Excellent survivorship of the Morscher monoblock cup with a 28-mm Metasul-on-Metasul bearing at a mean of 5-year follow-up

Minimum 15-year results of metasul 28-mm metal-on-metal total hip arthroplasty in patients younger than 50 years of age

Background

Some propitious mid- and long-term studies had been reported for MoM bearings; however, most studies have addressed specific patient groups rather than younger, active patients, who probably represent the most suitable population for investigations on wear and osteolysis. The purpose of this study to evaluate the long-term results of second-generation metal-on-metal cementless total hip arthroplasty (THA) in patients aged <50 years.

Methods

From December 1997 to January 2004, primary THA using a metal-on-metal bearing cementless implant was performed in 63 patients (72 hips) aged <50 years. The mean follow-up duration was 18.6 (range, 15.9–22.1) years, and the mean age at initial operation was 39 (range, 22–49) years. Clinical results, complications, survivorship, osteolysis, and aseptic loosening were evaluated.

Results

The mean Harris hip score and Western Ontario and McMaster Universities Arthritis Index scores were improved from 57.8 (range, 28–69) points and 73.4 (range, 63–94) points preoperatively to 91.7 (range, 80–100) points and 25.5 points (range, 17–38) points, respectively, at the last follow-up. Osteolysis lesions were found in 12 hips (acetabulum, 6 and femur, 6). The notching occurred on the femoral stem neck occurred in 12 hips. The mean serum cobalt and chromium concentrations were 2.3 (range, 0.2–10.6) μg/L and 1.7 (range, 0.4–8.1) μg/L, respectively, at a mean follow-up of 12.7 years in 32 patients (50.1%). The Kaplan-Meier survivorship curve analysis with revision for any reason as the endpoint revealed that 93.1% survived at 18.6 years’ follow-up.

Conclusions

Second-generation metal-on-metal cementless THA was found to produce satisfactory clinical and radiographic results with a low revision rate for osteolysis and aseptic loosening in patients aged less than 50 years.

A comparative assessment of small-head metal-on-metal and ceramic-on-polyethylene total hip replacement

Large-head metal-on-metal (MoM) total hip replacements (THR) have given rise to concern. Comparative studies of small-head MoM THRs over a longer follow-up period are lacking. Our objective was to compare the incidence of complications such as infection, dislocation, revision, adverse local tissue reactions, mortality and radiological and clinical outcomes in small-head (28 mm) MoM and ceramic-on-polyethylene (CoP) THRs up to 12 years post-operatively. A prospective cohort study included 3341 THRs in 2714 patients. The mean age was 69.1 years (range 24 to 98) and 1848 (55.3%) were performed in women, with a mean follow-up of 115 months (18 to 201). There were 883 MoM and 2458 CoP bearings. Crude incidence rates (cases/1000 person-years) were: infection 1.3 vs 0.8; dislocation 3.3 vs 3.1 and all-cause revision 4.3 vs 2.2, respectively. There was a significantly higher revision rate after ten years (adjusted hazard ratio 9.4; 95% CI 2.6 to 33.6) in the MoM group, and ten of 26 patients presented with an adverse local tissue reaction at revision. No differences in mortality, osteolysis or clinical outcome were seen. In conclusion, we found similar results for small-head MoM and CoP bearings up to ten years post-operatively, but after ten years MoM THRs had a higher risk of all-cause revision. Furthermore, the presence of an adverse response to metal debris seen in the small-head MOM group at revision is a cause for concern.