Preparation of the Mn/Co mixed oxide catalysts for low-temperature CO oxidation reaction

Highly efficient Rh-doped MnO2 nanocatalysts for complete elimination of CO at room temperature

Obliteration of carbon monoxide is significant due to its hazardous effect on human health and potential application in different fields. Catalytic CO oxidation at lower temperature is the most convenient method to diminish the toxicity of CO. The low-cost catalysts which are exhibiting higher activity at lower temperature with good stability are in demand. The nanosized Rh-doped MnO2 catalysts have been prepared by dextrose-assisted co-precipitation method. Catalytic CO oxidation reaction was carried out over these prepared nanocatalysts under environmentally suitable conditions. XRD confirms the phase formation of prepared catalysts. These samples exhibit rod-like morphology with thickness of rods of less than 10 nm which is substantiated from electron microscopy images. XPS data reveals the oxidation state of Mn (+ 4) and Rh (+ 3). These catalysts are highly active for CO oxidation reaction at lower temperature, and one showed complete CO conversion at room temperature. The time-on-stream studies revealed that these catalysts are highly stable for CO oxidation for several hours. These catalysts are decidedly stable in moist condition and also showed higher activity in the presence of moisture, indicating participation of moisture in the oxidation reaction at above room temperatures.

Insights into effects of grain boundary engineering in composite metal oxide catalysts for improving catalytic performance

Volatile Organic Compounds (VOCs) have long been a threat to human health. However, designing economical and efficient transition metal composite oxide catalysts for VOCs purification remains a challenge. Herein, this study demonstrates the enormous potential of grain boundary engineering in facilitating VOCs decomposition over ordered mesoporous composite oxide denoted as 3D-MnxCoy (x, y = 1, 3, 5, 7, 9). Specifically, the three-dimensional (3D) Mn7Co1 catalyst shows 100% ethyl acetate removal efficiency for a continuous airflow containing 1000 ppm ethyl acetate over 60000 h-1 space velocity at 160 °C. Mechanism study suggests that the high catalytic performance originates from the lattice distortion caused by the introduction of heteroatoms, along with the size effect of nanopore walls, which leads to the formation of various grain boundaries on the catalyst surface. The presence of grain boundaries facilitates the generation of oxygen vacancies, thus promoting the migration and activation of oxygen species. Furthermore, the near-atmospheric pressure X-ray photoelectron spectroscopy (NAP- XPS) monitoring results reveal that the bimetallic synergy enhanced by grain boundary accelerates the catalytic reaction rate of VOCs through Mn3++Co3+↔Mn4++Co2+ redox cycle. This study may shed light on the great potential of ordered mesoporous bimetallic oxide catalysts in VOCs pollution control.

Revealing the intrinsic nature of Ni-, Mn-, and Y-doped CeO2 catalysts with positive, additive, and negative effects on CO oxidation using operando DRIFTS-MS

The catalytic activity of a transition metal (host) oxide can be influenced by doping with a second cation (dopant), but the key factors dominating the activity of the doped catalyst are still controversial. Herein, CeO2 doped with Ni, Mn, and Y catalysts prepared using aerosol pyrolysis were used to demonstrate the positive, negative, and additive effects on CO oxidation as a model reaction. Various characterization results indicated that Ni, Mn, and Y had been successfully doped into the CeO2 lattice. The catalytic activities of each catalyst for CO conversion were in the order of Ni-CeO2 > Mn-CeO2 > CeO2 > Y-CeO2. Operando DRIFTS-MS and various characterization methods were applied to reveal the intrinsic nature of the doping effects. The accumulation rate of the surface bidentate carbonates determined the CO oxidation. A definition to evaluate the doping effect was proposed, which is anticipated to be useful for developing a rational catalyst with a high CO oxidation activity. The CO oxidation reactivities displayed strong correlations with the surface factors obtained from operando DRIFTS-MS analysis and the structure factors from XPS and Raman analyses.

Property and Reactivity Relationships of Co3O4 with Diverse Nanostructures for Soot Oxidation

Cobalt oxide (Co₃O₄) nanostructures with different morphologies (nanocubes, nanoplates, and nanoflowers) were synthesized by a simple hydrothermal method and used for catalytic oxidation of soot particles. Through the study of the physicochemical properties of the catalysts, the key factors affecting the performance of soot oxidation were investigated. The results showed that all three kinds of Co₃O₄ nanocrystals exhibited excellent low-temperature activity in catalytic oxidation of soot, and the Co₃O₄ nanoflowers showed higher oxidation activity of soot compared with Co₃O₄ nanocubes and Co₃O₄ nanoplates, whose T _m was only 370 °C. The excellent activity of Co₃O₄ nanoflowers was due to the large amount of Co³⁺ and lattice oxygen on their surface and highly defective structure, which promoted the adsorption and activation of oxygen species. The large crystallite size and few surface defects were the main reasons for the poor catalytic performance of Co₃O₄ nanocubes. During soot oxidation, the crystallite size of the catalysts and the contact between the catalysts and soot played a significant role in the catalytic performance.

Interactions between CO oxidation and selective catalytic reduction of NO with NH3 over Mn-based catalysts

The α-MnO2-Cu catalyst has a high NO and CO removal rate. CO reduced the NH3-SCR activity by inhibiting NO adsorption. NH3 negatively affected CO oxidation by minimizing the formate intermediate. NO decomposed intermediates to promote CO oxidation.