Synthesis of Mesoporous Hydroxyapatite with Controlled Pore Size Using the Chitosan as an Organic Modifier: Investigating the Effect of the Weight Ratio and pH Value of Chitosan on the Structural and Morphological Properties

Effects of Various Ripening Media on the Mesoporous Structure and Morphology of Hydroxyapatite Powders

Mesoporous hydroxyapatite (HA) materials demonstrate advantages as catalysts and as support systems for catalysis, as adsorbent materials for removing contamination from soil and water, and as nanocarriers of functional agents for bone-related therapies. The present research demonstrates the possibility of the enlargement of the Brunauer-Emmett-Teller specific surface area (SSA), pore volume, and average pore diameter via changing the synthesis medium and ripening the material in the mother solution after the precipitation processes have been completed. HA powders were investigated via chemical analysis, X-ray diffraction analysis, Fourier-transform IR spectroscopy, transmission electron microscopy (TEM), and scanning (SEM) electron microscopy. Their SSA, pore volume, and pore-size distributions were determined via low-temperature nitrogen adsorption measurements, the zeta potential was established, and electron paramagnetic resonance (EPR) spectroscopy was performed. When the materials were synthesized in water-ethanol and water-acetone media, the SSA and total pore volume were 52.1 m²g^-1 and 116.4 m²g^-1, and 0.231 and 0.286 cm³g^-1, respectively. After ripening for 21 days, the particle morphology changed, the length/width aspect ratio decreased, and looser and smaller powder agglomerates were obtained. These changes in their characteristics led to an increase in SSA for the water and water-ethanol samples, while pore volume demonstrated a multiplied increase for all samples, reaching 0.593 cm³g^-1 for the water-acetone sample.

Injectable eggshell-derived hydroxyapatite-incorporated fibroin-alginate composite hydrogel for bone tissue engineering

Tissue engineering is a promising approach to repair and regenerate damaged or lost tissues or organs. In dental aspect, reconstruction of the resorbed alveolar bone after tooth extraction plays an important role in the success of dental substitution, especially in dental implant treatment. The hydroxyapatite (HA)-incorporated fibroin-alginate composite injectable hydrogel was fabricated to be used as scaffold for bone regeneration. HA was synthesized from eggshell biowaste. Fibroin was extracted from Bombyx mori cocoon. The synthesized HA, fibroin and alginate hydrogel were characterized. HA-incorporated fibroin-alginate hydrogel had decreased pore size and porosity compared with pure alginate hydrogel. Thermal analysis showed that hydrogel had a degradation peak of approximately 250 °C. Hydrogel could absorb water, with a swelling ratio of around 300% at 24 h. Hydrogel was degraded as time passed and almost completely degraded at day 7. Its compressive Young's modulus was approximately 0.04 ± 0.02 N/mm² to 0.10 ± 0.02 N/mm². Primary cytotoxicity test indicated non-toxic potential of the fabricated hydrogel. Increased ALP activity was observed in MC3T3-E1 cultured in HA-incorporated fibroin-alginate hydrogel. Results suggested the potential use of injectable HA fibroin-alginate hydrogel as dental scaffolding material. Further studies including in vivo examinations are needed prior to its clinical application.