PVDF reinforced with core–shell structured Mo@MoO3 fillers: effects of semi-conductor MoO3 interlayer on dielectric properties of composites

Core@Double-Shell Engineering of Zn Particles toward Elevated Dielectric Properties: Multiple Polarization Mechanisms in Zn@Znch@PS/PVDF Composites

Flexible dielectrics with large dielectric constant (ε') coupled with low loss are highly pursued in many applications. To bolster the ε' of raw Zn (zinc)/poly(vinylidene fluoride, PVDF) while maintaining pimping dielectric loss, in this study, the core@double-shell structured Zn@zinc carbonate (ZnCH)@polystyrene (PS) particles are first synthesized through a suspension polymerization of styrene, and then composited with PVDF to elevate the ε' and keep low loss of the composites. By optimizing the PS shells' thickness and tailoring the electrical resistivity of Zn@ZnCH@PS particles, both the slow inter-particle polarization and fast intra-particle polarization in the composites can be decoupled and synergistically tuned, thus, the Zn@ZnCH@PS/PVDF achieves a much higher ε' and lower dielectric loss, simultaneously, which far exceed the unmodified Zn/PVDF. Both experiment and theoretic calculation reveal that the double-shell ZnCH@PS not only induces and promotes multiple polarizations enhancing the composites' ε', especially at the optimized PS's thickness, but also maintains suppressed loss and conductivity thanks to their obvious barrier effect on long-range charge migration. The core@double-shell filler design strategy facilitates the development of polymer composites with desirable dielectric properties for applications in electronic and electrical power systems.

Effect of High-Entropy Spinel Ferrite (Mn0.2Zr0.2Cu0.2Ca0.2Ni0.2)Fe2O4 Doping Concentration on the Ferroelectric Properties of PVDF-Based Polymers

Polyvinylidene fluoride (PVDF)-based dielectric energy storage materials have the advantages of environmental friendliness, high power density, high operating voltage, flexibility, and being light weight, and have enormous research value in the energy, aerospace, environmental protection, and medical fields. To investigate the magnetic field and the effect of high-entropy spinel ferrite (Mn_0.2Zr_0.2Cu_0.2Ca_0.2Ni_0.2)Fe₂O₄ nanofibers (NFs) on the structural, dielectric, and energy storage properties of PVDF-based polymers, (Mn_0.2Zr_0.2Cu_0.2Ca_0.2Ni_0.2)Fe₂O₄ NFs were prepared via the use of electrostatic spinning methods, and (Mn_0.2Zr_0.2Cu_0.2Ca_0.2Ni_0.2)Fe₂O₄/PVDF composite films were prepared via the use of the coating method. The effects of a 0.8 T parallel magnetic field, induced for 3 min, and the content of high-entropy spinel ferrite on the relevant electrical properties of the composite films are discussed. The experimental results show that, structurally, the magnetic field treatment causes the originally agglomerated nanofibers in the PVDF polymer matrix to form a linear fiber chain with different fiber chains parallel to each other along the magnetic field direction. Electrically, the introduction of the magnetic field enhanced the interfacial polarization, and the (Mn_0.2Zr_0.2Cu_0.2Ca_0.2Ni_0.2)Fe₂O₄/PVDF composite film with a doping concentration of 10 vol% had a maximum dielectric constant of 13.9, as well as a low energy loss of 0.068. The high-entropy spinel ferrite (Mn_0.2Zr_0.2Cu_0.2Ca_0.2Ni_0.2)Fe₂O₄ NFs and the magnetic field influenced the phase composition of the PVDF-based polymer. The α-phase and γ-phase of the cohybrid-phase B1 vol% composite films had a maximum discharge energy density of 4.85 J/cm³ and a charge/discharge efficiency of 43%.