Effect of temperature on surface characteristics of nitrogen ion implanted biocompatible titanium

Effect of Annealing on the Surface Hardness of High-Fluence Nitrogen Ion-Implanted Titanium

Commercially pure titanium grade II was kinetically nitrided by implanting nitrogen ions with a fluence in the range of (1-9)·10¹⁷ cm^-2 and ion energy of 90 keV. Post-implantation annealing in the temperature stability range of TiN (up to 600 °C) shows hardness degradation for titanium implanted with high fluences above 6·10¹⁷ cm^-2, leading to nitrogen oversaturation. Temperature-induced redistribution of interstitially located nitrogen in the oversaturated lattice has been found to be the predominant hardness degradation mechanism. The impact of the annealing temperature on a change in surface hardness related to the applied fluence of implanted nitrogen has been demonstrated.

Relation between Mechanical Hardening and Nitrogen Profile of PBII Nitrided Titanium Alloy

Surface treatments of Ti-6Al-4V alloys are of utmost importance for biomedical applications since they allow for tribological gain. Here, Ti-6Al-4V disks have been PBII nitrided at either 500, 600, 700 and 800 °C. A set of techniques (XRD, SEM-EDS, EBSD and GDOES) was used to characterize the surface microstructural and chemical changes. Nanoindentation was used to assess the induced changes in terms of mechanical properties. Two types of nitrided domains are revealed. Starting from the surface, a nitride bilayer composed of δ-TiN/ϵ-Ti2N with enhanced surface resistance is supported by an α-Ti(N) solid solution formed at depth. Hardness values peak at 12-14 GPa at the surface, which is almost twice as large as the bulk value (about 7 GPa). For the moderate temperatures used here, a deep (10-15 µm) and strong hardness (14 GPa) enhancement together with a smooth gradient can be achieved.

Influence of surface pre-treatment with mechanical polishing, chemical, electrochemical and ion sputter etching on the surface properties, corrosion resistance and MG-63 cell colonization of commercially pure titanium

The impact of four pre-treatment techniques on the surface morphology and chemistry, residual stress, mechanical properties, corrosion resistance in a physiological saline solution and cell colonization of commercially pure titanium is examined in detail. Mechanical polishing, electrochemical etching, chemical etching in Kroll's reagent, and ion sputter etching with argon ions were applied. Surface morphologies reflect the nature of surface layer removal. Significant roughening of the surface and a characteristic microtopology become apparent as a result of the sensitivity of chemical and ion sputter etching to the grain orientation. The hardness in the near surface region was controlled by the amount of residual stress. Etching of the stressed surface layer led to a reduction in residual stress and surface hardness. A compact passivation layer composed of TiO, TiO₂ and Ti₂O₃ native oxides imparted high corrosion resistance to the surface after mechanical polishing, chemical and electrochemical etching. The ion sputter etched surface showed substantially reduced corrosion resistance, where the corrosion process was controlled by electron transfer. The specific topology affected the adhesion of the cell to the surface rather than the cell area coverage. The cell area coverage increased with the corrosion stability of the surface.

Enhanced cell growth on 3D graphene scaffolds implanted with nitrogen ions

One of the key challenges in engineering tissues for cell-based therapies is developing biocompatible scaffold materials to direct cell behavior. In this paper, the cytocompatibilities of a flexible three-dimensional graphene scaffold (3D-G) and the same scaffold implanted with nitrogen ions (N⁺/3D-G) are compared using an in vitro assay based on 3(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide. The N⁺/3D-G samples were prepared from low-temperature hydrothermally synthesized flexible 3D-G by ion implantation and were found to display improved adhesion and proliferation of rat osteoblast and mouse fibroblast cells. In particular, the N⁺/3D-G sample with a nitrogen content of ∼10% showed the highest levels of cell viability and proliferation. The flexible N⁺/3D-G has potential applications as a biocompatible scaffold material that provides improved surface area and hydrophilic groups for cell growth and proliferation.