Composition tunable cobalt-nickel and cobalt-iron alloy nanoparticles below 10 nm synthesized using acetonated cobalt carbonyl

Controlled CO labilization of tungsten carbonyl precursors for the low-temperature synthesis of tungsten diselenide nanocrystals

We report a low-temperature colloidal synthesis of WSe2 nanocrystals from tungsten hexacarbonyl and diphenyl diselenide in trioctylphosphine oxide (TOPO). We identify TOPO-substituted intermediates, W(CO)5TOPO and cis-W(CO)4(TOPO)2 by infrared spectroscopy. To confirm these assignments, we synthesize aryl analogues of phosphine-oxide-substituted intermediates, W(CO)5TPPO (synthesized previously, TPPO = triphenylphosphine oxide) and cis-W(CO)4(TPPO)2 and fac-W(CO)3(TPPO)3 (new structures reported herein). Ligation of the tungsten carbonyl by either the alkyl or aryl phosphine oxides results in facile labilization of the remaining CO, enabling low-temperature decomposition to nucleate WSe2 nanocrystals. The reactivity in phosphine oxides is contrasted with syntheses containing phosphine ligands, where substitution results in decreased CO labilization and higher temperatures are required to induce nanocrystal nucleation.

The delicate balance of phase speciation in bimetallic nickel cobalt nanoparticles

Bimetallic nickel-cobalt nanoparticles are highly sought for their potential as catalytic and magnetic nanoparticles. These are typically prepared in organic solvents in the presence of strong stabilizing ligands such as tri-n-octylphosphine (TOP). Due to the variety of cobalt crystallographic phases and to the strong interaction of the ligands with the metallic surfaces, forming fcc nanoparticles rather than a phase mixture is a challenging endeavor. Here, using a two-step synthesis strategy that aims at a core-shell nickel-cobalt morphology, we demonstrated that many parameters have to be adjusted: concentration of the metal precursors, stoichiometry of TOP, and heating program from room temperature to 180 °C. We found optimized conditions to form size-controlled fcc NiCo nanoparticles from preformed Ni nanoparticles, and the phase attribution was confirmed with a combination of X-Ray diffraction on powder and X-Ray absorption spectroscopy at the Co K edge. We then investigated the early stages of Co nucleation on the nickel using a lower stoichiometry of Co, down to 0.05 equiv. vs. Ni. Using X-ray photoelectron spectroscopy and scanning transmission electron microscopy coupled to energy-dispersive X-Ray spectroscopy and electron energy loss spectroscopy, we showed that cobalt reacts first on the nickel nanoparticles but easily forms cobalt-rich larger aggregates in the further steps of the reaction.

Bimetallic Co/Al nanoparticles in an ionic liquid: synthesis and application in alkyne hydrogenation

CoAl- and Co₃Al-NPs are effective catalysts for alkyne-to-alkane hydrogenation with DIBAL-H as a co-catalyst under mild conditions (2 bar H₂, 30 °C).

Transition-Metal Nanoparticle Oxidation in a Chemically Nonhomogenous Environment Revealed by 2p3d Resonant X-ray Emission

X-ray absorption spectroscopy (XAS) is often employed in fields such as catalysis to determine whether transition-metal nanoparticles are oxidized. Here we show 2p3/2 XAS and 2p3d resonant X-ray emission spectroscopy (RXES) data of oleate-coated cobalt nanoparticles with average diameters of 4.0, 4.2, 5.0, 8.4, and 15.2 nm. Two particle batches were exposed to air for different periods of time, whereas the others were measured as synthesized. In the colloidal nanoparticles, the cobalt sites can have different chemical environments (metallic/oxidized/surface-coordinated), and it is shown that most XAS data cannot distinguish whether the nanoparticles are oxidized or surface-coated. In contrast, the high-energy resolution RXES spectra reveal whether more than the first metal layer is oxidized based on the unique energetic separation of spectral features related to the formal metal (X-ray fluorescence) or to a metal oxide (d-d excitations). This is the first demonstration of metal 2p3d RXES as a novel surface science tool.