Comparative Evaluation of Dimensional Accuracy and Tensile Strength of a Type IV Gypsum Using Microwave and Air Drying Methods

Comparative evaluation of diametral tensile strength of phosphate-bonded investment (ringless) material by using air-drying method, conventional hot air oven, microwave oven, and combination of microwave and conventional oven: An in vitro study

AIM

This study evaluated and compared the diametral tensile strength (DTS) of phosphate-bonded investment (PBI) material (ringless) used in removable cast partial denture fabrication.

SETTINGS AND DESIGN

Comparative - Invitro study.

MATERIALS AND METHODS

The PBI material, Wirovest used in this study was subjected to four different drying methods. A total of 80 specimens were prepared in a cylindrical form; 20 specimens were air dried for 2 h, 20 specimens were dried in a conventional oven at 230°C for 1 h, 20 specimens were dried in microwave oven at 600 W for 10 min, and remaining 20 specimens were dried first in microwave oven and then in conventional oven. The dried specimens were tested at 2-h interval for diametral compression at a crosshead speed of 0.5 cm/min.

STATISTICAL ANALYSIS USED

Pairwise analysis.

RESULTS

The microwave drying technique and drying by combination method resulted in greater DTS, respectively.

CONCLUSION

Within the limitation of this study, PBI specimens dried in microwave oven at 600W for 10 min increased the diametral strength and are also a time-saving procedure.

Analysis of the Mechanical Behavior and Surface Rugosity of Different Dental Die Materials

AIM

This work evaluated the mechanical and surface behavior of different die materials. The studied materials are polyurethane resin Exakto-Form (Bredent), Gypsum type IV, Fuji Rock EP (Gc), and Durone (Dentsply).

MATERIALS AND METHODS

Two metallic matrices molded in polyvinyl siloxane provided 30 cylindrical test specimens for the diametral compression test and 30 hemispherical test specimens for the surface rugosity test. The cylindrical test specimens were submitted to tests of diametral compression strength using a DL2000 universal assay machine, with a load cell of 2000 Kgf and constant speed of 1 mm/min connected to the software. Kruskal-Wallis and Dunn's nonparametric tests were used to analyze the results. The hemispheres were submitted to the surface rugosity assay using a SJ201-P rugosimeter with a sensitivity of 300 μm, speed of 0.5 mm/s, and cut-off of 0.8 mm, and the readings were taken on the convex surface of the test specimens and metallic matrix. Results were analyzed using with Fisher's least significant differences test (LSD) and Dunnett's test.

RESULTS

Kruskal-Wallis test showed significant difference between die materials for diametral compression strength (P = 0.002). Dunn's test showed significantly higher values for modified polyurethane resin (Exakto-Form). The gypsum type IV, which did not significantly differ regarding diametral compression strength, showed 34.0% (Durone) and 42.7% (Fuji Rock) lower values in comparison to Exakto-Form.

CONCLUSION

Within the parameters adopted in this study, it is possible to conclude that Exakto-Form polyurethane resin showed higher resistance to compression and was closer to the metallic matrix rugosity, and, along with the gypsum type IV Durone, showed better reproducibility of details relative to the Fuji Rock.