Effect of Bearing Type on Taper Material Loss in Hips From 1 Manufacturer

Interfacial compliance, energy dissipation, frequency effects, and long-term fretting corrosion performance of Ti-6Al-4V/CoCrMo interfaces

Fretting corrosion in modular orthopedic implants is a well-documented process that may be associated with adverse local tissue reactions, pain, and revisions. Engineering modular junction interfaces to withstand applied fretting motion without surface abrasion could prevent implant degradation and surface damage. Previous work on geometrically modified Ti-6Al-4V/CoCrMo interfaces with increased compliance showed reduced fretting currents and surface damage during short term, variable-load in vitro testing. This study assesses the same interfaces under long-term conditions using an in vitro pin-on-disk fretting corrosion test apparatus. Preliminary variable-load frequency testing of typical control pin geometries showed a frequency-dependent current response, with underlying contact conditions of metal-metal interfaces that remained unchanged. One-million-cycle testing showed diminished fretting currents in all groups by 5 × 10⁵  cycles, but consistently lower currents in the high-compliance group. Corresponding fretting currents and work of fretting measurements of high-compliance pins confirmed that minimal fretting was experienced at the interface, with elastic bending of the pin accounting for almost all applied displacement. Debris generated during testing were composed of titanium and chromium oxides, small amounts of cobalt and molybdenum oxides, and sodium and phosphate originating from the surrounding test solution. Post-test analyses of sample surfaces revealed substantially more surface damage on CoCrMo disks than Ti-6Al-4V pins, thought to be a result of adhesive wear of mixed oxide debris on the pin and abrasion of the disk by the oxide debris layer. Surface damage to high-compliance pins suggests some abrasion is unavoidable with geometric modifications.

Taper corrosion: a complication of total hip arthroplasty

The focus on taper corrosion in modular hip arthroplasty increased around 2007 as a result of clinical problems with large-head metal-on-metal (MoM) bearings on standard stems. Corrosion problems with bi-modular primary hip stems focused attention on this issue even more.

Factors increasing the risk of taper corrosion were identified in laboratory and retrieval studies: stiffness of the stem neck, taper diameter and design, head diameter, offset, assembly force, head and stem material and loading.

The high variability of the occurrence of corrosion in the clinical application highlights its multi-factorial nature, identifying the implantation procedure and patient-related factors as important additional factors for taper corrosion.

Discontinuing the use of MoM has reduced the revisions due to metal-related pathologies dramatically from 49.7% (MoM > 32 mm), over 9.2% (MoM ⩽ 32 mm) to 0.8% (excluding all MoM).

Further reduction can be achieved by omitting less stiff Ti-alloys and large metal heads (36 mm and above) against polyethylene (PE).

Standardized taper assembly of smaller and ceramic heads will reduce the clinical occurrence of taper corrosion even further. If 36 mm heads are clinically indicated, only ceramic heads should be used.

Taper-related problems will not comprise a major clinical problem anymore if the mentioned factors are respected.

Cite this article: EFORT Open Rev 2020;5:776-784. DOI: 10.1302/2058-5241.5.200013

Does diametrical clearance influence the wear of Pinnacle hip implants?

Aims

The optimum clearance between the bearing surfaces of hip arthroplasties is unknown. Theoretically, to minimize wear, it is understood that clearances must be low enough to maintain optimal contact pressure and fluid film lubrication, while being large enough to allow lubricant recovery and reduce contact patch size. This study aimed to identify the relationship between diametrical clearance and volumetric wear, through the analysis of retrieved components.

Methods

A total of 81 metal-on-metal Pinnacle hips paired with 12/14 stems were included in this study. Geometrical analysis was performed on each component, using coordinate and roundness measuring machines. The relationship between their as-manufactured diametrical clearance and volumetric wear was investigated. The Mann-Whitney U test and unpaired t-test were used, in addition to calculating the non-parametric Spearman's correlation coefficient, to statistically evaluate the acquired data.

Results

The hips in this study were found to have had a median unworn diametrical clearance of 90.31 μm (interquartile range (IQR) 77.59 to 97.40); 32% (n = 26) were found to have been below the manufacturing tolerance. There was no correlation found between clearance and bearing (r_s = -0.0004, p = 0.997) or taper (r_s = 0.0048, p = 0.966) wear rates. The wear performance of hips manufactured within and below these specifications was not significantly different (bearing: p = 0.395; taper: p = 0.653). Pinnacles manufactured from 2007 onwards had a greater prevalence of bearing clearance below tolerance (p = 0.004).

Conclusion

The diametrical clearance of Pinnacle hips did not influence their wear performance, even when below the manufacturing tolerance. The optimum clearance for minimizing hip implant wear remains unclear.Cite this article: Bone Joint Res 2020;9(8):515-523.

Hip simulator testing of the taper-trunnion junction and bearing surfaces of contemporary metal-on-cross-linked-polyethylene hip prostheses

Adverse reaction to metal debris released from the taper-trunnion junction of modular metal-on-polyethylene (MoP) total hip replacements (THRs) is an issue of contemporary concern. Therefore, a hip simulator was used to investigate material loss, if any, at both the articulating and taper-trunnion surfaces of five 32-mm metal-on-cross-linked-polyethylene THRs for 5 million cycles (Mc) with a sixth joint serving as a dynamically loaded soak control. Commercially available cobalt-chromium-molybdenum femoral heads articulating against cross-linked polyethylene (XLPE) acetabular liners were mounted on 12/14 titanium (Ti6Al4V) trunnions. Weight loss (mg) was measured gravimetrically and converted into volume loss (mm³ ) for heads, liners, and trunnions at regular intervals. Additionally, posttest volumetric wear measurements of the femoral tapers were obtained using a coordinate measuring machine (CMM). The surface roughness (Sa) of femoral tapers was measured posttest. After 5 Mc, the mean volumetric wear rate for XLPE liners was 2.74 ± 0.74 mm³ /Mc. The CMM measurements confirmed material loss from the femoral taper with the mean volumetric wear rate of 0.045 ± 0.024 mm³ /Mc. The Sa on the worn area of the femoral taper showed a significant increase (p < 0.001) compared with the unworn area. No other long-term hip simulator tests have investigated wear from the taper-trunnion junction of contemporary MoP THRs. © 2019 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 108B:156-166, 2020.

Wear performance of retrieved metal-on-metal Pinnacle hip arthroplasties implanted before and after 2007

Objectives

Previous studies have suggested that metal-on-metal (MoM) Pinnacle (DePuy Synthes, Warsaw, Indiana) hip arthroplasties implanted after 2006 exhibit higher failure rates. This was attributed to the production of implants with reduced diametrical clearances between their bearing surfaces, which, it was speculated, were outside manufacturing tolerances. This study aimed to better understand the performance of Pinnacle Systems manufactured before and after this event.

Methods

A total of 92 retrieved MoM Pinnacle hips were analyzed, of which 45 were implanted before 2007, and 47 from 2007 onwards. The ‘pre-2007’ group contained 45 implants retrieved from 21 male and 24 female patients, with a median age of 61.3 years (interquartile range (IQR) 57.1 to 65.5); the ‘2007 onwards’ group contained 47 implants retrieved from 19 male and 28 female patients, with a median age of 61.8 years (IQR 58.5 to 67.8). The volume of material lost from their bearing and taper surfaces was measured using coordinate and roundness measuring machines. These outcomes were then compared statistically using linear regression models, adjusting for potentially confounding factors.

Results

There was no significant difference between the taper and bearing wear rates of the ‘pre-2007’ and ‘2007 onwards’ groups (p = 0.67 and p = 0.39, respectively). Pinnacles implanted from 2007 onwards were revised after a mean time of 50 months, which was significantly earlier than the ‘pre-2007’ hips (96 months) (p < 0.001). A reduction in the time to revision was present year on year from 2003 to 2011.

Conclusion

We found no difference in the wear rate of these implants based on the year of implantation. The ‘pre-2007’ hips had a two-fold greater time to revision than those implanted after 2007; this may be due to the increased surveillance of MoM hips following UK regulatory advice and several high-profile failures. Interestingly, we observed a decreasing trend in the mean time to revision every year from 2003 onwards.

Cite this article: S. Bergiers, H. S. Hothi, J. Henckel, A. Eskelinen, J. Skinner, A. Hart. Wear performance of retrieved metal-on-metal Pinnacle hip arthroplasties implanted before and after 2007. Bone Joint Res 2018;7:595–600. DOI: 10.1302/2046-3758.711.BJR-2018-0143.R1.