Radiopacity of fiber-reinforced resins

A Novel High-Visibility Radiopaque Tantalum Marker for Biliary Self-Expandable Metal Stents

Background/Aims

Radiopaque metal markers are required to improve X-ray absorption by self-expandable metal stents (SEMSs) to enable precise stent placement. A new tantalum radiopaque marker was recently developed using an ultrasonic spray technique. The aim of the present study was to evaluate the safety and visibility of tantalum markers.

Methods

A total of three beagle dogs were used for a gastrointestinal tract absorption test. Five tantalum markers were placed in the stomach of each dog endoscopically. Excreted tantalum markers were collected, and their weights were compared to the original weights. In radiopacity tests, marker radiopacities on X-ray images were quantified using ImageJ software and compared with those of commercially available metal markers. Finally, the radiographic images of six patients who underwent biliary SEMS placement using tantalum marker Nitinol SEMSs (n=3) or gold marker Nitinol SEMSs (n=3) were compared with respect to marker brightness on fluoroscopic images.

Results

Absorption testing showed that the marker structures and weights were unaffected. Radiopacity tests showed that the mean brightness and total brightness scores were greater for tantalum markers (226.22 and 757, respectively) than for gold (A, 209 and 355, respectively; B, 204.96 and 394, respectively; C, 194.34 and 281, respectively) or platinum markers (D, 203.6 and 98, respectively). On fluoroscopic images, tantalum markers had higher brightness and total brightness scores (41.47 and 497.67, respectively) in human bile ducts than gold markers (28.37 and 227, respectively).

Conclusions

Tantalum markers were found to be more visible than other commercially available markers in X-ray images and to be resistant to gastrointestinal absorption.

Preparation and characterization of high radio-opaque E-glass fiber-reinforced composite with iodine containing methacrylate monomer

OBJECTIVE

The purpose of this study was to prepare radio-opaque E-glass fiber-reinforced composite (EFRC) with synthesized iodine containing methacrylate monomer.

METHODS

The synthesized iodine containing methacrylate monomer 2-hydroxy-3- methacryloyloxypropyl(2,3,5- triiodobenzoate) (HMTIB) was mixed with Bis-GMA and MMA in different mass ratio to prepare resin impregnating solution (RIS), and RIS without HMTIB was used as control. CQ and DMAEMA were added as photoinitiation system. E-glass fiber was thoroughly wetted by resin impregnating solution to prepare radio-opaque EFRC. Degree of double bond conversion (DC) was investigated by FT-IR analysis. Fiber volume fraction was analyzed by combustion and gravimetric analyzes. The Flexural strength (FS) and modulus (FM) of EFRC were measured using a three-point bending set up. Water sorption (WS) and solubility (SL) were measured until the mass variation of EFRC in distilled water kept stable. Radiographs were taken to determine the radiopacity of EFRC.

RESULTS

The FT-IR and ¹H NMR spectra of HMTIB revealed that it was the same as designed. ANOVA analysis revealed that increasing HMTIB concentration in RIS would decrease DC and increase fiber volume fraction. When compared with control EFRC, all of HMTIB containing EFRCs had higher or comparable FS and FM, no matter before or after water immersion. WS of EFRC decreased with increasing HMTIB concentration, while SL was nearly kept the same. Radiopacity of EFRC increased with increasing HMTIB concentration.

SIGNIFICANCE

The synthesized monomer HMTIB could be used to prepare EFRC with high radiopacity. Moreover, HMTIB containing EFRC would also have high mechanical properties and low WS.