Catalysis of Heteropoly Compounds (Polyoxometalates)

Selective Oxidation of Alcohols and Alkenes with Molecular Oxygen Catalyzed by Highly Dispersed Cobalt (II) Decorated 12-Tungstosilicic Acid-Modified Zirconia

Traditional procedures for oxidation processes suffer from a lack of selectivity, the use of organic solvents, the toxicity of the reagents, and waste production. As a cleaner alternative, highly dispersed Co over 12-tungstosilicicacid modified zirconia was synthesized and used for the selective oxidation of benzyl alcohol and styrene with molecular oxygen to carbonyl compounds under environmentally benign solvent-free conditions. The supremacy of the present catalyst lies in achieving excellent selectivity (>90%) for products with a very high turnover number. The catalytic activity of the recycled catalysts was also explored under optimized conditions to confirm sustainability. Further, the viability of the catalyst was studied via oxidation of various alcohols and alkenes under optimized conditions as well as superiority by comparison with the reported catalysts.

Isoprene synthesis from formaldehyde and isobutene over Keggin-type heteropolyacids supported on silica

Gas phase Prins condensation of isobutene with formaldehyde has been studied over different Keggin-type heteropolyacids supported on amorphous silica.

Unique properties of silver cations in solid-acid catalysis by zeolites and heteropolyacids

Reversible interconversion of Ag⁺ and Ag⁰ occurs in zeolite. Heterolytic dissociation of alkanes including methane and H₂ proceeds over Ag⁺-zeolite.

Novel composite material polyoxovanadate@MIL-101(Cr): a highly efficient electrocatalyst for ascorbic acid oxidation

A novel hybrid composite material, PMo10V2@MIL-101 was prepared by the encapsulation of the tetra-butylammonium (TBA) salt of the vanadium-substituted phosphomolybdate [PMo10V2O40](5-) (PMo10V2) into the porous metal-organic framework (MOF) MIL-101(Cr). The materials characterization by powder X-ray diffraction, Fourier transform infrared spectra and scanning electron microscopy confirmed the preparation of the composite material without disruption of the MOF porous structure. Pyrolytic graphite electrodes modified with the original components (MIL-101(Cr), PMo10V2), and the composite material PMo10V2@MIL-101 were prepared and their electrochemical responses were studied by cyclic voltammetry. Surface confined redox processes were observed for all the immobilized materials. MIL-101(Cr) showed one-electron reduction process due to chromium centers (Cr(III) → Cr(II)), while PMo10V2 presented five reduction processes: the peak at more positive potentials is attributed to two superimposed 1-electron vanadium reduction processes (V(V) → V(IV)) and the other four peaks to Mo-centred two-electron reduction processes (Mo(VI) → Mo(V)). The electrochemical behavior of the composite material PMo10V2@MIL-101 showed both MIL-101(Cr) and PMo10V2 redox features, although with the splitting of the two vanadium processes and the shift of the Mo- and Cr- centered processes to more negative potentials. Finally, PMo10V2@MIL-101 modified electrode showed outstanding enhanced vanadium-based electrocatalytic properties towards ascorbic acid oxidation, in comparison with the free PMo10V2, as a result of its immobilization into the porous structure of the MOF. Furthermore, PMo10V2@MIL-101 modified electrode showed successful simultaneous detection of ascorbic acid and dopamine.