Preparation of manganese oxide nanoparticles by thermal decomposition of nanostructured manganese carbonate

Research progress in green synthesis of manganese and manganese oxide nanoparticles in biomedical and environmental applications - A review

Nanomaterials and nanotechnology have this unassailable position for environmental remediation and medicine. Currently, global environmental pollution and public health problems are increasing and need to be urgently addressed. Manganese (Mn) is one of the essential metal elements for plants and animals, it is necessary to integrate with nanotechnology. Mn and Mn oxide (MnO) nanoparticles (NPs) have applications in dye degradation, biomedicine, electrochemical sensors, plant and animal growth, and catalysis. However, the current research is limited, especially in terms of optimal synthesis of Mn and MnO NPs, separation, purification conditions, and the development of potential application areas is too basic and do not support by in-depth studies. Hence, this review comprehensively discusses the classification, green synthesis methods, and applications of Mn and MnO NPs in biomedical, environmental, and other fields and gives a perspective for the future.

Tuning the size and composition of manganese oxide nanoparticles through varying temperature ramp and aging time

Manganese oxide (MnO) nanoparticles (NPs) can serve as robust pH-sensitive contrast agents for magnetic resonance imaging (MRI) due to Mn2+ release at low pH, which generates a ~30 fold change in T1 relaxivity. Strategies to control NP size, composition, and Mn2+ dissolution rates are essential to improve diagnostic performance of pH-responsive MnO NPs. We are the first to demonstrate that MnO NP size and composition can be tuned by the temperature ramping rate and aging time used during thermal decomposition of manganese(II) acetylacetonate. Two different temperature ramping rates (10°C/min and 20°C/min) were applied to reach 300°C and NPs were aged at that temperature for 5, 15, or 30 min. A faster ramping rate and shorter aging time produced the smallest NPs of ~23 nm. Shorter aging times created a mixture of MnO and Mn3O4 NPs, whereas longer aging times formed MnO. Our results indicate that a 20°C/min ramp rate with an aging time of 30 min was the ideal temperature condition to form the smallest pure MnO NPs of ~32 nm. However, Mn2+ dissolution rates at low pH were unaffected by synthesis conditions. Although Mn2+ production was high at pH 5 mimicking endosomes inside cells, minimal Mn2+ was released at pH 6.5 and 7.4, which mimic the tumor extracellular space and blood, respectively. To further elucidate the effects of NP composition and size on Mn2+ release and MRI contrast, the ideal MnO NP formulation (~32 nm) was compared with smaller MnO and Mn3O4 NPs. Small MnO NPs produced the highest amount of Mn2+ at acidic pH with maximum T1 MRI signal; Mn3O4 NPs generated the lowest MRI signal. MnO NPs encapsulated within poly(lactide-co-glycolide) (PLGA) retained significantly higher Mn2+ release and MRI signal compared to PLGA Mn3O4 NPs. Therefore, MnO instead of Mn3O4 should be targeted intracellularly to maximize MRI contrast.

Synthesis and Properties of Nanosized Stoichiometric Cobalt Ferrite Spinel

Nanoparticles with controllable sizes of ferrite spinel CoFe₂O₄ were formed by thermal treatment of cobalt-iron glycerolate. Thermal behavior during the heating was studied by differential thermal analysis combined with thermogravimetry. The precursor, as well as the prepared nanoparticles, were analyzed by a broad spectrum of analytic techniques (X-Ray photoelectron spectroscopy (XPS), X-Ray diffraction (XRD), Energy dispersive spectroscopy (EDS), Atomic absorption spectroscopy (AAS), Scanning electron microscopy (SEM), and Raman spectroscopy). The particle size of nanoparticles was obtained from Transmission electron microscopy and also calculated using Scherrer formula. A vibrating sample magnetometer (VSM) in a Physical Property Measurement System was used to analyze the magnetic properties of nanoparticles.