Preparation and characterization of ZnTiO3–TiO2/pillared montmorillonite composite catalyst for enhanced photocatalytic activity

A Fresh Perspective on the Impact of ZnTiO3 Coupling on the Microstructure and Photocatalytic Properties of TiO2 Fabricated at Varied Temperatures

ZnTiO3/TiO2 composite photocatalysts were synthesized via the sol-gel technique, and the impact of varying heat treatment temperatures (470, 570, 670 °C) on their crystalline arrangement, surface morphology, elemental composition, chemical state, specific surface area, optical characteristics, and photocatalytic efficacy was systematically investigated. The outcomes revealed that, as the temperature ascends, pure TiO2 undergoes a transition from anatase to rutile, ultimately forming a hybrid crystal structure at 670 °C. The incorporation of ZnTiO3 engenders a reduction in the TiO2 grain dimensions and retards the anatase-to-rutile phase transition. Consequently, the specimens manifest a composite constitution of anatase and ZnTiO3. In contrast, for pure TiO2, the specimen subjected to 670 °C annealing demonstrates superior photocatalytic performance due to its amalgamated crystal arrangement. The degradation efficacy of methylene blue (MB) aqueous solution attains 91% within a 60-min interval, with a calculated first-order reaction rate constant of 0.039 min-1. Interestingly, the ZnTiO3/TiO2 composite photocatalysts exhibit diminished photocatalytic activity in comparison to pristine TiO2 across all three temperature variations. Elucidation of the photocatalytic mechanism underscores that ZnTiO3 coupling augments the generation of photogenerated charge carriers. Nonetheless, concurrently, it undermines the crystalline integrity of the composite, yielding an excess of amorphous constituents that impede the mobility of photoinduced carriers. This dual effect also fosters escalated recombination of photogenerated charges, culminating in diminished quantum efficiency and reduced photocatalytic performance.

Synthesis of the ZnTiO3/TiO2 Nanocomposite Supported in Ecuadorian Clays for the Adsorption and Photocatalytic Removal of Methylene Blue Dye

Currently, the study of semiconductor materials is very promising for the photocatalytic remediation of hazardous organic substances present in the air and water. Various semiconductors have been investigated in this interesting photo-assisted methodology, among them metal oxides such as ZnO, TiO2 and their derivatives. In this study, ZnTiO3/TiO2 was synthesized by the sol-gel method using Ti(OC3H7)4 and Zn(CH3COO)2 · 2H2O as reagents. The role of several conditions such as synthesis temperature and TiO2:ZnO proportion on the morphology and purity of compounds obtained was studied, and the suitable conditions for the synthesis of photocatalysts were determined. Various techniques were used to conduct a systematic investigation on the structural, morphological, and photocatalytic properties of ZnTiO3/TiO2. Scanning Electron Microscopy (SEM) images show that ZnTiO3/TiO2 have a typical particle size of approximately 100 nm with a quasi-spherical shape. The adsorption and photocatalytic activity were investigated by the decolorization of Methylene Blue (MB) as an organic contaminant under UV irradiation both in TiO2 and ZnTiO3/TiO2 supported over some Ecuadorian clays. The materials evaluated were prepared in the shape of 0.2 cm (diameter) and 1.0 cm (length) cylindrical extrudates. The degradation percentage of MB obtained was 85% approximately after 150 min of irradiation. The results obtained allow us to conclude that these synthesized materials can be used as adsorbents and photocatalysts.

ZnO Surface Doping to Enhance the Photocatalytic Activity of Lithium Titanate/TiO2 for Methylene Blue Photodegradation under Visible Light Irradiation

Wastewater contaminated with dyes produced by textile industries is a major problem due to inadequate treatment prior to release into the environment. In this paper, the ability of ZnO to enhance the interfacial photocatalytic activity of lithium titanate/TiO2 (LTO/TiO2) for the photodegradation of methylene blue (MB) under visible light irradiation (4.38 mW/cm2) was assessed. The ZnO-doped lithium titanate/TiO2 (ZnO/LTO/TiO2) was synthesized using a combination of hydrothermal and wetness impregnation methods. The high-resolution transmission electron microscope (HRTEM) and X-ray Diffraction (XRD) analyses indicate that the ZnO/LTO/TiO2 contain several phases (ZnO, LTO, and TiO2). The adsorption capacity of LTO/TiO2 (70%) was determined to be higher compared to its photocatalytic activity (25%), which is attributed to the strong interaction between the Li and surface oxygen atoms with the MB dye molecules. The introduction of ZnO improved the photocatalytic ability of LTO/TiO2 by 45% and extended the life span of ZnO/LTO/TiO2. The ZnO/LTO/TiO2 can be reused without a significant loss up to four cycles, whereas LTO/TiO2 had reduced adsorption after the second cycle by 30%. The ZnO increased the surface defects and restrained the photo-induced electrons (e−) from recombining with the photo-induced holes (h+). Scavenging tests indicated that the hydroxyl radicals played a major role in the photodegradation of MB, which is followed by electrons and holes.