Comparative studies on PADC polymeric detector treated by gamma radiation and Ar ion beam

Comparative Study of Impact of Gamma and MeV Ion Irradiations on Electrical and Optical Properties Polystyrene/Eu2O3 Nanocomposites

In the present study, the effect of gamma irradiation and 90 MeV carbon ion beam irradiation on electrical properties and optical of Polystyrene/Eu2O3 nanocomposites at different fluences were examined. Modified electrical and optical responses of polymer nanocomposites were investigated using Impedance, Photoluminescence and UV-VIS spectroscopies. FTIR analysis shows a reduction of various modes of molecular vibrations caused by 90 MeV carbon ion beam irradiation. The polymer nanocomposites change into a graphite-like structure upon both kinds of irradiations as evidenced by the decrease in the optical band gap. The photoluminescence emission spectra show three characteristic peaks of Eu3+ ions, when excited at 247 nm wavelength. It emits intense red light suggesting its potential for usage in LED technology. The peak intensity of PL emission spectra is enhanced after ion beam irradiation and is because of the formation new radiative combination; however, it decreases upon gamma irradiation. Dielectric responses of pristine and irradiated polymer nanocomposites were studied over the frequency range of 100 Hz to 100 kHz using LCR meter. There appears a significant improvement in the dielectric response as a result of structural changes in both types of irradiations. AFM images show that the film becomes smoother upon both types of irradiations.

PLASMA-ETCHING AND MODIFICATION OF POLYETHYLENE FOR IMPROVED SURFACE STRUCTURE, WETTABILITY AND OPTICAL BEHAVIOR

In the present paper, the surface modification of low-density polyethylene (LDPE) polymer is done by plasma-etching to tune its surface structure, wettability and optical behavior to make it useful for technical applications. For this purpose, two gasses (N[Formula: see text] and (O[Formula: see text] are used as the discharge precursors in a home-built plasma reactor. The plasma-treated LDPE surface etch-rate (control other surface properties) is high at the beginning and slows down as the treatment time increases due to surface restructuring. The etched surfaces are analyzed by scanning electron microscopy (SEM), which indicate greater surface changes due to O2 plasma compared to that of N2. Also, the surface hardness is slightly low at the first treatment time and increases rapidly at higher exposure durations. Besides, the friction coefficient is significantly changed by plasma treatment, suggesting the formation of cohesive surface skin. The obtained X-ray diffraction (XRD) patterns show that the plasma-treated LDPE samples suffer disordering and structural changes which increase with raising the treatment duration. Surface restructuring is attributed to the combined effects of active species (from plasma) bombardments and surface oxidation. Also, the surface chemistry changes are evaluated using attenuated total reflection Fourier-transform infrared (ATR-FTIR) spectroscopy which reveals chain scission after N2 plasma treatment. Whereas, the O2 plasma-treated samples suffer surface oxidation and formation of polar groups which offer some surface oxidation coatings. Furthermore, the surface wettability has been determined by the sessile drop method and shows enhancement upon plasma treatment due to the combined influence of surface chemistry and morphology. Also, the surface free energy (SFE) and adhesion are found to increase with the plasma exposure time due to surface activation. The optical behavior of LDPE is studied using ultraviolet–visible (UV–Vis) spectrophotometer which indicates that the optical bandgap performance depends on the amorphous or crystalline nature of the polymer. Also, the conjugated carbon atoms were examined and correlated to the reduced bandgap. In conclusion, the studied home-built glow discharge plasma reactor could be utilized efficiently to tune polymer surface properties to be used in high technology applications.