Effect of Electron Beam Irradiation on the Mechanical and Thermal Properties of Ternary Polyamide Copolymer

Evaluation of Cross-Linked Polyamide 6 Micro-Indentation Properties: TAIC Concentration and Electron Radiation Intensity

Nowadays, technical practice puts emphasis on improving selected material properties of polymers which could lead to new applications. Material properties can be modified in numerous ways, among which is radiation treatment. This study looks into the influence of beta radiation on several properties of polyamide 6, e.g., indentation hardness, modulus and creep. Main changeable parameters were the concentration of triallyl isocyanurate (TAIC), which promotes cross-linking, and intensity of radiation. The concentration was in the range from 2 to 6 wt.%, while the radiation dose was 0, 66, 99 and 132 kGy. The treated materials were measured for indentation hardness, modulus and creep. Degree of cross-linking was verified by thermo-mechanical analysis (TMA), while degradation processes was investigated by Fourier-transform infrared spectroscopy (FTIR). The results indicate that electron radiation positively affects the tested material properties. The best results were seen in polyamide with 6 wt.% of TAIC, which demonstrated a 38% improvement in mechanical properties after exposure to 132 kGy. This improvement in properties affects the final parts and their application (e.g., in the automotive industry-engine parts; in electrical engineering-insulation of wires and cables; and in industry-pipes for underfloor heating, etc.).

Effects of Extrusion and Irradiation on the Mechanical Properties of a Water–Collagen Solution

This article describes 1D extension tests on bovine collagen samples (8% collagen in water). At such a high collagen concentration, the mechanical properties of semi-solid samples can be approximated by hyperelastic models (two-parametric HGO and Misof models were used), or simply by Hooke’s law and the modulus of elasticity E. The experiments confirm a significant increase in the E-modulus of the samples irradiated with high-energy electrons. The modulus E~9 kPa of non-irradiated samples increases monotonically up to E~250 kPa for samples absorbing an e-beam dose of ~3300 Gy. This amplification is attributed to the formation of cross-links by irradiation. However, E-modulus can be increased not only by irradiation but also by exposure to a high strain rate. For example, soft isotropic collagen extruded through a 200 mm long capillary increases the modulus of elasticity from 9 kPa to 30 kPa, and the increase is almost isotropic. This stiffening occurs when the corrugated collagen fibers are straightened and are aligned in the flow direction. It seems that the permanent structural changes caused by extrusion mitigate the effects of the ex post applied irradiation. Irradiation of extruded samples by 3300 Gy increases the modulus of E-elasticity only three times (from 30 kPa to approximately 90 kPa). Extruded and ex post irradiated samples show slight anisotropy (the stiffness in the longitudinal direction is on an average greater than the transverse stiffness).