In vitro abrasion of two acrylic veneers

Wear behavior of materials for additive manufacturing after simulated occlusion of deciduous dentition

OBJECTIVES

To evaluate wear characteristics of materials for additive manufacturing (AM) after a simulated occlusal test in primary teeth. Wear was simulated by means of impacting - sliding wear testing (ISWT) between specimens prepared from materials for AM against enamel derived from deciduous teeth.

METHODS

The prepared hemispherical upper specimens were subjected to impacting-sliding wear test (ISWT) machine against the flattened enamel of deciduous molars on lower specimens. The samples were subjected to 20,000 load cycles using a contact force of 30 N between the opposing surfaces under controlled conditions. In the upper specimens, five groups (n=9): four types of additively manufactured materials Dima, Zenith, Detax, Veltz and a deciduous enamel groups were tested in this study. The enamel-to-enamel group was used as the control. Wear characteristics comprised wear surface area, wear depth, wear volumetric loss, and surface roughness were measured with a confocal laser scanning microscopy (CLSM) and scanning electron microscopy (SEM). Data obtained were statistically analyzed by Kruskal-Wallis test and Dunn's test with Bonferroni correction (p < 0.05).

RESULTS

Dima showed significantly higher worn surface area (p = 0.009, 0.001, and < 0.001 for Zenith, Detax, and control enamel, respectively), volumetric loss (p = 0.027, 0.007, and < 0.001 for Zenith, Detax, and control enamel, respectively), and damaged opposing enamel (p = 0.002, 0.001, and 0.01 for Detax, Veltz, and control enamel, respectively). There was no significant difference among the volumetric loss in Zenith and Detax. However, SEM revealed that Zenith showed rough worn surfaces and chipping, Detax showed rather a smooth circular worn surface. The worn area of Veltz was smaller than Detax and Zenith at 5,000 cycles, but higher at 15,000 and 20,000 cycles, and SEM showed detachment.

CONCLUSION

Wear behavior was different among different materials for AM. In the upper specimens, DM and VZ showed large wear. In the lower specimens, DM caused largest enamel wear and damage. In contrast, ZT and DX showed lower wear and caused less damage to the antagonistic primary enamel. SEM image of ZT showed large losses due to chipping, whereas DX showed the rather smooth. DX was confirmed to have lowest wear and caused least damage to the opposing deciduous enamel, which might be applicable as restorative treatments in deciduous dentition.

SIGNIFICANCE

Additive manufactured dental materials could be considered as a treatment modality in deciduous teeth.

Wear characteristics of trimethylolpropane trimethacrylate filler-containing resins for the full crown restoration of primary molars

Although the demand for aesthetic restoration of primary molars has increased, the full-crown restorations using resin and the details of the wear characteristics of trimethylolpropane trimethacrylate (TMPT) filler containing resins for primary molars are not well understood. This study was conducted to determine whether new light-cured composite resin (Fantasista) and 4-META/MMATBB resin (Bondfill SB) are appropriate for full crown restoration of primary molars by evaluating their wear characteristics. Both resins products contain TMPT filler. The properties of the resins were evaluated through in vitro impacting-sliding wear tests; the wear properties of the opposing enamel specimens used in the tests were also studied. The properties of the resins were compared with those of Litefill, MetafilC, and Clearfil FII, which had been evaluated previously. Fantasista exhibited simple shape of wear that was suggestive of a higher wear resistance than that of Litefill. Fantasista caused the least damage to the antagonistic primary enamel.

Abrasion of 6 dentifrices measured by vertical scanning interference microscopy

Objectives

The abrasion of dentifrices is well recognized to eliminate the dental plaque. The aims of this study were to characterize the abrasive powders of 6 dentifrices (3 toothpastes and 3 toothpowders) and to measure the abrasion on a test surface by Vertical Scanning Interference microscopy (VSI).

Material and Methods

Bright field and polarization microscopy were used to identify the abrasive particles on the crude dentifrices and after prolonged washes. Scanning electron microscopy and microanalysis characterized the shape and nature of the particles. Standardized and polished blocks of poly(methylmethacrylate) were brushed with a commercial electric toothbrush with the dentifrices. VSI quantified the mean roughness (Ra) and illustrated in 3D the abraded areas.

Results

Toothpastes induced a limited abrasion. Toothpowders induced a significantly higher roughness linked to the size of the abrasive particles. One powder (Gencix^® produced a high abrasion when used with a standard testing weight. However, the powder is based on pumice particles covered by a plant homogenate that readily dissolves in water. When used in the same volume, or after dispersion in water, Ra was markedly reduced.

Conclusion

Light and electron microscopy characterize the abrasive particles and VSI is a new tool allowing the analysis of large surface of abraded materials.

Influence of laboratory light sources on the wear characteristics of indirect composites

The purpose of the current study was to evaluate the influence of light sources on the mechanical properties and wear characteristics of indirect composite materials. The two composite materials used were Estenia C&B and Epricord. The three laboratory polymerization units used, of which the wavelength range was 400-500 nm, were Hyper LII (two metal halide lamps of 4.82 mW/cm(2)), α-Light II (one halogen lamp and two fluorescent tubes of 3.60 mW/cm(2)), and Labolight LV-II (three fluorescent tubes of 0.63 mW/cm(2)). Three-body wear test was performed using indirect composite plate specimens, a gold alloy antagonist, and a polymer slurry. Wear depths of Estenia C&B polymerized with Hyper LII, α-Light II, and Labolight LV-II were 5.7, 18.5, and 64.2 µm respectively, whereas those of Epricord were 12.9, 18.7, and 48.5 µm respectively. Results showed that, after 100,000 cycles of localized loading, high-intensity light sources were effective in enhancing the wear resistance of both composite materials.

Wear and surface roughness of current prosthetic composites after toothbrush/dentifrice abrasion

STATEMENT OF PROBLEM

Surface changes of prosthetic composites caused by toothbrushing are known, although composite materials have been improved and are now widely used for various kinds of prosthetic restorations.

PURPOSE

This study evaluated the influence of toothbrushing on abrasive wear and surface roughness of current prosthetic composites.

MATERIAL AND METHODS

Seven composite materials (Artglass, Axis, Cesead II, Conquest Sculpture, Estenia, Infis, and Targis) were assessed, and a machinable ceramic material (Cerec 2 Vitablocs) was used as a reference. Composite specimens polymerized with their proprietary curing units and sectioned ceramic specimens were stored in water for 14 days, and subsequently subjected to toothbrush-dentifrice abrasion. The amount of vertical loss and the surface roughness of each specimen after 20,000 strokes were determined with a profilometer. Average values of groups of 5 specimens were compared with ANOVA and Duncan new multiple range test.

RESULT

Significantly (P < .05) less wear was observed with respect to the Targis (10.01 microm; SD = 0.53 microm) and Estenia (13.04 microm; 1.95 microm) materials than for the other composites assessed, whereas Artglass (34.08 microm; 3.66 microm) and Conquest Sculpture (31.78 microm; 4.67 microm) materials demonstrated the most wear. The least surface roughness was exhibited by Conquest Sculpture (Ra, 0.54 microm; 0.07 microm) material, and the greatest by Cesead II (1.10 microm; 0.13 microm). Ceramic material showed a more wear-resistant (4.54 microm; 0.79 microm) and smoother (0.26 microm; 0.02 microm) surface than any of the composite materials.

CONCLUSION

Abrasion and surface roughness of the prosthetic composites caused by toothbrushing varied in accordance with the material. Type of prosthetic composite significantly influenced the surface condition after toothbrushing.

Effectiveness of polymerization of a prosthetic composite using three polymerization systems

STATEMENT OF PROBLEM

Although properties of laboratory-polymerized composite materials are influenced by the type of polymerizing unit, little information is available regarding the comparison between use of a high-intensity light source and application of secondary heat treatment.

PURPOSE

This study examined properties of a prosthetic veneering composite polymerized with 3 polymerizing systems to evaluate the effects of varying polymerization modes on hardness, solubility, and depth of cure.

MATERIAL AND METHODS

A composite material designed for a prosthetic veneer (Conquest Crown and Bridge) was polymerized using 3 methods: (1) exposure in the proprietary photopolymerizing unit with 2 halogen lamps (Cure-Lite Plus), followed by heating in an oven (Conquest Automatic Curing Unit); (2) exposure in a photopolymerizing unit with a xenon stroboscopic light source (Dentacolor XS); and (3) exposure in a photopolymerizing unit with 2 metal halide lamps (Hyper LII). Knoop hardness, water solubility, and depth of cure were determined for groups of 5 specimens, according to standardized testing methods. Data were compared using analysis of variance and the Duncan new multiple range test (P <.05).

RESULT

The hardness number generated with the metal halide unit was statistically greater than those produced by the other 2 methods, and material component released into water was minimal when the material was exposed with the metal halide unit (P <.05). Among the 3 photopolymerizing units, the metal halide unit consistently exhibited the greatest depth of cure.

CONCLUSION

Certain properties generated with the use of the high-intensity polymerizing unit exceeded those obtained from a proprietary system that requires a postheat treatment.

In vitro abrasion using an air-powder polishing device and its quantification by radiotracer measurement

OBJECTIVES

This study was conducted to examine the assessment of abrasion of two different materials after neutron activation.

METHODS

A fissure sealant material (Fissurit F/VOCO with a compressive strength of 235 MPa) and a glass ionomer cement (Aqua Ionofil/VOCO with a compressive strength of 170 MPa) were activated by irradiation with neutrons. Subsequent measurements of the full-energy-peak (FEP) (1368.55 keV of 24Na) were made of the sample materials before and after abrasion via exposure to the air-powder polishing to accurately describe substance loss.

RESULTS

Abrasion varied more than three-fold between the two materials.

SIGNIFICANCE

Neutron activation and radiotracer measurement allows the quantification of abrasion effects in different materials. In comparison with other current methods its use may allow a superior measurement accuracy and precision in determining the abraded mass.

Evaluating the antagonistic wear of restorative materials when placed against human enamel

Several clinical and laboratory studies have reported data on the nature of tooth wear against restorative materials (that is, amalgam, gold, glass ceramic and various composite resin systems). Several antagonistic substrates are known to cause various in vitro wear rates when placed in opposition to enamel. In this study, the authors evaluated 10 commercially available posterior composite resin systems and a gold alloy control. The findings showed that posterior composite resins containing zirconium silicate or quartz fillers caused greater antagonistic enamel wear than did microfilled or barium silicate-filled composite resins.