Radioiodine-131 Therapy Used for Differentiated Thyroid Cancer Can Impair Titanium Dental Implants: An In Vitro Analysis

BACKGROUND

The aim was to assess, in vitro, the effects of radioiodine-131 (I-131) on the structure of titanium implants.

MATERIAL AND METHODS

A total of 28 titanium implants were divided into 7 groups (n = 4) and irradiated at 0, 6, 12, 24, 48, 192 and 384 hours. At the end of the experiment, each sample was investigated via scanning electron microscopy (SEM) and electrochemical measures.

RESULTS

The control sample revealed a smooth and compact surface. The small micro-sized porosity is slightly visible at the macroscopic level, but the precise details cannot be observed. A mild exposure to the radioactive solution for 6 to 24 h showed a good preservation of the macro-structural aspects such as thread details and surface quality. Significant changes occurred after 48 h of exposure. It was noticed that the open-circuit potential (OCP) value of the non-irradiated implants move toward more noble potentials during the first 40 min of exposure to the artificial saliva and then stabilizes at a constant value of -143 mV. A displacement of the OCP values toward more negative values was observed for all irradiated implants; these potential shifts are decreasing, as the irradiation period of the tested implants increased.

CONCLUSION

After exposure to I-131, the structure of titanium implants is well preserved up to 12 h. The eroded particles start to appear in the microstructural details after 24 h of exposure and their numbers progressively increase up to 384 h after exposure.

The Side Effects of Therapeutic Radioiodine-131 on the Structure of Enamel and Dentin in Permanent Human Teeth

Simple Summary

Our research suggest radioiodine-131 used for differentiated thyroid carcinomas has an impact on the oral health of patients. We found that alteration of dental hard tissues starts after 6 h post-radioiodine administration. These findings highlight the importance of the multidisciplinary team management in the quality of life of the oncological patient.

Abstract

Radioiodine-131 (I-131) is an essential therapy for patients with differentiated thyroid carcinomas (DTC). Generally, I-131 is safe and well tolerated, but patients may present early or late complications in the oral and maxillofacial areas. Thus, the aim of this study was to evaluate in-vitro, the alteration of enamel and dentin after I-131 exposure using histopathological assessment, scanning electron microscopy (SEM) and atomic force microscopy (AFM). For I-131 irradiation, an in-vitro protocol was used that simulates the procedure for irradiation therapy performed for patients with DTCs. A total of 42 teeth were divided into seven groups (n = 6) and irradiated as follows: control, irradiation groups (3, 6, 12, 36, 48 h, 8 days). Histological changes were observed at 48 h (enamel surface with multifocal and irregular areas) and at 8 days (enamel surface with multiple, very deep, delimited cavities). SEM imaging revealed the enamel destruction progresses along with the treatment time increasing. The alterations are extended into the enamel depth and the dislocated hydroxyapatite debris is overwhelming. The enamel-dentine interface shows small gaps after 6 h and a very well developed valley after 12 h; the interface microstructure resulted after 8 days is deeply altered. The AFM imaging shows that I-131 affects the protein bond between hydroxyapatite nano-crystals causing loss of cohesion, which leads to significant increasing of nano-particles diameter after 6 h. In conclusion, both enamel and dentin appear to be altered between 12 and 48 h and after 8 days of treatment are extended in depth.