Bernardini C, Zamparini F, Prati C, Salaroli R, Spinelli A, Zannoni A, Forni M, Gandolfi MG. Osteoinductive and regenerative potential of premixed calcium-silicate bioceramic sealers on vascular wall mesenchymal stem cells. Int Endod J 2024; 57:1264-1278. [PMID: 38943551 DOI: 10.1111/iej.14098] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/27/2023] [Revised: 04/04/2024] [Accepted: 05/13/2024] [Indexed: 07/01/2024]
Abstract
AIM The osteogenic potential of new premixed calcium-silicate-containing bioceramic sealers (Ca-Si sealers) was tested with porcine vascular wall-mesenchymal stem cells (pVW-MSCs). METHODOLOGY Two Ca-Si-containing sealers: Ceraseal (MetaBiomed, Cheong-si, South Korea) and AH Plus Bioceramic (Maruchi, Wonju-si, South Korea), and an epoxy resin sealer (AH Plus; Dentsply, Konstanz, Germany) as a control, were prepared according to the manufacturers' indications. All samples were allowed to set for 100% of their setting time in a sterile humid cabinet at 37°C and 95% relative humidity. pVW-MSC seeding efficiency and osteogenic differentiation were analysed as marker of gene/protein expression for up to 12 days. Mineralization assay and immunofluorescence staining were performed and evaluated over a period of 21 days. Statistical analyses were conducted using one-way analysis of variance (p < .05). Additional samples were prepared and stored under the same conditions and inspected using an environmental scanning electron microscope equipped with an energy dispersive X-ray spectroscopy system. RESULTS Significantly higher cell seeding efficiency (p < .05) was observed for both Ca-Si sealers from day 8. pVW-MSCs showed a significant shift towards the osteogenic lineage only when seeded in contact with Ca-Si sealers. Gene expression of osteopontin was upregulated significantly. Collagen I and osteocalcin were clearly expressed by cells in contact with Ca-Si sealers. Mineralization granules were observed in Alizarin red assays and confocal laser scanning microscopy analysis of both Ca-Si sealers. No gene expression or granule mineralization were observed on the epoxy resin sealer. CONCLUSIONS Premixed Ca-Si sealers displayed a higher potential for osteogenic activity on pVW-MSCs. Epoxy resin sealer was unable to induce any osteogenic activity. The properties of both Ca-Si sealers suggest their potential as osteoinductive platforms for vascular MSCs in periapical bone.
Collapse
Affiliation(s)
- Chiara Bernardini
- Department of Veterinary Medical Sciences, University of Bologna, Bologna, Italy
| | - Fausto Zamparini
- Endodontic Clinical Section, Dental School, Department of Biomedical and Neuromotor Sciences, University of Bologna, Bologna, Italy
- Laboratory of Green Biomaterials and Oral Pathology, Dental School, Department of Biomedical and Neuromotor Sciences, University of Bologna, Bologna, Italy
| | - Carlo Prati
- Endodontic Clinical Section, Dental School, Department of Biomedical and Neuromotor Sciences, University of Bologna, Bologna, Italy
| | - Roberta Salaroli
- Department of Veterinary Medical Sciences, University of Bologna, Bologna, Italy
| | - Andrea Spinelli
- Endodontic Clinical Section, Dental School, Department of Biomedical and Neuromotor Sciences, University of Bologna, Bologna, Italy
| | - Augusta Zannoni
- Department of Veterinary Medical Sciences, University of Bologna, Bologna, Italy
| | - Monica Forni
- Department of Medical and Surgical Sciences, University of Bologna, Bologna, Italy
- Health Sciences and Technologies-Interdepartmental Center for Industrial Research (CIRI-SDV), Alma Mater Studiorum-University of Bologna, Bologna, Italy
| | - Maria Giovanna Gandolfi
- Laboratory of Green Biomaterials and Oral Pathology, Dental School, Department of Biomedical and Neuromotor Sciences, University of Bologna, Bologna, Italy
| |
Collapse
|
2
|
Marger L, Abdelaziz M, di Bella E, Krejci I, Anton Y Otero CI. An in vitro study on the influence of laser-activated irrigation on infiltration and leakage of a dual curing-resin cement as an endodontic sealer. Biomater Investig Dent 2024; 11:41098. [PMID: 39045149 PMCID: PMC11265500 DOI: 10.2340/biid.v11.41098] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 05/01/2024] [Accepted: 06/27/2024] [Indexed: 07/25/2024] Open
Abstract
Objectives The study aims to investigate the effects of laser-activated irrigation on infiltration and microleakage of a dual-curing resin cement applied as a root canal sealer. Methods Thirty-eight extracted upper molars were attributed to four experimental groups. Roots were mechanically enlarged and disinfected (NaOCl). Control samples (n = 11) were irrigated with conventional needles and three different lasers were used to activate the irrigant in the other groups (n = 9): 2.94 µm Er:YAG laser, 9,300 µm CO2 laser and 808 nm diode laser with a modified black coated laser tip. Final irrigation was performed in each group with ethylenediaminetetraacetic acid (EDTA), sodium hypochlorite (NaOCl) and sodium chloride (NaCl) activated with lasers and in the control without activation.Dentin tubules were then labeled with a red fluorophore (Rhodamine B) and the root canals were sealed with a dual-curing resin cement (Paracore). The cement fixed the dye on the sealed and infiltrated dentin parts. To remove the Rhodamine not fixed by the cement, roots were then sectioned horizontally and immersed in hydrogen peroxide (H2O2). The empty dentin tubules spaces were then labeled with a green fluorophore (Fluorescein) allowing the visualization of infiltration and microleakage by confocal microscopy. Results Percentages of infiltration were significantly higher in the middle root third of the control and Er:YAG laser-activated samples compared to CO2 or diode laser groups. Microleakage was present in all experimental groups but significantly less after CO2 laser activation. Conclusion Laser-activated irrigation impacted resin cement infiltration and microleakage dependent on the applied wavelength. Er:YAG laser activation led to higher values of infiltration and microleakage compared to CO2 and diode lasers.
Collapse
Affiliation(s)
- Laurine Marger
- Division of Cariology and Endodontology, CUMD - University Clinics of Dental Medicine, Faculty of Medicine, University of Geneva Geneva, Switzerland
| | - Marwa Abdelaziz
- Division of Cariology and Endodontology, CUMD - University Clinics of Dental Medicine, Faculty of Medicine, University of Geneva Geneva, Switzerland
| | - Enrico di Bella
- Division of Cariology and Endodontology, CUMD - University Clinics of Dental Medicine, Faculty of Medicine, University of Geneva Geneva, Switzerland
| | - Ivo Krejci
- Division of Cariology and Endodontology, CUMD - University Clinics of Dental Medicine, Faculty of Medicine, University of Geneva Geneva, Switzerland
| | - Clara Isabel Anton Y Otero
- Division of Cariology and Endodontology, CUMD - University Clinics of Dental Medicine, Faculty of Medicine, University of Geneva Geneva, Switzerland
| |
Collapse
|
3
|
López-García S, Sánchez-Bautista S, García-Bernal D, Lozano A, Forner L, Sanz JL, Murcia L, Rodríguez-Lozano FJ, Oñate-Sánchez RE. Premixed calcium silicate-based ceramic sealers promote osteogenic/cementogenic differentiation of human periodontal ligament stem cells: A microscopy study. Microsc Res Tech 2024; 87:1584-1597. [PMID: 38433562 DOI: 10.1002/jemt.24545] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 08/31/2023] [Revised: 12/12/2023] [Accepted: 02/26/2024] [Indexed: 03/05/2024]
Abstract
To evaluate the effects of premixed calcium silicate based ceramic sealers on the viability and osteogenic/cementogenic differentiation of human periodontal ligament stem cells (hPDLSCs). The materials evaluated were TotalFill BC Sealer (TFbc), AH Plus Bioceramic Sealer (AHPbc), and Neosealer Flo (Neo). Standardized discs and 1:1, 1:2, and 1:4 eluates of the tested materials were prepared. The following in vitro experiments were carried out: ion release, cell metabolic activity 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay, cell migration, immunofluorescence experiment, cell attachment, gene expression, and mineralization assay. Statistical analyses were performed using one-way ANOVA followed by Tukey's post hoc test (p < .05). Increased Ca2+ release was detected in TFbc compared to AHPbc and Neo (*p < .05). Biological assays showed a discrete cell metabolic activity and cell migration in Neo-treated cell, whereas scanning electronic microscopy assay exhibited that TFbc group had a better cell adhesion process of substrate attachment, spreading, and cytoskeleton development on the niche-like structures of the cement than AHPbc and Neo. The sealers tested were able to induce overexpression of the CEMP-1, ALP, and COL1A1 genes in the first days of exposure, particularly in the case of TFbc (***p < .001). All materials tested significantly increased the mineralization of hPDLSCs when compared to the negative control, although more pronounced calcium deposition was observed in the TFbc-treated cells (***p < .001). Our results suggested that TFbc promotes cell differentiation, both by increasing the expression of key osteo/odontogenic genes and by promoting mineralization of the extracellular matrix, whereas this phenomenon was less evident in Neo and AHPbc. RESEARCH HIGHLIGHTS: TFbc group had a better cell adhesion process of substrate attachment, spreading, and cytoskeleton development on the niche-like structures of the cement than AHPbc and Neo. The sealers tested were able to induce overexpression of the CEMP-1, ALP, and COL1A1 genes in the first days of exposure, particularly in the case of TFbc. All materials tested significantly increased the mineralization of hPDLSCs when compared to the negative control, although more pronounced calcium deposition was observed in the TFbc-treated cells.
Collapse
Affiliation(s)
- Sergio López-García
- Departament d'Estomatologia, Facultat de Medicina I Odontologia, Universitat de València, Valencia, Spain
| | | | - David García-Bernal
- Department of Biochemistry, Molecular Biology B and Immunology, Faculty of Medicine, University of Murcia, IMIB Pascual Parrilla, Murcia, Spain
| | - Adrián Lozano
- Departament d'Estomatologia, Facultat de Medicina I Odontologia, Universitat de València, Valencia, Spain
| | - Leopoldo Forner
- Departament d'Estomatologia, Facultat de Medicina I Odontologia, Universitat de València, Valencia, Spain
| | - José L Sanz
- Departament d'Estomatologia, Facultat de Medicina I Odontologia, Universitat de València, Valencia, Spain
| | - Laura Murcia
- Department of Health Sciences, Catholic University San Antonio of Murcia, Murcia, Spain
| | - Francisco J Rodríguez-Lozano
- Department of Dermatology, Stomatology, Radiology and Physical Medicine, Morales Meseguer Hospital, Faculty of Medicine, University of Murcia, IMIB Pascual Parrilla, Murcia, Spain
| | - Ricardo E Oñate-Sánchez
- Department of Dermatology, Stomatology, Radiology and Physical Medicine, Morales Meseguer Hospital, Faculty of Medicine, University of Murcia, IMIB Pascual Parrilla, Murcia, Spain
| |
Collapse
|
4
|
Jurič R, Vidmar G, Blagus R, Jan J. Factors associated with the outcome of root canal treatment-A cohort study conducted in a private practice. Int Endod J 2024; 57:377-393. [PMID: 38243912 DOI: 10.1111/iej.14022] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 09/19/2023] [Revised: 01/02/2024] [Accepted: 01/03/2024] [Indexed: 01/22/2024]
Abstract
AIM To investigate the association of various pre-, intra- and post-operative factors on root canal treatment outcome. METHODOLOGY In this cohort study, primary or secondary root canal treatment of mature permanent teeth was performed by a single endodontist in a private practice over 13 years, and followed 1-4 years after treatment. Treatment details and clinical and radiographic data were collected. The proportion of successfully treated teeth and roots based on strict radiographic (periapical index (PAI) ≤2) and clinical criteria (absence of pain, swelling or sinus tract) was estimated. To evaluate joint associations of prognostic factors and treatment success probability, 44 pre, intra- and post-operative factors were investigated using bivariate associations, and a multiple logistic regression model was fitted using Generalized Estimating Equations. RESULTS 1259 teeth (2445 roots, 3149 canals) were assessed with a recall rate of 91%. The proportion of successfully treated teeth was 79.9% [95% confidence interval 77.7-82.1]. Eleven prognostic factors were identified that significantly reduced the odds ratio (OR) for treatment success at tooth level. Six were preoperative: injury history (OR = 0.05[0.01-0.24]), root PAI (OR = 0.29[0.20-0.42], 0.21[0.13-0.34] and 0.22[0.12-0.42] for PAI = 3, 4 and 5, respectively, against PAI = 1), lesion diameter (OR = 0.30[0.21-0.43] and 0.24[0.16-0.37] for diameters of 1-5 mm and ≥6 mm, respectively, against no lesion), tooth type (OR = 0.51[0.27-0.97] and OR = 0.45[0.24-0.83] for premolars and molars, respectively, against incisors or canines), tenderness to periapical palpation (OR = 0.64[0.43-0.94]) and two canals per root (OR = 0.67[0.54-0.83]). Four factors were intraoperative: root filling of unsatisfactory quality (OR = 0.18[0.08-0.40]) or extending beyond or shorter than 2 mm from the apex (OR = 0.44[0.26-0.75] and 0.62[0.40-0.97] respectively), resin sealer (OR = 0.58[0.39-0.87] against bioceramic sealer) and single visit treatment (OR = 0.40[0.21-0.75] against multiple visits). One factor was post-operative: defective coronal restoration (OR = 0.35[0.21-0.56]). CONCLUSION The following factors were associated with unsuccessful root canal treatment: (i) history of injury, apical periodontitis with increased severity (larger lesion, higher PAI, tenderness to periapical palpation), or complicated anatomic conditions (premolar or molar, two canals in a single root); (ii) technically suboptimal root filling (of unsatisfactory quality or not ending within 2 mm of radiographic apex) performed in a single-visit, or use of resin sealer instead of novel bioceramic sealer; (iii) suboptimal quality coronal restoration.
Collapse
Affiliation(s)
- Rok Jurič
- Odontos, Private Endodontic Practice, Ljubljana, Slovenia
- Department of Dental Diseases and Endodontics, Faculty of Medicine, University of Ljubljana, Ljubljana, Slovenia
| | - G Vidmar
- University Rehabilitation Institute, Ljubljana, Slovenia
- Faculty of Medicine, Institute for Biostatistics and Medical Informatics, University of Ljubljana, Ljubljana, Slovenia
- Faculty of Mathematics, Natural Sciences and Information Technologies, University of Primorska, Koper, Slovenia
| | - R Blagus
- Faculty of Medicine, Institute for Biostatistics and Medical Informatics, University of Ljubljana, Ljubljana, Slovenia
- Faculty of Mathematics, Natural Sciences and Information Technologies, University of Primorska, Koper, Slovenia
| | - Janja Jan
- Department of Dental Diseases and Endodontics, Faculty of Medicine, University of Ljubljana, Ljubljana, Slovenia
- Department of Restorative Dentistry and Endodontics, University Medical Centre Ljubljana, Ljubljana, Slovenia
| |
Collapse
|
5
|
Menarbazari AA, Mansoori-Kermani A, Mashayekhan S, Soleimani A. 3D-printed polycaprolactone/tricalcium silicate scaffolds modified with decellularized bone ECM-oxidized alginate for bone tissue engineering. Int J Biol Macromol 2024; 265:130827. [PMID: 38484823 DOI: 10.1016/j.ijbiomac.2024.130827] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/16/2023] [Revised: 03/10/2024] [Accepted: 03/11/2024] [Indexed: 03/18/2024]
Abstract
The treatment of large craniofacial bone defects requires more advanced and effective strategies than bone grafts since such defects are challenging and cannot heal without intervention. In this regard, 3D printing offers promising solutions through the fabrication of scaffolds with the required shape, porosity, and various biomaterials suitable for specific tissues. In this study, 3D-printed polycaprolactone (PCL)-based scaffolds containing up to 30 % tricalcium silicate (TCS) were fabricated and then modified by incorporation of decellularized bone matrix- oxidized sodium alginate (DBM-OA). The results showed that the addition of 20 % TCS increased compressive modulus by 4.5-fold, yield strength by 12-fold, and toughness by 15-fold compared to pure PCL. In addition, the samples containing TCS revealed the formation of crystalline phases with a Ca/P ratio near that of hydroxyapatite (1.67). Cellular experiment results demonstrated that TCS have improved the biocompatibility of PCL-based scaffolds. On day 7, the scaffolds modified with DBM and 20 % TCS exhibited 8-fold enhancement of ALP activity of placenta-derived mesenchymal stem/stromal cells (P-MSCs) compared to pure PCL scaffolds. The present study's results suggest that the incorporation of TCS and DBM-OA into the PCL-based scaffold improves its mechanical behavior, bioactivity, biocompatibility, and promotes mineralization and early osteogenic activity.
Collapse
Affiliation(s)
| | | | - Shohreh Mashayekhan
- Department of Chemical and Petroleum Engineering, Sharif University of Technology, Tehran, Iran.
| | - Afsane Soleimani
- Tarbiat Modares University, Faculty of Medical Sciences, Department of Clinical Biochemistry, Tehran, Iran
| |
Collapse
|
6
|
Azizi H, Hadad A, Levy DH, Ben Itzhak J, Kim HC, Solomonov M. Epoxy vs. Calcium Silicate-Based Root Canal Sealers for Different Clinical Scenarios: A Narrative Review. Dent J (Basel) 2024; 12:85. [PMID: 38667997 PMCID: PMC11048901 DOI: 10.3390/dj12040085] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/02/2024] [Revised: 03/02/2024] [Accepted: 03/19/2024] [Indexed: 04/28/2024] Open
Abstract
This study aimed to review the considerations for choosing a suitable sealer according to various endodontic scenarios. An electronic search of PubMed, Scopus, and the Web of Science was undertaken for the keywords of 'sealer choosing', 'appropriate sealer', 'suitable sealer', 'sealer for clinical scenario', and 'sealer for clinical situations'. However, the literature review revealed a lack of studies with practical clinical recommendations regarding the choice of appropriate endodontic root canal sealers for particular clinical situations of root canal treatment. Therefore, a narrative review was undertaken under the basis of the characteristics of an epoxy resin-based sealer (ERS) versus a calcium silicate-based sealer (CSS). Based on the evidence found through the review, the choice of an appropriate sealer in a variety of clinical scenarios was proposed. An ERS is recommended for one-visit non-vital cases, teeth with periodontal involvement, cracked teeth, and internal root resorption without root perforation. A CSS is recommended for vital or non-vital cases in multiple visits, teeth with internal root resorption with perforation or internal approach for external cervical resorption, teeth with open apices, and teeth with iatrogenic aberrations.
Collapse
Affiliation(s)
- Hadas Azizi
- Department of Endodontics, Israel Defense Forces (IDF) Medical Corps, Tel Hashomer, Ramat-Gan, Israel
- “Bina” Program, Faculty of Dental Medicine, Hebrew University of Jerusalem, Jerusalem, Israel
| | - Avi Hadad
- Department of Endodontics, Israel Defense Forces (IDF) Medical Corps, Tel Hashomer, Ramat-Gan, Israel
- “Bina” Program, Faculty of Dental Medicine, Hebrew University of Jerusalem, Jerusalem, Israel
| | - Dan Henry Levy
- Department of Endodontics, Israel Defense Forces (IDF) Medical Corps, Tel Hashomer, Ramat-Gan, Israel
- “Bina” Program, Faculty of Dental Medicine, Hebrew University of Jerusalem, Jerusalem, Israel
| | - Joe Ben Itzhak
- Department of Endodontics, Israel Defense Forces (IDF) Medical Corps, Tel Hashomer, Ramat-Gan, Israel
- “Bina” Program, Faculty of Dental Medicine, Hebrew University of Jerusalem, Jerusalem, Israel
| | - Hyeon-Cheol Kim
- Department of Conservative Dentistry, School of Dentistry, Dental Research Institute, Pusan National University, Yangsan 46241, Republic of Korea;
| | - Michael Solomonov
- Department of Endodontics, Israel Defense Forces (IDF) Medical Corps, Tel Hashomer, Ramat-Gan, Israel
- “Bina” Program, Faculty of Dental Medicine, Hebrew University of Jerusalem, Jerusalem, Israel
| |
Collapse
|
7
|
Elzanaty TK, Elashiry MM, Mahran AH. Retreatability of NeoSEALER Flo obturated with warm vertical compaction versus single-cone technique using two different retreatment systems. JOURNAL OF CONSERVATIVE DENTISTRY AND ENDODONTICS 2024; 27:286-292. [PMID: 38634031 PMCID: PMC11019814 DOI: 10.4103/jcde.jcde_314_23] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 12/07/2023] [Revised: 12/31/2023] [Accepted: 01/02/2024] [Indexed: 04/19/2024]
Abstract
Aim The aim of this study was to compare the retreatability of NeoSEALER Flo obturated with warm vertical compaction (WVC) and single-cone (SC) techniques using two different retreatment systems. Materials and Methods Thirty-two root canals were shaped and obturated with NeoSEALER Flo either in an SC obturation technique or a WVC technique. Samples were retreated using ProTaper retreatment or EdgeFile XR retreatment system. The percentage of remaining debris after retreatment was analyzed under a scanning electron microscope using ImageJ software. The time taken to reach full working length (WL) and induce patency was recorded. Statistical Analysis Statistical analysis was performed using an unpaired t-test and a one-way analysis of variance test. Results The percentage of remaining debris after retreatment was significantly higher in the SC technique than in the WVC technique, regardless of the retreatment system used. EdgeFile XR system removed more filling material than the ProTaper retreatment system, regardless of the obturation technique. The apical region showed significantly higher remaining debris than other regions in all groups. The WL and patency were achieved faster in the SC group, while in the WVC group, the EdgeFile XR system was faster. Conclusions The WVC technique showed better retrieval of the filling material; however, a longer time was taken for retreatment. EdgeFile XR system performed better in removing filling materials from inside the canals.
Collapse
Affiliation(s)
| | - Mohamed M. Elashiry
- Department of Endodontics, Dental College of Georgia, Augusta University, Augusta, GA, USA
- Department of Endodontics, Faculty of Dentistry, Ain Shams University, Cairo, Egypt
| | - Abeer Hashem Mahran
- Department of Endodontics, Faculty of Dentistry, Ain Shams University, Cairo, Egypt
| |
Collapse
|
8
|
Shin B, Seo JH, Kim W, Ahn YJ, Kim HY, Shon WJ. The flow behavior and sealing ability of calcium silicate root canal cement containing dimethyl sulfoxide: An in vitro study. J Mech Behav Biomed Mater 2024; 150:106156. [PMID: 38041883 DOI: 10.1016/j.jmbbm.2023.106156] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/27/2023] [Revised: 09/26/2023] [Accepted: 09/27/2023] [Indexed: 12/04/2023]
Abstract
INTRODUCTION To develop a calcium silicate (CaSi)-based cement containing dimethyl sulfoxide (DMSO) and cement deliver device for new root canal filling technique, and to assess the flow behavior, leakage, and root canal filling quality of CaSi containing DMSO. METHODS CaSi containing DMSO (CSC-DMSO) and CaSi containing PEG (CSC-PEG) were prepared, and the flow characteristics of both cements were compared in gypsum and resin channels using a high-speed camera. Eight root canals were obturated by CSC-DMSO or CSC-PEG using a cement delivery device, and root canal filling quality was assessed in terms of filling length using periapical radiographs. The filling length was evaluated by 'apico-coronal extension,' measuring length in reference to apical constriction. Microleakage was measured for thirty human molars that were randomly filled with CSC-DMSO, CSC-PEG, or gutta-percha and AH plus. Preliminary obturation of CSC-DMSO with cement delivery device in human teeth was analyzed in terms of filling length and void, using periapical radiographs. Statistical analysis was performed with the Kruskal Wallis test for simulated root canal fillings and one-way ANOVA for leakage test. RESULTS The flow speed of CSC-DMSO reduced in gypsum channels compared to resin channels, but CSC-PEG did not exhibit significant differences in the channels. The median absolute value of apico-coronal extension was significantly lower in CSC-DMSO compared to CSC-PEG (p < 0.05). Microleakage did not statistically differ between the groups (p > 0.05). In the preliminary obturation, the mean apico-coronal extension of CSC-DMSO was -0.297 ± 0.724 mm, while CSC-PEG was not feasible due to excess apical extrusions. CONCLUSIONS CSC-DMSO could be considered as an alternative filling material for root canal obturation.
Collapse
Affiliation(s)
- Bokyung Shin
- Department of Conservative Dentistry, Dental Research Institute, Seoul National University School of Dentistry, Daehak-ro 101, Jongro-gu, Seoul, South Korea
| | - Ji-Hwan Seo
- Department of Mechanical Engineering, Seoul National University, Gwanak-ro 1, Gwanak-gu, Seoul, South Korea
| | - Wonjung Kim
- Department of Mechanical Engineering, Sogang University, Seoul, South Korea
| | - Yu Jin Ahn
- Department of Conservative Dentistry, Dental Research Institute, Seoul National University School of Dentistry, Daehak-ro 101, Jongro-gu, Seoul, South Korea
| | - Ho-Young Kim
- Department of Mechanical Engineering, Seoul National University, Gwanak-ro 1, Gwanak-gu, Seoul, South Korea
| | - Won-Jun Shon
- Department of Conservative Dentistry, Dental Research Institute, Seoul National University School of Dentistry, Daehak-ro 101, Jongro-gu, Seoul, South Korea.
| |
Collapse
|
9
|
Makhlouf MP, El Helou JD, Zogheib CE, Makhlouf ACP, Karam ME, Khalil IT. Comparative Evaluation of Push-out Bond Strength of Three Different Root Canal Sealers: An In Vitro Study. J Contemp Dent Pract 2024; 25:15-19. [PMID: 38514426 DOI: 10.5005/jp-journals-10024-3610] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 03/23/2024]
Abstract
AIM The aim of this present study was to compare the dislodgement resistance of calcium silicate-based sealer, zinc oxide sealer, and a new sealer combining both zinc oxide and calcium silicate-based sealer in vitro. MATERIALS AND METHODS 60 single-rooted human teeth were instrumented with F3 Protaper Gold. All endodontic canals were filled using gutta percha cones using the cold lateral condensation technique in combination using one of the mentioned sealers (n = 20 per group). The teeth were divided into three groups: group A consisted of Sealite® Ultra, group B consisted of K-Sealer®, and group C consisted of BioRoot® RC. After 2 months of incubation (37°C, 100% humidity) and after cutting out 2 mm from the most apical portion of the root apex, six slices of 1 mm thickness were generated. Mechanical dislodgement resistance was examined using a universal pressure-testing machine and the push-out bond strength (POBS) was calculated. Specimens were examined under 20× magnification to define the bond failure mode. Statistical analysis was executed using ANOVA, post hoc Turkey test for pairwise comparisons and Kruskal-Wallis tests. RESULTS The POBS of BioRoot® was significantly higher than the POBS of the two other sealers with a mean of 10.54 MPa ± 2.10 and 5.73 MPa ± 2.34, respectively (p < 0.001). Sealite® and K-Sealer® showed similar results in the median and coronal part. K-Sealer® revealed highest POBS compared with Sealite® in the apical part (p < 0.05). CONCLUSION The POBS of the zinc oxide and calcium silicate-based sealer was significantly lower compared with calcium silicate. Sealite® and K-Sealer® exhibited almost same results. BioRoot showed the highest POBS of all sealers. CLINICAL SIGNIFICANCE The current study was needed to evaluate the bond strength of three different cements to dentinal walls, by evaluating their respective POBS in vitro. The findings of this study may provide guidance for the clinician in the selection of an adequate endodontic sealer that guarantees an enhanced adhesive seal between the Gutta-percha and the dentinal canal walls. How to cite this article: Makhlouf MP, El Helou JD, Zogheib CE, et al. Comparative Evaluation of Push-out Bond Strength of Three Different Root Canal Sealers: An In Vitro Study. J Contemp Dent Pract 2024;25(1):15-19.
Collapse
Affiliation(s)
- Michèle Paul Makhlouf
- Department of Endodontics, Faculty of Dentistry, Saint Joseph University, Beirut, Lebanon, Phone: +961-1-(2800)-421000, e-mail:
| | - Joe David El Helou
- Department of Orthodontics - Dentofacial Medicine, Faculty of Medicine, American University of Beirut, Beirut, Lebanon
| | - Carla Elias Zogheib
- Department of Endodontics, Faculty of Dentistry, Saint Joseph University, Beirut, Lebanon
| | | | - Mariana Elie Karam
- Department of Endodontics, Faculty of Dentistry, Saint Joseph University, Beirut, Lebanon
| | - Issam Tanios Khalil
- Department of Endodontics, Faculty of Dentistry, Saint Joseph University, Beirut, Lebanon
| |
Collapse
|
10
|
Quaresma SAL, Alves Dos Santos GN, Silva-Sousa AC, Camargo RV, Silva-Sousa YT, Lopes-Olhê FC, Mazzi-Chaves JF, Sousa-Neto MD. Influence of bioceramic cones on the quality of root canal filling relative to bond strength and adaptation of the adhesive interface. Clin Oral Investig 2023; 27:7919-7933. [PMID: 38032392 DOI: 10.1007/s00784-023-05385-5] [Citation(s) in RCA: 2] [Impact Index Per Article: 2.0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 05/30/2023] [Accepted: 11/13/2023] [Indexed: 12/01/2023]
Abstract
AIM To evaluate the bond strength (BS) and analysis of the adhesive interface in root canals filled with bioceramic gutta percha sealers and cones. MATERIAL AND METHODS Ninety-six maxillary canines were divided into eight groups according to the endodontic sealer (AH Plus, AH Plus Bioceramic, Bio-C Sealer or Bio-C Sealer Ion+ and gutta percha cones (conventional or bioceramic) tested. They were analyzed using the BS test, failure pattern, analysis of the adhesive interface by scanning electron microscopy and confocal laser scanning microscopy. The BS data were compared between groups using the analysis of variance test with the Turkey post-test. The chi-square test was used to assess the type of failure and the non-parametric Mann-Whitney and Kruse-Wallis tests (P < 0.05). RESULTS Analysis of variance showed higher BS values for the groups of bioceramic gutta percha cones in Bio-C Sealer Ion+ (8.38 ± 4.27), AH Plus Bioceramic (6.19 ± 3.28), Bio-C Sealer (5.70 ± 3.18), AH Plus (4.61 ± 2.11) and for conventional gutta percha cones in AH Plus sealers (4.26 ± 2.35), Bio-C Sealer Ion + (3.63 ± 2.29), Bio-C Sealer (2.94 ± 2.32) and AH Plus Bioceramic (1.19 ± 0.89) (P < 0.05). Relative to the type of failure and adaptation of the types of filling material, a higher percentage of mixed failures was observed (gaps between 1 µm-10 µm) for the group with bioceramic gutta percha cones (P < 0.001). CONCLUSION The bond between sealers and bioceramic gutta percha cones showed higher bond strength values and greater penetration into the dentin tubules. CLINICAL RELEVANCE The filling the root canal system with bioceramic sealers should be associated with bioceramic gutta percha cones.
Collapse
Affiliation(s)
- Sérgio André Lopes Quaresma
- Department of Restorative Dentistry, School of Dentistry of Ribeirão Preto, University of São Paulo (USP), Av. do Café, s/n, Ribeirão Preto, São Paulo, 14020-904, Brazil
| | - Guilherme Nilson Alves Dos Santos
- Department of Restorative Dentistry, School of Dentistry of Ribeirão Preto, University of São Paulo (USP), Av. do Café, s/n, Ribeirão Preto, São Paulo, 14020-904, Brazil
| | - Alice Corrêa Silva-Sousa
- Department of Restorative Dentistry, School of Dentistry of Ribeirão Preto, University of São Paulo (USP), Av. do Café, s/n, Ribeirão Preto, São Paulo, 14020-904, Brazil
| | - Rafael Verardino Camargo
- Department of Restorative Dentistry, School of Dentistry of Ribeirão Preto, University of São Paulo (USP), Av. do Café, s/n, Ribeirão Preto, São Paulo, 14020-904, Brazil
| | | | - Fabiane Carneiro Lopes-Olhê
- Department of Restorative Dentistry, School of Dentistry of Ribeirão Preto, University of São Paulo (USP), Av. do Café, s/n, Ribeirão Preto, São Paulo, 14020-904, Brazil
| | - Jardel Francisco Mazzi-Chaves
- Department of Restorative Dentistry, School of Dentistry of Ribeirão Preto, University of São Paulo (USP), Av. do Café, s/n, Ribeirão Preto, São Paulo, 14020-904, Brazil
| | - Manoel Damião Sousa-Neto
- Department of Restorative Dentistry, School of Dentistry of Ribeirão Preto, University of São Paulo (USP), Av. do Café, s/n, Ribeirão Preto, São Paulo, 14020-904, Brazil.
| |
Collapse
|
11
|
Katakidis A, Kodonas K, Fardi A, Gogos C. A scientometric, bibliometric, and thematic map analysis of hydraulic calcium silicate root canal sealers. Restor Dent Endod 2023; 48:e41. [PMID: 38053781 PMCID: PMC10695731 DOI: 10.5395/rde.2023.48.e41] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/11/2023] [Revised: 09/20/2023] [Accepted: 09/21/2023] [Indexed: 12/07/2023] Open
Abstract
Objectives This scientometric and bibliometric analysis explored scientific publications related to hydraulic calcium silicate-based (HCSB) sealers used in endodontology, aiming to describe basic bibliometric indicators and analyze current research trends. Materials and Methods A comprehensive search was conducted in Web of Science and Scopus using specific HCSB sealer and general endodontic-related terms. Basic research parameters were collected, including publication year, authorship, countries, institutions, journals, level of evidence, study design and topic of interest, title terms, author keywords, citation counts, and density. Results In total, 498 articles published in 136 journals were retrieved for the period 2008-2023. Brazil was the leading country, and the universities of Bologna in Italy and Sao Paolo in Brazil were represented equally as leading institutions. The most frequently occurring keywords were "calcium silicate," "root canal sealer MTA-Fillapex," and "biocompatibility," while title terms such as "calcium," "sealers," "root," "canal," "silicate based," and "endodontic" occurred most often. According to the thematic map analysis, "solubility" appeared as a basic theme of concentrated research interest, and "single-cone technique" was identified as an emerging, inadequately developed theme. The co-occurrence analysis revealed 4 major clusters centered on sealers' biological and physicochemical properties, obturation techniques, retreatability, and adhesion. Conclusions This analysis presents bibliographic features and outlines changing trends in HCSB sealer research. The research output is dominated by basic science articles scrutinizing the biological and specific physicochemical properties of commonly used HCSB sealers. Future research needs to be guided by studies with a high level of evidence that utilize innovative, sophisticated technologies.
Collapse
Affiliation(s)
- Anastasios Katakidis
- Department of Endodontology, School of Dentistry, Aristotle University of Thessaloniki, Thessaloniki, Greece
| | - Konstantinos Kodonas
- Department of Endodontology, School of Dentistry, Aristotle University of Thessaloniki, Thessaloniki, Greece
| | - Anastasia Fardi
- Department of Dentoalveolar Surgery, Surgical Implantology & Radiology, School of Dentistry, Aristotle University of Thessaloniki, Thessaloniki, Greece
| | - Christos Gogos
- Department of Endodontology, School of Dentistry, Aristotle University of Thessaloniki, Thessaloniki, Greece
| |
Collapse
|
12
|
Saber S, Galal MM, Ismail AG, Hamdy TM. Thermal, chemical and physical analysis of VDW.1Seal, Fill Root ST, and ADseal root canal sealers. Sci Rep 2023; 13:14829. [PMID: 37684307 PMCID: PMC10491594 DOI: 10.1038/s41598-023-41798-8] [Citation(s) in RCA: 1] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 03/21/2023] [Accepted: 08/31/2023] [Indexed: 09/10/2023] Open
Abstract
This study aimed to evaluate the thermal, chemical, and physical properties of VDW.1Seal, Fill Root ST, and ADseal sealers. Thermal properties were analyzed using Thermogravimetric analysis (TGA) and Differential thermal analysis (DTA). Attenuated total reflection Fourier Transform Infrared Spectroscopy (ATR-FTIR) analysis was performed as a complementary test to confirm TGA/DTA analysis. The chemical composition of the set sealer material was identified using an X-ray powder diffraction (XRD) system. Other physical properties of each sealer were investigated; ten specimens were used to measure the solubility (at 24 h and 28 days), and another ten specimens were used to assess pH changes and calcium ion release (after 7 and 14 days). Film thickness was done according to ISO 6876 specs. The data were analyzed using the two-way ANOVA test. Results showed that for all sealers, TGA analysis revealed a direct relationship between sealer mass loss and temperature rise. In addition, the decomposition of the tested sealers started at 145 °C, 135 °C and 91 °C for VDW.1Seal, ADseal sealer, and Fill Root ST, respectively. XRD analysis revealed a higher degree of crystallinity for VDW.1Seal and ADseal. ADseal showed the least solubility; VDW.1Seal exhibited the highest alkalinity, calcium ion release, and the lowest film thickness.
Collapse
Affiliation(s)
- Shehabeldin Saber
- Endodontic Department, Faculty of Dentistry, The British University in Egypt, 81-11-11 El-Rehab, Cairo, 11841, Egypt.
- Center for Innovative Dental Sciences, The British University in Egypt, El Sherouk City, Egypt.
- Endodontic Department, Faculty of Dentistry, Ain Shams University, Cairo, Egypt.
| | - Manar M Galal
- Restorative and Dental Materials Department, Oral and Dental Research Institute, National Research Centre (NRC), Giza, Dokki, 12622, Egypt
| | - Amira Galal Ismail
- Restorative and Dental Materials Department, Oral and Dental Research Institute, National Research Centre (NRC), Giza, Dokki, 12622, Egypt
| | - Tamer M Hamdy
- Restorative and Dental Materials Department, Oral and Dental Research Institute, National Research Centre (NRC), Giza, Dokki, 12622, Egypt
| |
Collapse
|
13
|
Balbinot GS, Leitune VCB, Zatta KC, Benin T, Guterres SS, Collares FM. Controlled drug delivery from metronidazole-containing bioactive endodontic cements. Dent Mater 2023; 39:839-845. [PMID: 37500315 DOI: 10.1016/j.dental.2023.07.006] [Citation(s) in RCA: 1] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 05/01/2023] [Revised: 07/17/2023] [Accepted: 07/18/2023] [Indexed: 07/29/2023]
Abstract
OBJECTIVES This study aims to formulate metronidazole liquid nanocapsules (MTZLNC) and evaluate their effect on the physicochemical and biological properties of calcium silicate-based bioactive endodontic cements, in vitro. METHODS A MTZLNC suspension was formulated by deposition of the preformed polymer and characterized by laser diffraction and high-performance liquid chromatography (HPLC). Calcium silicate (CS) was mixed with a radiopaque agent (calcium tungstate - CaWO4), at 10 wt%, to produce the cement powder. Cements liquids were used with two concentrations of MTZLNC suspension: 0.3 mg/ml and 0.15 mg/ml. Cements prepared with distilled water were used as the control. The radiopacity, setting time, and flow were evaluated following ISO 6876:2012. The compressive strength analysis was conducted according to ISO 9917:2007. pH and mineral deposition were evaluated after immersion in simulated body fluid (SBF). Cell behavior was evaluated by the viability of pre-osteoblastic cells and pulp fibroblasts by SRB and MTT and the antibacterial activity against Enterococcus faecalis was analyzed immediately and after nine months of water storage. RESULTS MTZLNCs were formulated with a median diameter of 148 nm and 83.44 % load efficiency. Increased flow and reduced strength were observed for both MTZLNCs concentrations. The incorporation of MTZLNCs maintained the ability of cements to increase pH media and promote mineral deposition over the samples, without promoting cytotoxicity. A 2 log10 reduction in E. faecalis CFU was observed immediately and after nine months in water storage. CONCLUSION The formulation of MTZLNCs allowed the development of antibacterial calcium silicate-based-cements with suitable physicochemical properties and bioactivity, with a reduction in mechanical strength. The 0.3 mg/ml concentration in cements liquid promoted effective and sustainable antibacterial activity.
Collapse
Affiliation(s)
- Gabriela Souza Balbinot
- Department of Dental Materials, School of Dentistry, Universidade Federal do Rio Grande do Sul, Porto Alegre, RS, Brazil
| | - Vicente Castelo Branco Leitune
- Department of Dental Materials, School of Dentistry, Universidade Federal do Rio Grande do Sul, Porto Alegre, RS, Brazil
| | - Kelly Cristina Zatta
- Cosmetology and Pharmaceutical Nanotechnology Laboratory, School of Pharmaceutical Sciences, Universidade Federal do Rio Grande do Sul, Av. Ipiranga 2752, 90610-000 Porto Alegre, RS, Brazil
| | - Tainara Benin
- Pharmaceutical Nanotechnology Laboratory, School of Pharmaceutical Sciences, Universidade Federal do Rio Grande do Sul, Av. Ipiranga 2752, 90610-000 Porto Alegre, RS, Brazil
| | - Silvia Stanisçauski Guterres
- Programa de Pós-Graduação em Ciências Farmacêuticas, Universidade Federal do Rio Grande do Sul (UFRGS), Porto Alegre, RS, Brazil; Faculdade de Farmácia, Universidade Federal do Rio Grande do Sul (UFRGS), Porto Alegre, RS, Brazil
| | - Fabricio Mezzomo Collares
- Department of Dental Materials, School of Dentistry, Universidade Federal do Rio Grande do Sul, Porto Alegre, RS, Brazil.
| |
Collapse
|
14
|
Nomura LH, Bortoluzzi EA, Tay FR, Garcia LDFR, Teixeira CDS. The effects of heating on the physicochemical properties of tricalcium silicate root canal sealers. Braz Dent J 2023; 34:34-43. [PMID: 37909640 PMCID: PMC10642270 DOI: 10.1590/0103-6440202305237] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 10/03/2022] [Accepted: 07/16/2023] [Indexed: 11/03/2023] Open
Abstract
This study evaluated the effect of heating on the physicochemical properties and surface changes of tricalcium silicate sealers. Three tricalcium silicate root canal sealers (Bio-C Sealer, BioRoot-RCS, EndoSequence BC Sealer), and one epoxy resin-based sealer (AH Plus; control) were tested. The effect of heating on setting time (ST) and flowability were assessed according to ANSI/ADA 57 and ISO 6876 standards. Solubility and dimensional change (DC) of the set sealers were evaluated at 24 hours and after 30 days; the pH of the water used in the DC testing was also measured. Tests were repeated with heated sealers in an oven at 100 °C for 1 min. SEM and EDS analysis were performed. Data were analyzed using One-Way ANOVA and Tukey post-hoc tests (α=5%). Heating decreased the ST for AH Plus and EndoSequence (p<0.05). Heating reduced flowability (p<0.05) and increased pH for AH Plus (p<0.05). The solubility of Bio-C (dried specimens) was not in accordance with the ANSI/ADA standard. The solubility of EndoSequence was significantly higher (p<0.05) when it was heated and dried after 30 days. DC of Bio-C (24 h and 30 days), BioRoot-RCS (30 days) and AH Plus (24 h and 30 days) were not in accordance with the standards. SEM and EDS analysis showed significant changes in sealer microstructure after heating. In conclusion, heating decreased the ST and increased the solubility of EndoSequence BC sealer. No significant changes in flowability, DC, and pH were identified for all three tricalcium silicate sealers after heat application. However, all sealers had significant surface changes.
Collapse
Affiliation(s)
- Lincon Hideo Nomura
- Department of Dentistry, Federal University of Santa Catarina (UFSC), Florianópolis, SC, Brazil
| | - Eduardo Antunes Bortoluzzi
- Department of Dentistry, Federal University of Santa Catarina (UFSC), Florianópolis, SC, Brazil
- Department of Diagnosis & Oral Health, Division of Endodontics, University of Louisville, Louisville, KY, USA
| | - Franklin R. Tay
- Department of Endodontics, The Dental College of Georgia, Augusta University, GA, USA
| | | | | |
Collapse
|
15
|
Küçükkaya Eren S. Clinical applications of calcium silicate-based materials: a narrative review. Aust Dent J 2023; 68 Suppl 1:S96-S109. [PMID: 37885314 DOI: 10.1111/adj.12986] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Accepted: 10/04/2023] [Indexed: 10/28/2023]
Abstract
Calcium silicate-based materials are hydrophilic materials with biocompatibility and bioactivity properties. Despite many advantages, they might present some problems related to discolouration, setting time, manipulation and solubility depending on the composition of the product and the type of clinical application. Calcium silicate-based materials can be evaluated under two types according to their intended use: calcium silicate-based cements (CSCs) and calcium silicate-based sealers (CSSs). CSCs can be used in many endodontic procedures including perforation repair, resorption repair, apical barriers, guided endodontic repair, vital pulp treatment, endodontic surgery, root fractures and root canal filling as a core obturation material. CSSs are available for use with gutta-percha to obturate root canals using cold and warm techniques, including the sealer-based obturation technique. The purpose of this review is to evaluate the available literature on CSCs and CSSs and to provide up-to-date information and recommendations for their clinical applications.
Collapse
Affiliation(s)
- S Küçükkaya Eren
- Faculty of Dentistry, Department of Endodontics, Hacettepe University, Ankara, Turkey
| |
Collapse
|
16
|
Rebolledo S, Alcántara-Dufeu R, Luengo Machuca L, Ferrada L, Sánchez-Sanhueza GA. Real-time evaluation of the biocompatibility of calcium silicate-based endodontic cements: An in vitro study. Clin Exp Dent Res 2023; 9:322-331. [PMID: 36866428 PMCID: PMC10098287 DOI: 10.1002/cre2.714] [Citation(s) in RCA: 3] [Impact Index Per Article: 3.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 08/19/2022] [Revised: 01/08/2023] [Accepted: 01/16/2023] [Indexed: 03/04/2023] Open
Abstract
INTRODUCTION An ideal filling material should hermetically seal the communication pathways between the canal system and surrounding tissues. Therefore, during the last few years, the development of obturation materials and techniques to create optimal conditions for the proper healing of apical tissues has been a focus of interest. The effects of calcium silicate-based cements (CSCs) on periodontal ligament cells have been investigated, and promising results have been obtained. To date, there are no reports in the literature that have evaluated the biocompatibility of CSCs using a real-time live cell system. Therefore, this study aimed to evaluate the real-time biocompatibility of CSCs with human periodontal ligament cells (hPDLCs). METHODOLOGY hPDLC were cultured with testing media of endodontic cements for 5 days: TotalFill-BC Sealer, BioRoot RCS, Tubli-Seal, AH Plus, MTA ProRoot, Biodentine, and TotalFill-BC RRM Fast Set Putty. Cell proliferation, viability, and morphology were quantified using real-time live cell microscopy with the IncuCyte S3 system. Data were analyzed using the one-way repeated measures (RM) analysis of variance multiple comparison test (p < .05). RESULTS Compared to the control group, cell proliferation in the presence of all cements was significantly affected at 24 h (p < .05). ProRoot MTA and Biodentine lead to an increase in cell proliferation; there were no significant differences with the control group at 120 h. In contrast, Tubli-Seal and TotalFill-BC Sealer inhibited cell growth in real-time and significantly increased cell death compared to all groups. hPDLC co-cultured with sealer and repair cements showed a spindle-shaped morphology except with cements Tubli-Seal and TotalFill-BC Sealer where smaller and rounder cells were obtained. CONCLUSIONS The biocompatibility of the endodontic repair cements performed better than the sealer cements, highlighting the cell proliferation of the ProRoot MTA and Biodentine in real-time. However, the calcium silicate-based TotalFill-BC Sealer presented a high percentage of cell death throughout the experiment similar to that obtained.
Collapse
Affiliation(s)
- Soledad Rebolledo
- Departamento de Odontología Restauradora, Facultad de Odontología, Universidad de Concepción, Concepción, Chile
| | - Raúl Alcántara-Dufeu
- Departamento de Odontología Restauradora, Facultad de Odontología, Universidad de Concepción, Concepción, Chile
| | - Luis Luengo Machuca
- Departamento de Salud Pública, Facultad de Odontología, Universidad de Concepción, Concepción, Chile
| | - Luciano Ferrada
- Facultad de Ciencias Biológicas, Universidad de Concepción, Concepción, Chile
| | | |
Collapse
|
17
|
Biodentine Inhibits the Initial Microbial Adhesion of Oral Microbiota In Vivo. Antibiotics (Basel) 2022; 12:antibiotics12010004. [PMID: 36671205 PMCID: PMC9855060 DOI: 10.3390/antibiotics12010004] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 12/01/2022] [Revised: 12/15/2022] [Accepted: 12/19/2022] [Indexed: 12/24/2022] Open
Abstract
This study aimed to evaluate the in vivo initial microbial adhesion of oral microorganisms on the biomaterial Biodentine compared to MTA and AH Plus. Cylindrical samples of the materials were prepared, and dentin slabs served as a control. An individual intraoral lower jaw splint served as a carrier for the samples and was worn by six volunteers. The specimens were worn for 120 min. Adherent bacteria were quantified by determining the colony-forming units (CFUs), while the visualization and quantification of total adherent microorganisms were facilitated by using DAPI and live/dead staining combined with fluorescence microscopy. Bovine dentin had a significantly higher number of aerobic CFUs compared to Biodentine (p = 0.017) and MTA (p = 0.013). The lowest amounts of DAPI-stained adherent microorganisms were quantified for Biodentine (15% ± 9%) and the control (18% ± 9%), while MTA showed the highest counts of initially adherent microorganisms (38% ± 10%). Significant differences were found for MTA and Biodentine (p = 0.004) as well as for MTA and the control (p = 0.021) and for AH Plus and the control (p = 0.025). Biodentine inhibited microbial adherence, thereby yielding an antimicrobial effectivity similar to that of MTA.
Collapse
|
18
|
Donnermeyer D, Schemkämper P, Bürklein S, Schäfer E. Short and Long-Term Solubility, Alkalizing Effect, and Thermal Persistence of Premixed Calcium Silicate-Based Sealers: AH Plus Bioceramic Sealer vs. Total Fill BC Sealer. MATERIALS (BASEL, SWITZERLAND) 2022; 15:7320. [PMID: 36295385 PMCID: PMC9607285 DOI: 10.3390/ma15207320] [Citation(s) in RCA: 16] [Impact Index Per Article: 8.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Figures] [Subscribe] [Scholar Register] [Received: 09/28/2022] [Revised: 10/12/2022] [Accepted: 10/14/2022] [Indexed: 06/16/2023]
Abstract
This study aimed to investigate the short- and long-term solubility, alkalizing potential, and suitability for warm-vertical compaction of AH Plus Bioceramic Sealer (AHBC), and Total Fill BC Sealer (TFBC) compared to the epoxy-resin sealer AH Plus (AHP). A solubility test was performed according to ISO specification 6876 and further similar to ISO requirements over a period of 1 month in distilled water (AD) and 4 months in phosphate-buffered saline (PBS). The pH of the immersion solution was determined weekly. Sealers were exposed to thermal treatment at 37, 57, 67, and 97 °C for 30 s. Furthermore, heat treatment at 97 °C was performed for 180 s to simulate inappropriate implementation of warm vertical filling techniques. Physical properties (setting time, flow, film thickness according to ISO 6876) and chemical properties (Fourier transformed infrared spectroscopy) were assessed. AHBC and TFBC were associated with significantly higher solubility than AHP over 1 month in AD and 4 months in PBS (p < 0.05). AHBC and TFBC both reached high initial alkaline pH, while TFBC was associated with a longer-lasting alkaline potential than AHBC. Initial pH of AHBC and TFBC was higher in AD than in PBS. None of the sealers were compromised by thermal treatment.
Collapse
Affiliation(s)
- David Donnermeyer
- Department of Periodontology and Operative Dentistry, Westphalian Wilhelms-University, Albert-Schweitzer-Campus 1, Building W 30, 48149 Münster, Germany
| | - Patrick Schemkämper
- Department of Periodontology and Operative Dentistry, Westphalian Wilhelms-University, Albert-Schweitzer-Campus 1, Building W 30, 48149 Münster, Germany
| | - Sebastian Bürklein
- Central Interdisciplinary Ambulance in the School of Dentistry, Albert-Schweitzer-Campus 1, Building W 30, 48149 Münster, Germany
| | - Edgar Schäfer
- Central Interdisciplinary Ambulance in the School of Dentistry, Albert-Schweitzer-Campus 1, Building W 30, 48149 Münster, Germany
| |
Collapse
|
19
|
Gutmann J, Manjarrés V, De La Espriella C. Revisiting the future of root canal obturation. ENDODONTOLOGY 2022. [DOI: 10.4103/endo.endo_142_22] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/04/2022] Open
|