Porous Cellulose Acetate by Specific Solvents with Water Pressure Treatment for Applications to Separator and Membranes

Structure modification and property improvement of plant cellulose: Based on emerging and sustainable nonthermal processing technologies

Cellulose has attracted high attention due to its advantages of abundant resources, renewable and biodegradable. Modification of natural plant cellulose has become a hot topic worldwide. Conventional chemical modification methods commonly cause great damage to the environment. The current review presents the effects of innovative, eco-friendly and sustainable nonthermal processing technologies on cellulose structure and properties. Typical techniques include high pressure processing, cold plasma, ultrasonic and irradiation treatment. Their superiorities in the modification of cellulose are highlighted, and the advantages and limitations of nonthermal processing technologies for plant cellulose modification are also discussed. Nonthermal processing technologies can improve cellulose functional properties by playing an important role in the chemical bonds of the molecular chains, crystalline regions or amorphous parts through energy or active particles generated in the process, or promoting the crosslinking and graft copolymerization of cellulose molecules. The development of modified cellulose functional materials will have wider applications.

Study on the Preparation of Cellulose Acetate Separation Membrane and New Adjusting Method of Pore Size

As a kind of eco-friendly (biodegradable) material and with a natural anti-fouling ability, cellulose acetate (CA) is more suitable for single-use membrane (especially in bioprocess). In this study, the method for preparing CA membrane by Vapor-assisted Nonsolvent Induced Phase Separation (VNIPS) was studied. The influences of ratio compositions (solid content, acetone/N,N-Dimethylacetamide ratio, glycerol/CA ratio) and membrane preparation conditions (evaporation time, evaporation temperature and humidity) on the microstructure and other properties were systematically evaluated. Results indicated that acetone/N,N-Dimethylacetamide ratio and glycerol/CA ratio had great influence on the cross-section structure of membranes. Additionally, the membrane with homogeneous sponge-like porous structure could be prepared stably within certain limits of ratios. Under the premise of keeping the content of other components fixed, the separation membrane with a full sponge pore structure can be obtained when the ratio of glycerol/CA is ≥2.5 or the acetone/solvent ratio is between 0.25 and 0.5. Evaporation time and temperature, humidity and other membrane preparation conditions mainly affected the surface morphology and the pore size. This kind of high-performance membrane with homogeneous sponge-like pore and controllable surface morphology could be potentially used for bioseparation processes.

Nanocomposite Film Based on Cellulose Acetate and Lignin-Rich Rice Straw Nanofibers

Nanofibers isolated from unbleached neutral sulfite rice straw pulp were used to prepare transparent films without the need to modify the isolated rice straw nanofibers (RSNF). RSNF with loading from 1.25 to 10 wt.% were mixed with cellulose acetate (CA) solution in acetone and films were formed by casting. The films were characterized regarding their transparency and light transmittance, microstructure, mechanical properties, crystallinity, water contact angle, porosity, water vapor permeability, and thermal properties. The results showed good dispersion of RSNF in CA matrix and films with good transparency and homogeneity could be prepared at RSNF loadings of less than 5%. As shown from contact angle and atomic force microscopy (AFM) measurements, the RSNF resulted in increased hydrophilic nature and roughness of the films. No significant improvement in tensile strength and Young’s modulus was recorded as a result of adding RSNF to CA. Addition of the RSNF did not significantly affect the porosity, crystallinity and melting temperature of CA, but slightly increased its glass transition temperature.