Electrochemical Fabrication of Well-Defined Spherical Iridium Nanoparticles and Electrocatalytic Activity towards Carbon Monoxide Adlayer Oxidation

A Simple and Fast Method to Synthesize Cubic Iridium Nanoparticles with Clean Surface Free from Surfactants

Cubic Iridium nanoparticles without any surfactants on the surface have been synthesized successfully in this work. The process of synthesis was quite simple by just injecting one drop of 400 µL solution containing Iridium precursor onto Cu foil (1 cm × 1 cm), and through galvanic reaction between the Ir precursor and Cu foil, the cubic Iridium nanoparticle could be obtained quite quickly (<30 s). The Cu foil played the roles of both reducing agent and substrate. This method could also be employed to synthesize cubic nanoparticles of other Pt-group metals such as Rh. By employing this method, cubic metal nanoparticles with surfactant-free surfaces could be produced economically and efficiently, and as a result, a realistic relationship between structure and catalytic activity could be established.

Nanoengineered Ircore@Ptshell Nanoparticles with Controlled Pt Shell Coverages for Direct Methanol Electro-Oxidation

The design and application of bimetallic alloy nanoparticles (NPs) for electrocatalytic applications are challenged by the need to clearly identify and understand the individual effect of each component. In the present work, the focus has been on PtIr NPs, with alloyed NPs being previously shown to be active toward the methanol oxidation reaction (MOR), but for which the mode of action of the Ir component remains uncertain. We have therefore nanoengineered a family of Ir_core@Pt_shell NPs, using a modified polyol method, to control the Pt shell coverage (up to 2 monolayers) and thus to allow the separation of the bifunctional and electronic effects of Ir on the Pt activity. It is shown that the Ir core size and crystallinity do not change with the deposition of the Pt shell, as confirmed by transmission electron microscopy and X-ray diffraction. CO stripping and hydrogen underpotential deposition/removal were used for the first time to determine the surface composition of the Ir_core@Pt_shell NPs. It is shown that the Ir_core enhances the MOR activity of the Pt_shell primarily through the bifunctional effect, with an optimum Pt coverage of 0.4 of a monolayer. At 60 °C, an additional electronic effect of Ir on Pt can be discerned, causing an inhibition in the MOR rate by weakening the adsorption of methanol on the Pt_shell, thus helping to remove the adsorbed CO intermediate from the shell surface.