Evaluation of soldered connectors of two base metal ceramic alloys

Effects of conventional welding and laser welding on the tensile strength, ultimate tensile strength and surface characteristics of two cobalt-chromium alloys: a comparative study

The purpose of this study was to evaluate the efficacy of laser welding and conventional welding on the tensile strength and ultimate tensile strength of the cobalt-chromium alloy. Samples were prepared with two commercially available cobalt-chromium alloys (Wironium plus and Diadur alloy). The samples were sectioned and the broken fragments were joined using Conventional and Laser welding techniques. The welded joints were subjected to tensile and ultimate tensile strength testing; and scanning electron microscope to evaluate the surface characteristics at the welded site. Both on laser welding as well as on conventional welding technique, Diadur alloy samples showed lesser values when tested for tensile and ultimate tensile strength when compared to Wironium alloy samples. Under the scanning electron microscope, the laser welded joints show uniform welding and continuous molt pool all over the surface with less porosity than the conventionally welded joints. Laser welding is an advantageous method of connecting or repairing cast metal prosthetic frameworks.

Bond strength of gold alloys laser welded to cobalt-chromium alloy

The objective of this study was to investigate the joint properties between cast gold alloys and Co-Cr alloy laser-welded by Nd:YAG laser. Cast plates were fabricated from three types of gold alloys (Type IV, Type II and low-gold) and a Co-Cr alloy. Each gold alloy was laser-welded to Co-Cr using a dental laser-welding machine. Homogeneously-welded and non-welded control specimens were also prepared. Tensile testing was conducted and data were statistically analyzed using ANOVA. The homogeneously-welded groups showed inferior fracture load compared to corresponding control groups, except for Co-Cr. In the specimens welded heterogeneously to Co-Cr, Type IV was the greatest, followed by low-gold and Type II. There was no statistical difference (P<0.05) in fracture load between Type II control and that welded to Co-Cr. Higher elongations were obtained for Type II in all conditions, whereas the lowest elongation occurred for low-gold welded to Co-Cr. This study indicated that, of the three gold alloys tested, the Type IV gold alloy was the most suitable alloy for laser-welding to Co-Cr.

Laser welding of a cobalt-chromium removable partial denture alloy

STATEMENT OF PROBLEM

The electric alloy brazed joints of removable partial denture alloys have failed frequently after routine usage.

PURPOSE

A technique providing higher joint strengths was investigated. This investigation compared the tensile strengths of electric-brazed and laser-welded joints for a cobalt-chromium removable partial denture alloy.

MATERIAL AND METHODS

Twenty-four cobalt-chromium standard tensile testing rods were prepared and divided into three groups of eight. All specimens in the control group (group 1) were left in the as-cast condition. Groups 2 and 3 were the test specimens, which were sectioned at the center of the rod. Eight specimens were joined by using electric brazing, and the remaining specimens were joined by using laser welding. After joining, each joint was ground to a uniform diameter, then tested to tensile failure on an Instron universal testing machine. Failure loads were recorded and fracture stress calculated. Statistical analysis was applied.

RESULTS

The student-Newman-Keuls test showed a highly significant difference between the joint strengths of the as-cast control specimens, the electric-brazed and laser-welded joints.

CONCLUSIONS

The tensile strengths of the as-cast joints were higher than those for the laser-welded joints, and both were higher than the electric-brazed joint strengths.

A comparison of infrared- and torch-soldering of Au-Pd and Co-Cr metal-ceramic alloys using a high-fusing solder

PURPOSE

The purpose of this study was to compare the bond strengths and fracture modes of soldered joints formed by infrared and gas-oxygen torch heating of a high-fusing, gold-based solder in two metal-ceramic alloys.

MATERIALS AND METHODS

Pairs of half-dumbbell-shaped specimens of either an Au-Pd or a Co-Cr alloy were positioned with a 0.25-mm gap and were joined using a high-fusing, gold-based solder by either gas-oxygen torch heating or infrared heating. The resulting specimens were subjected to a heat treatment that simulated ceramic firing. Each specimen was fractured in tension at a loading rate of 0.5 cm/min, and its bond strength was measured. The halves of the specimen were rejoined using the other heating method and were heat treated, and the specimen's bond strength was again measured. Fractured cross-sections were examined at a magnification of 40x to determine the following: the fracture mode (adhesive, cohesive, or mixed); the percentage of adhesive fracture; the presence or absence of voids, porosities, or flux inclusions; and the percentage of the cross-section that was discolored.

RESULTS

Three-factor analyses of variance showed that neither the heating method, the particular specimen tested, nor the order of testing significantly affected the bond strength (P < .05). For each alloy, significantly fewer infrared-heated joints than torch-heated joints contained voids, porosities, or flux inclusions visible at 40x (chi 2 test, P < .05). All fractures were either entirely cohesive in the solder or mixed cohesive and adhesive. When infrared heating was used, entirely cohesive fractures occurred more frequently in the Au-Pd alloy specimens than in the Co-Cr alloy specimens (chi 2 test, P < .05). The coefficients of variation of the bond strengths for the infrared-heated joints were smaller than those for the torch-heated joints.

CONCLUSIONS

Although the two heating methods produced solder joints that had strengths that were not significantly different, infrared-heated joints showed less scatter in bond strengths. It was suggested that, in the hands of most technicians, fewer infrared-heated joints would contain defects visible at a magnification of 40x. The presence of such defects may increase the probability of in vivo failure caused by cyclic stresses.