Preheating acrylic bone cement powder is not recommended for all brands

Ambient theatre temperature and cement setting time in total knee arthroplasty

BACKGROUND

Polymethylmethacrylate cement is used in total knee arthroplasty and plays a significant role in the success of the procedure. Temperature variation is known to influence cement setting time in vitro. Our aim is to evaluate the relationship between ambient theatre temperature and cement setting time in vivo.

METHODS

Theatre temperature and cement setting time were prospectively recorded during 683 total knee arthroplasties over 8 years using a single cement and vacuum mixing system (Simplex with tobramycin). Setting time was defined as the time until a scalpel blade could not indent the cement surface.

RESULTS

Mean temperature was 18.92°C (SD 1.16) and setting time 13.08 min (SD 1.92). A moderate inverse relationship exists between ambient temperature and setting time (Pearson's R = -0.423); however, potential setting times within a given temperature range varied considerably (<19°C: 8-19.1 min, 19-20°C: 7-18 min and >20°C: 7.5-16 min), suggesting that temperature alone cannot reliably predict setting time.

CONCLUSION

Our data support the current understanding of bone cement properties in vivo and suggest that surgeons should be mindful in regards to unpredictable cement setting time and optimal theatre environment.

Not all approved antibiotic-loaded PMMA bone cement brands are the same: ranking using the utility materials selection concept

In the literature on in vitro characterization of approved antibiotic-loaded poly(methyl methacrylate) bone cement brands, there is no information on the basis for selection of a given brand for use in cemented arthroplasties. This shortcoming is addressed in the present study. It involved determining four key properties (fatigue limit, fracture toughness, polymerization rate, and phosphate buffered saline diffusion coefficient) for six brands and then using the mean property values, in conjunction with a materials selection methodology, called the utility concept, to rank the brands. It is emphasized that the present work is an illustration of a rational approach to selection of a cement brand and, as such, the study findings are not intended to be recommendations regarding clinical use or otherwise of a brand.

Pore distribution and material properties of bone cement cured at different temperatures

Implant heating has been advocated as a means to alter the porosity of the bone cement/implant interface; however, little is known about the influence on cement properties. This study investigates the mechanical properties and pore distribution of 10 commercially available cements cured in molds at 20, 37, 40 and 50 degrees Celsius. Although each cement reacted differently to the curing environments, the most prevalent trend was increased mechanical properties when cured at 50 degrees Celsius vs. room temperature. Pores were shown to gather near the surface of cooler molds and near the center in warmer molds for all cement brands. Pore size was also influenced. Small pores were more often present in cements cured at cooler temperatures, with higher-temperature molds producing more large pores. The mechanical properties of all cements were above the minimum regulatory standards. This work shows the influence of curing temperature on cement properties and porosity characteristics, and supports the practice of heating cemented implants to influence interfacial porosity.