissue, and irrigating solutions during root canal therapy. Some instruments such as stereomicroscopy and scanning electron microscopy are used to observe corrosion of endodontic files which are complicated and dependent on preparation methods. Having knowledge of the corrosion and ion release of endodontic files can help in drawing firm deductions as to which files would perform better in the clinical scenario. Therefore, we have used energy dispersive X-ray analysis and an atomic absorption spectrophotometer to track oxygen on the surface and iron in the exposed media to observe the oxidative rate of the media. In this study, corrosion by blood was higher than other biological fluids, but less than with sodium hypochlorite (NaOCl). Observations of energy dispersive X-ray analysis and atomic absorption spectrophotometer results demonstrated that after exposure the amount of oxygen on the surface and surrounding areas increased. Therefore, the files should be rinsed as soon as possible during and after use to hinder the oxidation rate, but blood may produce a different behavior and it might be considered as a decreased risk of broken stainless steel files remaining in the root canal after treatment.

Metallic ions released from stainless steel, nickel-free, and titanium orthodontic alloys: toxicity and DNA damage

INTRODUCTION

The aims of this study were to determine the amounts of metallic ions that stainless steel, nickel-free, and titanium alloys release to a culture medium, and to evaluate the cellular viability and DNA damage of cultivated human fibroblasts with those mediums.

METHODS

The metals were extracted from 10 samples (each consisting of 4 buccal tubes and 20 brackets) of the 3 orthodontic alloys that were submerged for 30 days in minimum essential medium. Next, the determination of metals was performed by using inductively coupled plasma mass spectrometry, cellular viability was assessed by using the tetrazolium reduction assay (MTT assay) (3-[4,5-dimethylthiazol-2-yl]-2, 5-diphenyltetrazolium bromide), and DNA damage was determined with the Comet assay. The metals measured in all the samples were Ti(47), Cr(52), Mn(55), Co(59), Ni(60), Mo(92), Fe(56), Cu(63), Zn(66), As(75), Se(78), Cd(111), and Pb(208).

RESULTS

The cellular viability of the cultured fibroblasts incubated for 7 days with minimum essential medium, with the stainless steel alloy submerged, was close to 0%. Moreover, high concentrations of titanium, chromium, manganese, cobalt, nickel, molybdenum, iron, copper, and zinc were detected. The nickel-free alloy released lower amounts of ions to the medium. The greatest damage in the cellular DNA, measured as the olive moment, was also produced by the stainless steel alloy followed by the nickel-free alloy. Conversely, the titanium alloy had an increased cellular viability and did not damage the cellular DNA, as compared with the control values.

CONCLUSIONS

The titanium brackets and tubes are the most biocompatible of the 3 alloys studied.

Nickel-free austenitic stainless steels for medical applications

The adverse effects of nickel ions being released into the human body have prompted the development of high-nitrogen nickel-free austenitic stainless steels for medical applications. Nitrogen not only replaces nickel for austenitic structure stability but also much improves steel properties. Here we review the harmful effects associated with nickel in medical stainless steels, the advantages of nitrogen in stainless steels, and emphatically, the development of high-nitrogen nickel-free stainless steels for medical applications. By combining the benefits of stable austenitic structure, high strength and good plasticity, better corrosion and wear resistances, and superior biocompatibility compared to the currently used 316L stainless steel, the newly developed high-nitrogen nickel-free stainless steel is a reliable substitute for the conventional medical stainless steels.