Once the fit of the cast metal framework on a removable partial denture (RPD) has been verified, the manufacturer's prefabricated denture teeth are typically secured on the cast metal framework to prepare for a wax evaluation. Although prefabricated denture teeth are available in different tooth forms and sizes, they require modification to fit an edentulous space. In arches with severe space discrepancy, it may be inefficient and time-consuming to make modifications to prefabricated denture teeth. The technique described uses digital technology to fabricate custom denture teeth on a cast metal framework and establish harmonious occlusion. An edentulous space with more than a single tooth replacement is designed as a splinted fixed partial denture with a connector. The designed teeth are milled in the double-cross-linked polymer to prepare for a wax evaluation, and once verified, the RPD is processed by using heat polymerization. Modifications are made to the milled denture teeth after wax elimination to reduce the likelihood of acrylic resin bond failure.

Two Body Wear of Newly Introduced Nanocomposite Teeth and Cross Linked Four Layered Acrylic Teeth: a Comparitive In Vitro Study

STATEMENT OF PROBLEM

Wear of complete denture teeth results in compromise in denture esthetics and functions. To counteract this problem, artificial teeth with increased wear resistance had been introduced in the market such as nanocomposite teeth.

PURPOSE

The purpose of this study was to compare the amount of wear between nanocomposite teeth and acrylic teeth.

MATERIALS AND METHODS

Fifteen specimens were chosen from each group namely the nanocomposite teeth (SR_-PHONARES) and the acrylic teeth (ACRY PLUS). Maxillary premolar was only chosen for testing and the samples were customized according to the specifications of the pin on disc machine. Pin on disc machine is a two body tribometer which quantifies the amount of wear under a specific load and time. Test samples were mounted on to the receptacle of the pin on disc machine and tested under a load of 0.3 kg for 1,000 cycles of rotation against a 600 grit emery paper. The amount of wear is displayed from the digital reading obtained from the pin on disc machine.

RESULTS

After statistical analysis, it was found that, the amount of wear is more in four layered acrylic teeth. The p value obtained is 0.002 (<0.005) thus implies that the difference in wear between nanocomposite teeth and acrylic teeth is statistically significant.

CONCLUSION

Though the nanocomposite teeth has less amount of wear than the four layered acrylic teeth, the difference is very less and adds only to a little clinical significance but the cost of the nanocomposite is four times that of the acrylic teeth. Further clinical studies must be performed to confirm our results.

Composite occlusal surfaces for acrylic resin denture teeth

Acrylic resin denture teeth often exhibit rapid occlusal wear, which may lead to a loss of chewing efficiency and a loss of vertical dimension of occlusion. The use of metal occlusal surfaces on the acrylic resin denture teeth will minimize occlusal wear. Several articles have described methods to construct metal occlusal surfaces; however, these methods are time-consuming, costly, and sometimes considered to be unesthetic. These methods also require that the patient be without the prosthesis for the time necessary to perform the laboratory procedures. This article presents a quick, simple, and relatively inexpensive procedure for construction of composite occlusal surfaces on complete and partial dentures.