Anisotropy and NMR spectroscopy

A new solvent-free pathway for inducing quaternized lignin-derived high molecular weight polymer

In this work, kraft lignin (KL) was polymerized with vinylbenzyl chloride (VBC) in a molar ratio of 1.8:1 (KL: VBC) using sodium persulfate (Na2S2O8) as an initiator at pH 9-10 and temperature of 80-90 °C for 3 h to produce polymer kraft lignin-g-poly(4-vinylbenzyl chloride) KL-poly(VBC) 1. Then, the grafting reaction was conducted with two different imidazole-based monomers of different side-chain lengths (methyl and n-butyl), namely, 1-methylimidazole (MIM), 1-n-butylimidazole (BIM), which led to the formation of novel polymers, kraft lignin-g-poly(4-vinylbenzyl-1-methylimidazolium chloride) KL-poly(VBC-MIM) 2a and kraft lignin-g-poly(4-vinylbenzyl-1-n-butyl imidazolium chloride) KL-poly(VBC-BIM) 2b. The polymer 2a generated a larger molecular weight polymer with a higher charge density and solubility than polymer 2b since the n-butyl group would cause steric hindrance and weaker monomer to react with intermediate polymer 1 in the second stage. The contact angle analysis confirmed more hydrophilicity of polymer 2a, and elemental analysis confirmed the more successful polymerization of polymer 2a. Applying the generated polymers as flocculants for a kaolin suspension confirmed that polymer 2a had similar performance with commercial cationic polyacrylamide (CPAM) flocculants, even though polymer 2a had a smaller molecular weight. This polymerization offers a promising pathway for generating cationic polymers with excellent performance as a flocculant for suspensions.

From nano to the macro: tuning hierarchical aggregation of thermoresponsive PEG/PCL-based polyurethanes via molar mass/composition control

Amphiphilic hyperbranched polyurethanes (HPUs) based on PEG and PCL are promising for several biomedical applications. However, the lack of control over the molar mass and composition hinders a deep understanding of the aqueous self-assembly of HPUs. In this paper, the control over the HPU molar mass and composition was provided by dynamic urea bond-mediated polymerization (DUBMP), enabling a careful evaluation of their aqueous self-assembly by 1H NMR, DLS, and Cryo-TEM. HPUs containing a single PCL block per chain self-assemble into nanoaggregates (Rh ≈ 10 nm) in water up to its cloud-point temperature (Tcp) of 34 °C. On the other hand, HPUs with more than one PCL block per chain self-assemble into nanoaggregates and their clusters below Tcp. In this case, the solution behavior can be tuned by the HPU molar mass. Increasing $$\overline{{\mathrm{M} }_{\mathrm{w}}}$$ M w ¯ from 4 to 19 kDa, HPUs of similar composition can form colloidally stable cluster suspensions ($$\overline{{\mathrm{M} }_{\mathrm{w}}}$$ M w ¯ = 4 kDa) and phase separate into a denser liquid aggregate–cluster phase ($$\overline{{\mathrm{M} }_{\mathrm{w}}}$$ M w ¯ = 7 kDa) or into a highly viscous aggregate-network phase ($$\overline{{\mathrm{M} }_{\mathrm{w}}}$$ M w ¯ = 19 kDa). This type of control over the hierarchical aggregation of HPUs was reported for the first time and is interesting for biomedical applications.

Graphical abstract