Preparation and properties of propylene oxide and octenylsuccinic anhydride modified potato starches

Investigation of dual modification on physicochemical, morphological, thermal, pasting, and retrogradation characteristics of sago starch

The aim of this study was to evaluate the characteristics of dually modified sago starch by acid hydrolysis (AH)-hydroxypropylation (HP). For this purpose, sago starch was modified with the combination by AH (5-20 h hydrolysis times) followed by HP (5%-25% ratio of propylene oxide) processes. The results showed that the dual modification of the sago starch structure didn't have a significant effect on the size of starch granules, and the granule size was in the range of 0.005-0.151 µm; however, the pasting properties and the glass transition temperature decreased significantly (p < .05). Increasing the level of propylene oxide from 5% to 25% caused a significant increase in the substitution degree (DS) and swelling ability of starches and reduced the syneresis, while with increasing acid hydrolysis time from 5 h to 20 h, starch swelling decreased and syneresis increased (p < .05). AH process at high hydrolysis times (20 h) increased the gelatinization temperatures and decreased retrogradation temperatures. Increasing the level of propylene oxide in both single and dual modification reduced the temperatures and enthalpy of gelatinization and retrogradation of sago starch. In summary, dually modified sago starch has a great potential to use in specific food products such as frozen dough or frozen bakery products.

The effects of dual modification on functional, microstructural, and thermal properties of tapioca starch

The aim of this study was to investigate the effects of dual modification on the functional, microstructural, and thermal properties of tapioca starch. Tapioca starch was first hydrolyzed by 0.14 M HCl for 0, 6, 12, 18, and 24 hr and then hydroxypropylated by adding 0%, 10%, 20%, and 30% (v/w) propylene oxide. The degree of hydroxypropylation, solubility, water absorption, rheological, thermal, and microstructure characterization of dually modified tapioca starch was determined. Hydroxypropylation did not cause any considerable changes in the starch granular size and shape of tapioca starch. Acid hydrolysis disrupts the starch granules, and the starches with smaller sizes were produced. The degree of molar substitution (DS) of dual modified starches ranged from 0.118 to 0.270. The dual modified starches significantly had higher solubility than native starch (p < .05). Hydrolysis of starches with acid decreases swelling power while hydroxypropylation increases the swelling power. The results also showed lower gelatinization (To, Tp, Tc, and ΔH) and pasting parameters (the peak and final viscosity, peak time, and pasting temperature) for the dual modified starches than other treatments. In summary, this study showed that dually modified tapioca starch has potential application in dip molding and coating.

Dual modification of various starches: Synthesis, properties and applications

The problems associated with native starches (NSs) and single modified starches were stated in order to justify dual modification of various starches. Broadly, there are two types of dual modification, i.e., homogeneous dual modification and heterogeneous dual modification. The combination of two physical modifications, e.g., (extrusion/annealing); two chemical modifications, e.g., (succinylation/cross-linking) and two enzymes modification (α-amylase/pullulanase) falls under the former classification and the latter classification is the combination of two of each of the differently stated modifications, e.g., acetylation/annealing, extrusion/succinylation, and microwave-assisted phosphorylation, etc. The classification, synthesis, properties and applications of dually modified starches were discussed. There is an attempt to elucidate the problems of each of the single modification in order to justify dual modifications. In dual modifications, the order of reactions, the reaction conditions, the medium of reaction, and the botanical sources of the various starches are very important parameters.