Semi-continuous emulsion copolymerization of vinyl acetate and butyl acrylate in presence of AMPS

Application of Polyvinyl Acetate/Lignin Copolymer as Bio-Based Coating Material and Its Effects on Paper Properties

In this work, lignin-vinyl acetate copolymers containing different fractions of lignin were synthesized by the copolymerization technique. The synthesized copolymer was successfully applied to coat the paper for enhancing its properties and performance. The effects of the lignin-vinyl acetate copolymer on the physicochemical, air permeability and mechanical properties of paper were investigated. The mechanical strength, hydrophilic, and air permeability properties of coated paper were improved with the increasing content of the lignin. Lignin-vinyl acetate copolymer containing 15% lignin coated paper exhibited a 1.86 times increase in the tensile index, 45 times increase in the water contact angle, and a 41.1% reduction in the air permeability compared with uncoated paper. Scanning electron microscopy was applied to study the morphology of the coated and uncoated paper. The results showed that paper surface porosity structure was decreased, while the surface smoothness was enhanced considerably with increasing lignin fraction in the copolymer. Therefore, the successful fabrication of such an enchanting coated paper may afford new potential and great applications in the packaging paper.

Preparation and Characterization of Soap-Free Vinyl Acetate/Butyl Acrylate Copolymer Latex

The soap-free emulsion of vinyl acetate (VAc)/butyl acrylate (BA) copolymer was prepared by a semi-continuous and pre-emulsification polymerization method, using ammonium sulfate allyloxy nonylphenoxy poly(ethyleneoxy) (10) ether (DNS-86) as a reactive emulsifier. The effects of DNS-86 on the stability of the emulsion and the properties of the latex film were investigated. The infrared spectrum, thermal stability, glass transition temperature and micromorphology of latex were also studied. The results showed that the emulsion had the best stability and the conversion rate reached a maximum of 98.46% when the DNS-86 amount was 4 wt % of the total amount of monomers. Compared with the PVAc latex synthesized with octylphenol polyoxyethylene ether (10) (OP-10), the latex prepared with DNS-86 has higher thermal stability and ionic stability, whereas the latex film has better water resistance.

Improvement in Wood Bonding Strength of Poly (Vinyl Acetate-Butyl Acrylate) Emulsion by Controlling the Amount of Redox Initiator

Polyvinyl acetate emulsion adhesive has been widely used due to its good bonding performance and environmentally friendly properties. Indeed, the bonding performance can be further improved by copolymerizing with other monomers. In this study, the effect of the adjunction of redox initiator (hydrogen peroxide–tartaric acid, H₂O₂–TA) on the properties of the poly (vinyl acetate-butyl acrylate) (P (VAc–BA)) emulsion adhesive was investigated. With increasing dosage, the reaction became more complete and the obtained film was more compact, as identified via SEM. The core-shell structure of the emulsion particles was confirmed via TEM. Results indicate that while the initiator content increased from 0.5 to 1.0%, a clearer core-shell structure was obtained and the bonding strength of the plywood improved from 2.34 to 2.97 MPa. With the further incorporation of H₂O₂–TA (i.e., 1.5%), the bonding performance deteriorated. The optimum wood bonding strength (2.97 MPa) of the prepared P (VAc-BA) emulsion adhesive was even better than that (2.55 MPa) of a commercial PVAc emulsion adhesive, suggesting its potential application for the wood industry.