Surface and Subsurface Layers Defects Analysis After WEDM Affecting the Subsequent Lifetime of Produced Components

Analysis of Machinability and Crack Occurrence of Steels 1.2363 and 1.2343ESR Machined by Die-Sinking EDM

Die-sinking electric discharge machining (EDM) is an indispensable technological operation, especially in the production of molds and all internal and external shapes and cavities. For this reason, the effect of machine parameter settings (open-voltage, pulse current, pulse on time, and pulse off time) on the machining of two types of steels, 1.2363 and 1.2343ESR, was carefully investigated using graphite or copper electrodes in 10 mm × 10 mm or 100 mm × 100 mm shapes. For this purpose, a two-level half factor experiment was performed with one replication at the corner points and two replications at the central points, with a total of 80 rounds. The subject of the evaluation was the topography and morphology of machined surfaces including a detailed analysis of surface and subsurface defects in the form of cracks including the creation of regression equations describing the probability of crack occurrence. Furthermore, a study of the local hardness change in the subsurface area was performed, and lamellas were also made and studied by transmission electron microscopy. It has been found that by using die-sinking EDM, it is possible to effectively predict the probability of cracking on machined surfaces and also on machine 1.2363 and 1.2343ESR steels with a very good surface quality of Ra 1.9 and 2.1 µm using graphite electrodes. These findings will ensure the production of parts with the required surface quality without cracks, which is a crucial aspect for maintaining the required functionality and service life of the parts.

Analysis of the Machinability of Copper Alloy Ampcoloy by WEDM

The unconventional technology of wire electrical discharge machining is widely used in all areas of industry. For this reason, there is always an effort for efficient machining at the lowest possible cost. For this purpose, the following comprehensive study has been carried out to optimize the machining of the copper alloy Ampcoloy 35, which is particularly useful in plastic injection moulds. Within the study, a half-factor experiment of 2^5-1 with 10 axial points and seven central points of a total of 33 rounds was carried out, which was focused on the response monitoring of the input factors in the form of the machine parameters setup: gap voltage, pulse on time, pulse off time, discharge current, and wire speed. Based on the study of the response in the form of cutting speed and surface topography, their statistical models were created, while the optimal setting of machine parameters was determined to maximize the cutting speed and minimize the topography parameters. Further, a detailed cross-sectional analysis of surface and subsurface layer morphology was performed using electron microscopy including chemical composition analysis. In order to study microstructural changes in the material at the atomic level, a lamella was created, which was then studied using a transmission electron microscope.

The Influence of WEDM Parameters Setup on the Occurrence of Defects When Machining Hardox 400 Steel

The unconventional technology wire electrical discharge machining is a highly used technology for producing precise and indented shaped parts of all materials that are at least electrically conductive. Its wide use makes this technology applicable in almost all branches of industry, even in the automotive industry, where the abrasion resistant material under investigation Hardox 400 steel is widely used for the manufacturing of truck bodies. The aim of this study was a comprehensive analysis of the machinability of this material using WEDM employing a 33−round experiment. Based on the change in machine parameters (pulse off time, gap voltage, discharge current, pulse on time, and wire feed), the cutting speed, the topography of machined surfaces, and the chemical composition of the workpiece surface, the morphology and condition of the subsurface layer including lamella production and a subsequent determination of the distribution of individual elements in the given area were analyzed. It has been found that during the machining of this steel, many defects occur in the subsurface layer of the material in the form of cracks with a depth of up to 22 µm and burned cavities. However, by appropriately adjusting the machine parameters, it was possible to completely remove these cracks.