The mechanism of suspension reduction on Fe enrichment with low-grade carbonate-containing iron ore

Eco-friendly strategy for preparation of high-purity silica from high-silica IOTs using S-HGMS coupling with ultrasound-assisted fluorine-free acid leaching technology

Iron ore tailings (IOTs), a typical hazardous solid waste, seriously threaten human health and the ecological environment. However, the abundance of quartz, particularly in high-silica IOTs, renders them useful. Yet, state-of-the-art technologies have rarely reported the preparation of high-purity silica from high-silicon IOTs. Thus, this study proposed an eco-friendly technology for producing high-purity silica from high-silica IOTs through the coupling of superconducting high gradient magnetic separation (S-HGMS) preconcentration with leaching followed by the use of ultrasound-assisted fluorine-free acid solution. Following an analysis of the separation index and chemical composition, the optimum conditions for the quartz preconcentration were determined as a magnetic flow ratio of 0.068 T s/m, a slurry flow velocity of 500 mL/min, and a pulp concentration of 40 g/L. Consequently, the SiO₂ grade increased from 69.32% in the raw sample to 93.12% in quartz concentrate following the application of S-HGMS, with the recovery reaching 45.24%. X-ray diffraction, vibrating sample magnetometer, and scanning electron microscope analyses indicated that quartz was effectively preconcentrated from the tailings by S-HGMS. Subsequently, employing the "ultrasound-assisted fluorine-free acid leaching process," impurity elements were removed and high-purity silica was produced. Under optimal leaching conditions, the SiO₂ purity of silica sand increased to 97.42%. Following a three-stage acid leaching process with 4 mol/LHCl +2 mol/LH₂C₂O₄, the removal efficiency of Al, Ca, Fe, and Mg exceeded 97% for all cases, and the SiO₂ purity in high-purity silica reached 99.93%. Thus, this study proposes a new strategy for the preparation of high-purity quartz from IOTs, which facilitated the effective realization of the high-value utility of the tailings. Furthermore, it provides a theoretical basis for the industrial application of IOTs, which is of great scientific significance and practical application value.

Pilot Study on a New Conveyor Bed Magnetization Roasting Process for Efficient Iron Extraction from Low-Grade Siderite

Realizing the large-scale development and utilization of siderite, a difficult iron ore reserve, has great practical significance in ensuring the supply of iron ore resources. Therefore, a new in-house conveyor bed magnetization roasting–dry cooling process was pilot-tested using low-grade siderite from the Daxigou iron ore mine. A two-stage weak magnetic separation method was used for a beneficiation test to investigate the influence of temperature and CO content on the magnetization of siderite. At 600 °C and 800 °C under suspension, iron minerals were converted into magnetite with an effective 3–5 s residence time. Furthermore, at 600 °C and 750 °C, increasing the calcination temperature increased the iron grade and the concentrate recovery rate. However, calcination at temperatures >750 °C resulted in a slight decrease in the iron grade and recovery rate of the concentrate. 61.50% Fe grade and 80.30% concentrate recovery rate were obtained under 750 °C from magnetization roasting. Magnetization roasting in a reducing atmosphere provides mainly magnetite as the roasted ore, and increased CO content can efficiently promote this effect. At 700–780 °C and when the CO content was increased to more than 3 wt.%, the improvement of the roasting effect was very limited. Rapid cooling of the roasted ore using a mixture of circulating exhaust gas and air could prevent considerable oxidation of the magnetic ferrous material. Therefore, the preferred process conditions are 700–780 °C with a CO content range of 1–3%. It provided a concentrate iron grade of 59.27–61.50% and a recovery rate of 78.32–80.30%. The results of this study provide a reference for the development of conveyor bed magnetization technology, process design, and production control.

High-Efficiency Iron Extraction from Low-Grade Siderite via a Conveyor Bed Magnetization Roasting-Magnetic Separation Process: Kinetics Research and Applications

Upgrading and utilizing low-grade iron ore is of great practical importance to improve the strategic security of the iron ore resource supply. In this study, a thermal analysis-infrared (IR) analysis-in-situ IR method was used to investigate the reaction mechanism and kinetics of Daxigou siderite. Experiments were conducted using a conveyor bed magnetization roasting process (CBMRP) to investigate the magnetization of siderite. Multi-stage magnetic separation processes were adopted to extract magnetite. The results show that simultaneously the iron carbonate in siderite decomposes, and magnetite is formed between 364 °C and 590 °C under both inert and reducing atmospheres. The activation energy of the magnetization roasting reaction is 106.1 kJ/mol, consistent with a random nucleation and growth reaction mechanism. Magnetization roasting at 750-780 °C for approximately 3.5 s in the CBMRP results in a magnetic conversion rate of >0.99 of the iron minerals in the siderite. A beneficiation process of one roughing, one sweeping, and three cleaning processes was adopted. A dissociation particle size of -400 mesh accounting for 94.78%, a concentrate iron grade of 62.8 wt.%, and a recovery of 68.83% can be obtained. Overall, a theoretical and experimental basis is presented for the comprehensive utilization of low-grade siderite.