Synthesis of Nanoscale Tips Using Femtosecond Laser Radiation under Ambient Condition

Study of nanostructure growth with nanoscale apex induced by femtosecond laser irradiation at megahertz repetition rate

Leaf-like nanostructures with nanoscale apex are induced on dielectric target surfaces by high-repetition-rate femtosecond laser irradiation in ambient conditions. We have recently developed this unique technique to grow leaf-like nanostructures with such interesting geometry without the use of any catalyst. It was found to be possible only in the presence of background nitrogen gas flow. In this synthesis method, the target serves as the source for building material as well as the substrate upon which these nanostructures can grow. In our investigation, it was found that there are three possible kinds of nanotips that can grow on target surfaces. In this report, we have presented the study of the growth mechanisms of such leaf-like nanostructures under various conditions such as different laser pulse widths, pulse repetition rates, dwell times, and laser polarizations. We observed a clear transformation in the kind of nanotips that grew for the given laser conditions.

Characterization of MHz pulse repetition rate femtosecond laser-irradiated gold-coated silicon surfaces

In this study, MHz pulse repetition rate femtosecond laser-irradiated gold-coated silicon surfaces under ambient condition were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction analysis (XRD), and X-ray photoelectron spectroscopy (XPS). The radiation fluence used was 0.5 J/cm2 at a pulse repetition rate of 25 MHz with 1 ms interaction time. SEM analysis of the irradiated surfaces showed self-assembled intermingled weblike nanofibrous structure in and around the laser-irradiated spots. Further TEM investigation on this nanostructure revealed that the nanofibrous structure is formed due to aggregation of Au-Si/Si nanoparticles. The XRD peaks at 32.2°, 39.7°, and 62.5° were identified as (200), (211), and (321) reflections, respectively, corresponding to gold silicide. In addition, the observed chemical shift of Au 4f and Si 2p lines in XPS spectrum of the irradiated surface illustrated the presence of gold silicide at the irradiated surface. The generation of Si/Au-Si alloy fibrous nanoparticles aggregate is explained by the nucleation and subsequent condensation of vapor in the plasma plume during irradiation and expulsion of molten material due to high plasma pressure.