Structural consequences of the jellium model for alkali metal clusters

Synthesis, Structures, and Photoluminescence of Elongated Face-Centered-Cubic Ag14 Clusters Containing Lipoic Acid and Its Amide Analogue

Three face-centered-cubic (fcc) silver clusters-namely, [Ag₁₄(LA)₂(HLA)₄(PPh₃)₈]^2- (1), [Ag₁₄(HLA)₆(PPh₃)₈] (2), and [Ag₁₄(NLA)₆(PPh₃)₈] (3)-that are coprotected by lipoic acid (or its amide derivative) and phosphine ligands have been synthesized and structurally characterized (HLA = (±)-α-lipoic acid, LA = (±)-α-lipoate, and NLA = d,l-6,8-thioctamide). These clusters possess two superatomic electrons (the Jellium model), in harmony with a bonding octahedral Ag₆ core capped with 8 Ag atoms. Alternatively, the metal framework of 1-3 can be described as adopting a face-centered cubic (fcc) structure elongated along one of the 3-fold axes. The 12 S atoms from the six bioligands bridge the 12 edges of the (fcc) cube, forming a distorted icosahedron. The counterions, solvent or guest molecules play an important role in dictating the crystal lattices of the products. This is the first report of atom-precise structures of Ag-lipoic acid (or its derivatives) clusters, paving the way for further study of structure-property relationships of these bioligand protected metal nanoclusters. Photoluminescence was observed for cluster 3 with complex temperature-dependent emission patterns and efficiencies.

The submersion of sodium clusters in helium nanodroplets: identification of the surface → interior transition

The submersion of sodium clusters beyond a critical size in helium nanodroplets, which has recently been predicted on theoretical grounds, is demonstrated for the first time. Confirmation of a clear transition from a surface location, which occurs for alkali atoms and small clusters, to full immersion for larger clusters, is provided by identifying the threshold electron energy required to initiate Na(n) cluster ionization. On the basis of these measurements, a lower limit for the cluster size required for submersion, n ≥ 21, has been determined. This finding is consistent with the recent theoretical prediction.

High-Nuclearity Close-Packed Palladium-Nickel Carbonyl Phosphine Clusters: Heteropalladium [Pd16Ni4(CO)22(PPh3)4]2- and [Pd33Ni9(CO)41(PPh3)6]4- Containing Pseudo-Td ccp Pd16Ni4 and Pseudo-D3h hcp Pd33Ni9 Cores

[Pd(16)Ni(4)(CO)(22)(PPh(3))(4)](2)(-) (1) and [Pd(33)Ni(9)(CO)(41)(PPh(3))(6)](4)(-) (2) were obtained as the two major products from the reduction of PdCl(2)(PPh(3))(2) with [Ni(6)(CO)(12)](2)(-). Their crystal structures as [PPh(4)](+) salts were unambiguously determined from CCD X-ray crystallographic analyses; the resulting stoichiometries were ascertained from elemental analyses. Infrared, multinuclear (1)H, (31)P[(1)H] NMR, UV-vis, CV, variable-temperature magnetic susceptibility, and ESI FT/ICR mass spectrometric measurements were performed. The Pd(16)Ni(4) core of 1 ideally conforms to a ccp nu(3) tetrahedron of pseudo-T(d)() (4 3m) symmetry. Its geometry normal to each tetrahedral Pd(7)Ni(3) face (i.e., along each of the four 3-fold axes) may be viewed as a four-layer stacking of 20 metal atoms in a ccp [a(Ni(1)) b(Pd(3)) c(Pd(6)) a(Pd(7)Ni(3))] sequence. A comparative analysis of the different ligand connectivities about the analogous metal-core geometries in 1 and the previously reported [Os(20)(CO)(40)](2)(-) has stereochemical implications pertaining to the different possible modes of carbon monoxide attachment to ccp metal(111) surfaces. The unique geometry of the Pd(33)Ni(9) core of 2, which has pseudo-D(3)(h)() (6 2m) symmetry, consists of five equilateral triangular layers that are stacked in a hcp [a(Pd(7)Ni(3)) b(Pd(6)) a(Pd(7)Ni(3)) b(Pd(6)) a(Pd(7)Ni(3))] sequence. Variable-temperature magnetic susceptibility measurements indicated both 1 and 2 to be diamagnetic over the entire temperature range from 5.0 to 300 K. Neutral Pd(12)(CO)(12)(PPh(3))(6) (3) and [Pd(29)(CO)(28)(PPh(3))(7)](2)(-) (4) as the [PPh(4)](+) salt were obtained as minor decomposition products from protonation reactions of 1 and 2, respectively, with acetic acid. Compound 3 of pseudo-D(3)(d)() (3 2/m) symmetry represents the second highly deformed hexacapped octahedral member of the previously established homopalladium family of clusters containing uncapped, monocapped, bicapped, and tetracapped Pd(6) octahedra. The unprecedented centered 28-atom polyhedron for the Pd(29) core of 4 of pseudo-C(3)(v)() (3m) symmetry may be described as a four-layer stacking of 29 metal atoms in a mixed hcp/ccp [a(Pd(1)) b(Pd(3)) a(Pd(10)) c(Pd(15))] sequence.