Quiñones-Gurrola JR, Rendón-Angeles JC, Matamoros-Veloza Z, López-Cuevas J, Pérez-Garibay R, Yanagisawa K. Facile Preparation of SrZr
1-xTi
xO
3 and SrTi
1-xZr
xO
3 Fine Particles Assisted by Dehydration of Zr
4+ and Ti
4+ Gels under Hydrothermal Conditions.
NANOMATERIALS (BASEL, SWITZERLAND) 2023;
13:2195. [PMID:
37570513 PMCID:
PMC10420865 DOI:
10.3390/nano13152195]
[Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Subscribe] [Scholar Register] [Received: 07/06/2023] [Revised: 07/20/2023] [Accepted: 07/21/2023] [Indexed: 08/13/2023]
Abstract
In recent decades, perovskite-type compounds (ABB'O3) have been exhaustively studied due to their unique ferroelectric properties. In this work, a systematic study aiming to prepare fine particles in the binary system SrZrO3-SrTiO3 was conducted under hydrothermal conditions in a KOH (5 M) solution at 200 °C for 4 h under a constant stirring speed of 130 rpm. The precursors employed were SrSO4 powder (<38 μm size) and coprecipitated hydrous gels of Zr(OH)4•9.64 H2O (Zr-gel) and Ti(OH)4•4.5H2O (Ti-gel), which were mixed according to the stoichiometry of the SrZr1-xTixO3 in the compositional range of 0.0 > x > 100.0 mol% Ti4+. The XRD results revealed the formation of two crystalline phases rich in Zr4+, an orthorhombic structured SrZr0.93Ti0.07O3 and a cubic structured SrZr0.75Ti0.25O3 within the compositional range of 0.1-0.5 mol of Ti4+. A cubic perovskite structured solid solution, SrTi1-xZrxO3, was preferentially formed within the compositional range of 0.5 > x > 0.1 mol% Ti4+. The SrZrO3 and SrZr0.93Ti0.07O3-rich phases had particle sizes averaging 3 μm with a cubic morphology. However, a remarkable reduction in the particle size occurred on solid solutions prepared with hydrous Ti-gel over contents of 15 mol% Ti4+ in the reaction media, resulting in the formation of nanosized particle agglomerates with a cuboidal shape self-assembled via a 3D hierarchical architecture, and the sizes of these particles varied in the range between 141.0 and 175.5 nm. The limited coarsening of the particles is discussed based on the Zr-gel and Ti-gel dehydration capability differences that occurred under hydrothermal processing.