Immobilization of Oxyanions on the Reconstructed Heterostructure Evolved from a Bimetallic Oxysulfide for the Promotion of Oxygen Evolution Reaction

In situ evolution of bulk-active γ-CoOOH with immobilized Gd dopants enabling efficient oxygen evolution electrocatalysis

Promoting the in situ reconstruction of transition metal (TM)-based precatalysts into low-crystalline and well-modified TM (oxy)hydroxides (TMOxHy) during the alkaline oxygen evolution reaction (OER) is crucial for enhancing their catalytic performances. In this study, we incorporated gadolinium (Gd) into a cobalt hydroxide precatalyst, achieving a deep reconstruction into cobalt oxyhydroxide (γ-CoOOH) while retaining the incorporated Gd during the activation process of the alkaline OER. The unconventional non-leaching Gd dopants endow γ-CoOOH with reduced crystallinity, increasing the exposure of electrolyte-accessible Co atoms and enhancing its bulk activity. Furthermore, the modulation of the electronic structure of γ-CoOOH substantially boosts the intrinsic activity of the active Co sites. As a result, when supported on nickel foam, the catalyst exhibits remarkable alkaline OER performance, achieving a current density of 100 mA cm-2 at a low overpotential of approximately 327 mV. Notably, an ultrahigh current density of 1000 mA cm-2 is robustly maintained for 5 days, highlighting its immense potential for practical applications in large-scale hydrogen production.

Electrochemical reconfiguration of iron-modified Ni3S2 surface induced oxygen vacancies to immobilize sulfate for enhanced oxygen evolution reaction

There is an urgent need for highly active, durable, and low-cost electrocatalysts to overcome the shortcomings of high overpotential in the oxygen evolution reaction (OER) process. In this work, the nickel-iron hydroxysulfate rich in sulfate and oxygen vacancies (SO42-@Fe-NiOOH-Ov/NiS) is legitimately constructed. SO42-@Fe-NiOOH-Ov/NiS only requires a low overpotentials of 190 mV and 232 mV at 10 mA cm-2 and 100 mA cm-2 current densities in 1 M KOH, with excellent stability for 200 h at 100 mA cm-2 current density. In situ Raman spectroscopy and Fourier transform infrared spectroscopy demonstrated the stable adsorption of more SO42- on the surface of catalyst. Density functional theory calculations testify surface reconstruction, doped Fe and oxygen vacancies significantly reduced the adsorption energy of sulfate on the surface. More importantly, the formation of *OOH to O2 is facilitated by the highly hydrogen bonding between SO42- and *OOH, accelerating the OER process.

Atomic-scale Ru anchored on chromium-shavings as a precursor for a pH-universal hydrogen evolution reaction electrocatalyst

In the leather manufacturing industry, the management of substantial quantities of solid waste containing chrome shavings remains a formidable challenge. Concurrently, there is a pressing need for the development of pH-universal and economically viable electrocatalysts for the hydrogen evolution reaction (HER). In response to these intertwined challenges, this study proposes an innovative approach wherein the amino groups present on the surface of chrome shavings are utilized to immobilize single ruthenium atoms during pyrolysis, thereby facilitating the synthesis of hydrogen evolution electrocatalysts. The optimized sample, denoted as CN/Cr2O3/Ru-1, demonstrates exceptional electrocatalytic performance, exhibiting an ultra-low overpotential of -28 mV in 1.0 M KOH at a current density of 10 mA cm-2, and it also exhibits good performance in acidic and neutral electrolytes. Importantly, these overpotentials surpass those reported for many previous ruthenium-based catalysts. Density functional theory (DFT) calculations elucidate that both oxygen (O) and chromium (Cr) moieties within Cr2O3 can engage in favorable interactions with the coordination patterns of the ruthenium (Ru) atoms, thereby elucidating the synergistic enhancement conferred by the chromium element in CN/Cr2O3/Ru, which ultimately facilitates and promotes the catalytic activity of the ruthenium atoms serving as the catalytic center. This facile synthesis route not only presents a green solution for addressing waste chromium pollutants but also offers a promising avenue for the development of high-performance, cost-efficient electrocatalysts.

Understanding Advanced Transition Metal-Based Two Electron Oxygen Reduction Electrocatalysts from the Perspective of Phase Engineering

Non-noble transition metal (TM)-based compounds have recently become a focal point of extensive research interest as electrocatalysts for the two electron oxygen reduction (2e- ORR) process. To efficiently drive this reaction, these TM-based electrocatalysts must bear unique physiochemical properties, which are strongly dependent on their phase structures. Consequently, adopting engineering strategies toward the phase structure has emerged as a cutting-edge scientific pursuit, crucial for achieving high activity, selectivity, and stability in the electrocatalytic process. This comprehensive review addresses the intricate field of phase engineering applied to non-noble TM-based compounds for 2e- ORR. First, the connotation of phase engineering and fundamental concepts related to oxygen reduction kinetics and thermodynamics are succinctly elucidated. Subsequently, the focus shifts to a detailed discussion of various phase engineering approaches, including elemental doping, defect creation, heterostructure construction, coordination tuning, crystalline design, and polymorphic transformation to boost or revive the 2e- ORR performance (selectivity, activity, and stability) of TM-based catalysts, accompanied by an insightful exploration of the phase-performance correlation. Finally, the review proposes fresh perspectives on the current challenges and opportunities in this burgeoning field, together with several critical research directions for the future development of non-noble TM-based electrocatalysts.

Reinforcement of Electrocatalytic Oxygen Evolution Activity Enabled by Constructing Silver-Incorporated NiCo-PBA@NiFe-LDH Hierarchical Nanoboxes

Complicated oxygen evolution reaction (OER) poses the bottleneck in improving the efficiency of hydrogen production through water electrolysis. Herein, an integrated strategy to modulate the electronic structure of NiFe layered double hydroxide (NiFe-LDH) is reported by constructing Ag-incorporated NiCo-PBA@NiFe-LDH heterojunction with a hierarchical hollow structure. This "double heterojunction" facilitates local charge polarization at the interface, thereby promoting electron transfer and reducing the adsorption energy of intermediates, ultimately enhancing the intrinsic activity of the catalyst. It is noteworthy that an exchange bias field is observed between NiCo-PBA and NiFe-LDH, which will be conducive to regulating the electron spin states of metals and facilitating the production of triplet oxygen. Additionally, the unique hierarchical nanoboxes provide a large specific surface area that ensures adequate exposure to adsorption sites and active sites. Profiting from the synergistic advantages, the overpotential is as low as 190 mV at a current density of 10 mA cm-2, with a low Tafel slope of 21 mV dec-1. Moreover, density functional theory (DFT) calculation further substantiated that the incorporation of Ag in the heterojunction can effectively reduce the adsorption energy of reactant intermediates and enhance the conductivity.

Tuning the Electronic Property of Reconstructed Atomic Ni-CuO Cluster Supported on N/O-C for Electrocatalytic Oxygen Evolution

Electrochemical activation usually accompanies in situ atom rearrangement forming new catalytic sites with higher activity due to reconstructed atomic clusters or amorphous phases with abundant dangling bonds, vacancies, and defects. By harnessing the pre-catalytic process of reconstruction, a multilevel structure of CuNi alloy nanoparticles encapsulated in N-doped carbon (CuNi nanoalloy@N/C) transforms into a highly active compound of Ni-doped CuO nanocluster supported on (N/O-C) co-doped C. Both the exposure of accessible active sites and the activity of individual active sites are greatly improved after the pre-catalytic reconstruction. Manipulating the Cu/Ni ratios of CuNi nanoalloy@N/C can tailor the electronic property and d-band center of the high-active compound, which greatly optimizes the energetics of oxygen evolution reaction (OER) intermediates. This interplay among Cu, Ni, C, N, and O modifies the interface, triggers the active sites, and regulates the work functions, thereby realizing a synergistic boost in OER.

Durable Ru Nanocrystal with HfO2 Modification for Acidic Overall Water Splitting

Durable and efficient bi-functional catalyst, that is capable of both oxygen evolution reaction and hydrogen evolution reaction under acidic condition, are highly desired for the commercialization of proton exchange membrane water electrolysis. Herein, we report a robust L-Ru/HfO2 heterostructure constructed via confining crystalline Ru nanodomains by HfO2 matrix. When assembled with a proton exchange membrane, the bi-functional L-Ru/HfO2 catalyst-based electrolyzer presents a voltage of 1.57 and 1.67 V to reach 100 and 300 mA cm-2 current density, prevailing most of previously reported Ru-based materials as well as commercial Pt/C||RuO2 electrolyzer. It is revealed that the synergistic effect of HfO2 modification and small crystalline domain formation significantly alleviates the over-oxidation of Ru. More importantly, this synergistic effect facilitates a dual-site oxide path during the oxygen evolution procedure via optimization of the binding configurations of oxygenated adsorbates. As a result, the Ru active sites maintain the metallic state along with reduced energy barrier for the rate-determining step (*O→*OOH). Both of water adsorption and dissociation (Volmer step) are strengthened, while a moderate hydrogen binding is achieved to accelerate the hydrogen desorption procedure (Tafel step). Consequently, the activity and stability of acidic overall water splitting are simultaneously enhanced.

In situ self-reconstructed hierarchical bimetallic oxyhydroxide nanosheets of metallic sulfides for high-efficiency electrochemical water splitting

The advancement of economically efficient electrocatalysts for alkaline water oxidation based on transition metals is essential for hydrogen production through water electrolysis. In this investigation, a straightforward one-step solvent method was utilized to spontaneously cultivate bimetallic sulfide S-FeCo1 : 1/NIF on the surface of a nickel-iron foam (NIF). Capitalizing on the synergistic impact between the bimetallic constituents and the highly active species formed through electrochemical restructuring, S-FeCo1 : 1/NIF exhibited remarkable oxygen evolution reaction (OER) performance, requiring only a 310 mV overpotential based on 500 mA cm-2 current density. Furthermore, it exhibited stable operation at 200 mA cm-2 for 275 h. Simultaneously, the catalyst demonstrated excellent hydrogen evolution reaction (HER) and overall water-splitting capabilities. It only requires an overpotential of 191 mV and a potential of 1.81 V to drive current densities of 100 and 50 mA cm-2. Density functional theory (DFT) calculations were also employed to validate the impact of the bimetallic synergistic effect on the catalytic activity of sulfides. The results indicate that the coupling between bimetallic components effectively reduces the energy barrier required for the rate-determining step in water oxidation, enhancing the stability and activity of bimetallic sulfides. The exploration of bimetallic coupling to improve the OER performance holds theoretical significance in the rational design of advanced electrocatalysts.