Tran DT, Chen FH, Wu GL, Ching PCO, Yeh ML. Influence of Spin Coating and Dip Coating with Gelatin/Hydroxyapatite for Bioresorbable Mg Alloy Orthopedic Implants: In Vitro and In Vivo Studies. ACS Biomater Sci Eng 2023; 9:705-718. [PMID: 36695051 DOI: 10.1021/acsbiomaterials.2c01122] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 01/26/2023]
Abstract
Suitable biomechanical properties, good biocompatibility, and osteoconductivity of a degradable magnesium (Mg) alloy make it a potential material for orthopedic implants. The main limitation of Mg is its high corrosion rate in the human body. Surface modification is necessary to improve the Mg corrosion resistance. In this work, a polymeric layer of gelatin/nanohydroxyapatite (Gel/nHA) was coated on a ZK60 Mg alloy by dip coating and spin coating to test the corrosion resistance and biocompatibility in vitro and in vivo. The results from the in vitro test revealed that the coated groups reduced the corrosion rate with the corrosion current density by 59 and 81%, from 31.22 to 12.83 μA/cm2 and 5.83 μA/cm2 in the spin coating and dip coating groups, respectively. The dip coating group showed better corrosion resistance than the spin coating group with the lowest released hydrogen content (17.5 mL) and lowest pH value (8.23) and reducing the current density by 45%. In vitro, the relative growth rate was over 75% in all groups tested with MG63, demonstrating that the Mg substrate and coating materials were within the safety range. The dip coating and spin coating groups enhanced the cell proliferation with significantly higher OD values (3.3, 3.0, and 2.5, respectively) and had better antihemolysis and antiplatelet adhesion abilities than the uncoated group. The two coating methods showed no difference in the cellular response, cell migration, hemolysis, and platelet adhesion test. In in vivo tests in rats, the dip coating group also showed a higher corrosion resistance with a lower corrosion rate and mass loss than the spin coating group. In addition, the blood biochemistry and histopathology results indicated that all materials used in this study were biocompatible with living subjects. The present research confirmed that the two methods have no noticeable difference in cell and organ response but the corrosion resistance of dip coating was higher than that of spin coating either in vitro or in vivo.
Collapse
Affiliation(s)
- Duong-Thuy Tran
- Department of Biomedical Engineering, National Cheng Kung University, No. 1, Daxue Road, East District, Tainan701, Taiwan
| | - Fang-Hsu Chen
- Department of Biomedical Engineering, National Cheng Kung University, No. 1, Daxue Road, East District, Tainan701, Taiwan
| | - Guan-Lin Wu
- Department of Biomedical Engineering, National Cheng Kung University, No. 1, Daxue Road, East District, Tainan701, Taiwan
| | - Paula Carmela O Ching
- Department of Biomedical Engineering, National Cheng Kung University, No. 1, Daxue Road, East District, Tainan701, Taiwan
| | - Ming-Long Yeh
- Department of Biomedical Engineering, National Cheng Kung University, No. 1, Daxue Road, East District, Tainan701, Taiwan.,Medical Device Innovation Center, National Cheng Kung University, No. 1, Daxue Road, East District, Tainan701, Taiwan
| |
Collapse
|
2
|
Degradable Pure Magnesium Used as a Barrier Film for Oral Bone Regeneration. J Funct Biomater 2022; 13:jfb13040298. [PMID: 36547558 PMCID: PMC9781112 DOI: 10.3390/jfb13040298] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/04/2022] [Revised: 12/08/2022] [Accepted: 12/09/2022] [Indexed: 12/23/2022] Open
Abstract
The barrier membrane plays an extremely critical role in guided bone regeneration (GBR), which determines the success or failure of GBR technology. In order to obtain barrier membranes with high mechanical strength and degradability, some researchers have focused on degradable magnesium alloys. However, the degradation rate of pure Mg-based materials in body fluids is rather fast, thus posing an urgent problem to be solved in oral clinics. In this study, a novel micro-arc oxidation (MAO) surface-treated pure Mg membrane was prepared. Electrochemical tests, immersion experiments and in vivo experiments were carried out to investigate its potential use as a barrier membrane. The experimental results showed that the corrosion resistance of a pure Mg membrane treated by MAO is better than that of the uncoated pure Mg. The results of cell experiments showed no obvious cytotoxicity, which suggests the enhanced differentiation of osteoblasts. At the same time, the MAO-Mg membrane showed better biological activity than the pure Ti membrane in the early stage of implantation, exhibiting relatively good bone regeneration ability. Consequently, the MAO membrane has been proven to possess good application prospects for guided bone regeneration.
Collapse
|
3
|
Wang M, Yang Y, Yuan K, Yang S, Tang T. Dual-functional hybrid quaternized chitosan/Mg/alginate dressing with antibacterial and angiogenic potential for diabetic wound healing. J Orthop Translat 2021; 30:6-15. [PMID: 34466384 PMCID: PMC8365451 DOI: 10.1016/j.jot.2021.07.006] [Citation(s) in RCA: 11] [Impact Index Per Article: 3.7] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Received: 04/20/2021] [Revised: 07/25/2021] [Accepted: 07/27/2021] [Indexed: 01/07/2023] Open
Abstract
BACKGROUND Clinic treatment of diabetic foot ulcers (DFUs) is considerably challenging. Impaired wound healing may be caused by poor vascularization and dysfunction of the extracellular matrix, which leads to poor re-epithelialization and increased risk of infection. In this study, we evaluated the treatment potential of a functional dressing comprising quaternized chitosan (hydroxypropyltrimethyl ammonium chloride chitosan) and magnesium (Mg) on DFUs. METHODS Dressings were prepared by vacuum freeze-drying. The cellular proliferation, migration, and angiogenesis potential of the functional dressings were determined in vitro. Methicillin-resistant Staphylococcus aureus (MRSA, ATCC43300) and methicillin-resistant Staphylococcus epidermidis 287 (MRSE287) were used to evaluate the antibacterial efficiency of the dressings. Finally, a diabetic rat model with infected wounds was used to further evaluate the effects of functional dressings on the healing of DFUs. RESULTS Functional dressings facilitated the migration of human dermal fibroblasts and human umbilical vein endothelial cells (HUVECs), while also stimulating angiogenesis in HUVECs. Additionally, the functional dressing could effectively eradicate MRSA and MRSE, exhibiting excellent antibacterial ability against drug-resistant bacteria. The results of in vivo microbiological and histological tests demonstrated effective anti-infection ability and wound-healing potential of this functional dressing. CONCLUSIONS The dual-functional dressing exhibited wound-healing ability and anti-infection efficiency, demonstrating potential application prospects in DFU treatment. TRANSLATIONAL POTENTIAL OF THIS ARTICLE As one of the common and serious complications of diabetes, DFUs do not heal easily, causing great suffering to patients. Therefore, improvement in the prognosis of DFUs is a crucial clinical need. The dual-functional dressing prepared in this study was proven to improve the treatment of DFUs, both in vitro and in vivo. Considering its urgent clinical necessity and good biocompatibility of its raw materials, such as alginate, Mg, and chitosan derivatives, this dual-functional dressing presents good prospects for clinical translation.
Collapse
Affiliation(s)
- Minqi Wang
- Shanghai Key Laboratory of Orthopaedic Implants, Department of Orthopaedic Surgery, Shanghai Ninth People's Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai, China
| | - Yiqi Yang
- Shanghai Key Laboratory of Orthopaedic Implants, Department of Orthopaedic Surgery, Shanghai Ninth People's Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai, China
| | - Kai Yuan
- Shanghai Key Laboratory of Orthopaedic Implants, Department of Orthopaedic Surgery, Shanghai Ninth People's Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai, China
| | - Shengbing Yang
- Shanghai Key Laboratory of Orthopaedic Implants, Department of Orthopaedic Surgery, Shanghai Ninth People's Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai, China
| | - Tingting Tang
- Shanghai Key Laboratory of Orthopaedic Implants, Department of Orthopaedic Surgery, Shanghai Ninth People's Hospital, Shanghai Jiao Tong University School of Medicine, Shanghai, China
| |
Collapse
|
4
|
Research status of biodegradable metals designed for oral and maxillofacial applications: A review. Bioact Mater 2021; 6:4186-4208. [PMID: 33997502 PMCID: PMC8099919 DOI: 10.1016/j.bioactmat.2021.01.011] [Citation(s) in RCA: 33] [Impact Index Per Article: 11.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 10/24/2020] [Revised: 01/10/2021] [Accepted: 01/10/2021] [Indexed: 01/08/2023] Open
Abstract
The oral and maxillofacial regions have complex anatomical structures and different tissue types, which have vital health and aesthetic functions. Biodegradable metals (BMs) is a promising bioactive materials to treat oral and maxillofacial diseases. This review summarizes the research status and future research directions of BMs for oral and maxillofacial applications. Mg-based BMs and Zn-based BMs for bone fracture fixation systems, and guided bone regeneration (GBR) membranes, are discussed in detail. Zn-based BMs with a moderate degradation rate and superior mechanical properties for GBR membranes show great potential for clinical translation. Fe-based BMs have a relatively low degradation rate and insoluble degradation products, which greatly limit their application and clinical translation. Furthermore, we proposed potential future research directions for BMs in the oral and maxillofacial regions, including 3D printed BM bone scaffolds, surface modification for BMs GBR membranes, and BMs containing hydrogels for cartilage regeneration, soft tissue regeneration, and nerve regeneration. Taken together, the progress made in the development of BMs in oral and maxillofacial regions has laid a foundation for further clinical translation.
Collapse
|
5
|
Li W, Yuan F, Bai J, Cheng J, Li H, Zheng J, Bai W, Lyu P. In vivo evaluation of bending strengths and degradation rates of different magnesium pin designs for oral stapler. J Appl Biomater Funct Mater 2020; 18:2280800019836400. [PMID: 33372827 DOI: 10.1177/2280800019836400] [Citation(s) in RCA: 2] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 01/14/2023] Open
Abstract
Magnesium alloys have been potential biodegradable implants in the areas of bone, cardiovascular system, gastrointestinal tract, and so on. The purpose of this study is to evaluate Mg-2Zn alloy degradation as a potential suture material. The study included Sprague-Dawley (SD) rats in vivo. In 24 male SD rats, tests in the leg muscle were conducted using traditional surgical incision and insertion of magnesium alloys of different designs into the tissue. The material degradation topography, elemental composition, and strength of the pins were analyzed. This paper explores magnesium pins with different cross-sectional shapes and diameters to establish a suitable pin diameter and shape for use as an oral stapler, which must have a good balance of degradation rate and strength. The results showed there were good bending strengths over different degradation periods in groups with diameters of 0.8 mm and 0.5 mm, and no significantly different bending strength between the groups of triangle and round cross-section shapes with same diameter of 0.3 mm, although the degradation rate still needs to be improved.
Collapse
Affiliation(s)
- Wenjun Li
- Center of Digital Dentistry, Peking University School and Hospital of Stomatology, Beijing, China.,Research Center of Engineering and Technology for Digital Dentistry, Ministry of Health, Beijing, China
| | - Fusong Yuan
- Center of Digital Dentistry, Peking University School and Hospital of Stomatology, Beijing, China.,Research Center of Engineering and Technology for Digital Dentistry, Ministry of Health, Beijing, China
| | - Jing Bai
- School of Materials Science and Engineering, Southeast University, Nanjing, China
| | - Junyao Cheng
- School of Materials Science and Engineering, Southeast University, Nanjing, China
| | - Hongxiang Li
- State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, China
| | - Jianqiao Zheng
- Center of Digital Dentistry, Peking University School and Hospital of Stomatology, Beijing, China.,Research Center of Engineering and Technology for Digital Dentistry, Ministry of Health, Beijing, China
| | - Wei Bai
- Dental Medical Devices Testing Center, Peking University School of Stomatology, Beijing, China
| | - Peijun Lyu
- Center of Digital Dentistry, Peking University School and Hospital of Stomatology, Beijing, China.,Research Center of Engineering and Technology for Digital Dentistry, Ministry of Health, Beijing, China
| |
Collapse
|
6
|
Lin LH, Lee HP, Yeh ML. Characterization of a Sandwich PLGA-Gallic Acid-PLGA Coating on Mg Alloy ZK60 for Bioresorbable Coronary Artery Stents. MATERIALS (BASEL, SWITZERLAND) 2020; 13:E5538. [PMID: 33291735 PMCID: PMC7730464 DOI: 10.3390/ma13235538] [Citation(s) in RCA: 10] [Impact Index Per Article: 2.5] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 11/08/2020] [Revised: 11/30/2020] [Accepted: 12/02/2020] [Indexed: 02/07/2023]
Abstract
Absorbable magnesium stents have become alternatives for treating restenosis owing to their better mechanical properties than those of bioabsorbable polymer stents. However, without modification, magnesium alloys cannot provide the proper degradation rate required to match the vascular reform speed. Gallic acid is a phenolic acid with attractive biological functions, including anti-inflammation, promotion of endothelial cell proliferation, and inhibition of smooth muscle cell growth. Thus, in the present work, a small-molecule eluting coating is designed using a sandwich-like configuration with a gallic acid layer enclosed between poly (d,l-lactide-co-glycolide) layers. This coating was deposited on ZK60 substrate, a magnesium alloy that is used to fabricate bioresorbable coronary artery stents. Electrochemical analysis showed that the corrosion rate of the specimen was ~2000 times lower than that of the bare counterpart. The released gallic acid molecules from sandwich coating inhibit oxidation by capturing free radicals, selectively promote the proliferation of endothelial cells, and inhibit smooth muscle cell growth. In a cell migration assay, sandwich coating delayed wound closure in smooth muscle cells. The sandwich coating not only improved the corrosion resistance but also promoted endothelialization, and it thus has great potential for the development of functional vascular stents that prevent late-stent restenosis.
Collapse
Affiliation(s)
- Li-Han Lin
- Department of Biomedical Engineering, National Cheng Kung University, Tainan 701, Taiwan;
| | - Hung-Pang Lee
- Biomedical Engineering, Dwight Look College of Engineering, Texas A&M University, College Station, TX 77843, USA;
| | - Ming-Long Yeh
- Department of Biomedical Engineering, National Cheng Kung University, Tainan 701, Taiwan;
- Medical Device Innovation Center, National Cheng Kung University, Tainan 701, Taiwan
| |
Collapse
|
7
|
Ferrández-Montero A, Lieblich M, González-Carrasco J, Benavente R, Lorenzo V, Detsch R, Boccaccini A, Ferrari B. Development of biocompatible and fully bioabsorbable PLA/Mg films for tissue regeneration applications. Acta Biomater 2019; 98:114-124. [PMID: 31085363 DOI: 10.1016/j.actbio.2019.05.026] [Citation(s) in RCA: 39] [Impact Index Per Article: 7.8] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 12/14/2018] [Revised: 05/08/2019] [Accepted: 05/09/2019] [Indexed: 12/17/2022]
Abstract
During recent years, Mg reinforced polylactic acid (PLA) composites have emerged as potential biocompatible and bioabsorbable materials for biomedical applications. It has been shown that Mg particles added to a matrix based on a biodegradable polymer can address the lack of bioactivity and the low mechanical properties of the polymers and, furthermore, it can counteract the detrimental effects associated to the high degradation rate of Mg, as alkalinization and elevated H2 release. Additionally, the polymer can protect the Mg particles, by tailoring their degradation rate. Former processing of these composites performed by extrusion, compression and injection molding employed Mg contents up to 10 wt%. Higher amounts of Mg resulted in heterogeneous materials and thermally degraded matrices, with the corresponding higher degradation rate. In the present work, Mg reinforced PLA films with Mg content as high as 50 wt% were obtained without compromising the thermal stability of the polymer. Firstly, a successful dispersion of Mg microparticles was achieved by a breakthrough in processing introducing a colloidal step where organic additives were added to modify the Mg particle surface and promote a chemically stable suspension. The resulting colloidal suspension was then used as feedstock to obtain composite films by tape casting. The films show advantageous in vitro behaviour in terms of degradation, hydrogen release and oxygen permeability. In addition, the viability with fibroblast cells (MEF) opens a window of opportunity for these composite films as bioabsorbable material for tissue engineering and wound dressing applications. STATEMENT OF SIGNIFICANCE: Magnesium materials have extraordinary biodegradable properties and bioactive behavior due to release of Mg2+ ions, which offer a promising opportunity for their applicability as biomaterials for tissue regeneration. However, Mg is one of the most reactive metals with a high degradation rate. In contact with water produces H2, associated with a risk of failure of the implant. One alternative to minimize this drawback is the use of Mg particles surrounded by a biodegradable biocompatible polymer such as polylactic acid (PLA) to obtain PLA/Mg composites. In this work we processed Mg reinforced PLA in the shape of films that would be suitable for tissue regeneration. In vitro behavior of PLA/Mg films demonstrated that Mg2+ ions increase the fibroblast cells growth.
Collapse
|
8
|
Shuai C, Zhou Y, Yang Y, Gao C, Peng S, Wang G. Ag-Introduced Antibacterial Ability and Corrosion Resistance for Bio-Mg Alloys. BIOMED RESEARCH INTERNATIONAL 2018; 2018:6023460. [PMID: 30112405 PMCID: PMC6077360 DOI: 10.1155/2018/6023460] [Citation(s) in RCA: 12] [Impact Index Per Article: 2.0] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 04/11/2018] [Revised: 06/22/2018] [Accepted: 07/03/2018] [Indexed: 11/18/2022]
Abstract
Bone implants are expected to possess antibacterial ability and favorable biodegradability. Ag possesses broad-spectrum antibacterial effects through destroying the respiration and substance transport of bacteria. In this study, Ag was introduced into Mg-3Zn-0.5Zr (ZK30) via selective laser melting technology. Results showed that ZK30-Ag exhibited a strong and stable antibacterial activity against the bacterium Escherichia coli. Moreover, the degradation resistance was enhanced due to the comprehensive effect of positive shifted corrosion potential (from -1.64 to -1.53 V) and grains refinement. The positive shifted corrosion potential reduced the severe galvanic corrosion by lowering the corrosion potential difference between the matrix and the second phase. Meanwhile, the introduction of Ag caused the grain refinement strengthening and precipitated-phase strengthening, resulting in improved compressive yield strength and hardness. Furthermore, ZK30-0.5Ag exhibited good biocompatibility. It was suggested that Ag-modified ZK30 was potential candidate for bone implants.
Collapse
Affiliation(s)
- Cijun Shuai
- Jiangxi University of Science and Technology, Nanchang 330013, China
- State Key Laboratory of High Performance Complex Manufacturing, College of Mechanical and Electrical Engineering, Central South University, Changsha 410083, China
- Key Laboratory of Organ Injury, Aging and Regenerative Medicine of Hunan Province, Changsha 410008, China
| | - Yuanzhuo Zhou
- State Key Laboratory of High Performance Complex Manufacturing, College of Mechanical and Electrical Engineering, Central South University, Changsha 410083, China
| | - Youwen Yang
- Jiangxi University of Science and Technology, Nanchang 330013, China
- State Key Laboratory of High Performance Complex Manufacturing, College of Mechanical and Electrical Engineering, Central South University, Changsha 410083, China
| | - Chengde Gao
- State Key Laboratory of High Performance Complex Manufacturing, College of Mechanical and Electrical Engineering, Central South University, Changsha 410083, China
| | - Shuping Peng
- The Key Laboratory of Carcinogenesis of the Chinese Ministry of Health, Xiangya Hospital, Central South University, Changsha 410078, China
| | - Guoyong Wang
- Jiangxi University of Science and Technology, Nanchang 330013, China
| |
Collapse
|
9
|
Development of a Novel Degradation-Controlled Magnesium-Based Regeneration Membrane for Future Guided Bone Regeneration (GBR) Therapy. METALS 2017. [DOI: 10.3390/met7110481] [Citation(s) in RCA: 8] [Impact Index Per Article: 1.1] [Reference Citation Analysis] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 02/05/2023]
|
10
|
Lee HP, Lin DJ, Yeh ML. Phenolic Modified Ceramic Coating on Biodegradable Mg Alloy: The Improved Corrosion Resistance and Osteoblast-Like Cell Activity. MATERIALS 2017; 10:ma10070696. [PMID: 28773055 PMCID: PMC5551739 DOI: 10.3390/ma10070696] [Citation(s) in RCA: 17] [Impact Index Per Article: 2.4] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 05/16/2017] [Revised: 06/11/2017] [Accepted: 06/22/2017] [Indexed: 12/18/2022]
Abstract
Magnesium alloys have great potential for developing orthopedic implants due to their biodegradability and mechanical properties, but the rapid corrosion rate of the currently-available alloys limits their clinical applications. To increase the corrosion resistance of the substrate, a protective ceramic coating is constructed by a micro-arc oxidation (MAO) process on ZK60 magnesium alloy. The porous ceramic coating is mainly composed of magnesium oxide and magnesium silicate, and the results from cell cultures show it can stimulate osteoblastic cell growth and proliferation. Moreover, gallic acid, a phenolic compound, was successfully introduced onto the MAO coating by grafting on hydrated oxide and chelating with magnesium ions. The gallic acid and rough surface of MAO altered the cell attachment behavior, making it difficult for fibroblasts to adhere to the MAO coating. The viability tests showed that gallic acid could suppress fibroblast growth and stimulate osteoblastic cell proliferation. Overall, the porous MAO coating combined with gallic acid offered a novel strategy for increasing osteocompatibility.
Collapse
Affiliation(s)
- Hung-Pang Lee
- Department of Biomedical Engineering, National Cheng Kung University, Tainan 701, Taiwan.
| | - Da-Jun Lin
- Department of Materials Science and Engineering, National Cheng Kung University, Tainan 701, Taiwan.
| | - Ming-Long Yeh
- Department of Biomedical Engineering, National Cheng Kung University, Tainan 701, Taiwan.
- Medical Device Innovation Center, National Cheng Kung University, Tainan 701, Taiwan.
| |
Collapse
|