Letter to the Editor on "Trunnion Failure of the Recalled Low Friction Ion Treatment Cobalt Chromium Alloy Femoral Head"

Quantification of trunnion damage in a series of intact total hip arthroplasty femoral stems previously identified to be at risk of catastrophic failure

BACKGROUND

Corrosion at the head-neck junction of femoral stems is a rare complication of total hip arthroplasty (THA) with manifestations ranging from subclinical wear to failure. Prior studies have identified a single femoral component design with an increased propensity for catastrophic trunnion failure. The purpose of the present study was to quantify trunnion damage of this femoral component retrieved from patients undergoing revision THA for non-trunnionosis indications.

METHODS

24 femoral components from a single manufacturer were identified for study inclusion. Each prosthesis underwent stereomicroscopic inspection. Corrosion and fretting scores were assigned per the Goldberg criteria to quadrants of the trunnion. Material loss was calculated based on cone angles across trunnion quadrants. This was carried out using a coordinate measuring machine that digitised each trunnion surface. Stems were compared to a series of femoral stems with the same trunnion design.

RESULTS

20 of the 24 (83%) trunnions demonstrated corrosion, all 24 trunnions demonstrated fretting. Corrosion scores did not statistically differ with respect to trunnion zone (p = 0.53), while fretting scores were higher in the inferior compared to the superior zones (p < 0.001). There was no significant difference in cone angles assessing material loss between stems (p = 0.25).

CONCLUSIONS

Evidence of trunnion damage was observed in each stem retrieved for non-trunnionosis revision. Fretting occurred more frequently about the inferior quadrants. However, digitised trunnion shapes were similar between compared stems exhibiting no material loss. Therefore, it is possible that previous reports of trunnion failures for this implant are not a systemic issue, and that further investigation is required.

High Incidence of Mechanically Assisted Crevice Corrosion at 10 Years in Non-Cemented, Non-Recalled, Contemporary Total Hip Arthroplasties

BACKGROUND

One percent to 3% of contemporary non-cemented total hip arthroplasties (THAs) present with symptomatic mechanically assisted crevice corrosion (MACC). The incidence of this problem, however, as well as the rate of asymptomatic elevations in serum cobalt, is unknown.

METHODS

Cobalt and chromium levels were obtained in conjunction with radiographs at routine 10-year surveillance follow-up of THAs from a single manufacturer with a titanium stem, cobalt alloy femoral head, and cross-linked polyethylene countersurface.

RESULTS

Ten-year follow-up of patients with 162 consecutive THAs revealed that 17 patients with 18 hips had died of unrelated causes prior to metal ion testing. Two hips were revised for other reasons, and of the remaining 142 hips, 33 were in patients who were lost, leaving 109 hips (77% of those in alive patients and unrevised for other reasons and 67% of the entire cohort) for investigation. Sixty-three patients (58%) had a serum cobalt less than 1 ppb, and 35 (32%) a cobalt of ≥1 ppb, a cutoff consistent with MACC. Of the 32 hips with definite MACC, 15 of 32 (47%) patients were symptomatic, 16 of 30 (53%) patients had adverse local tissue reaction on magnetic resonance imaging, and 19 of 32 (59%) patients have undergone revision surgery for MACC to date.

CONCLUSION

At 10-year follow-up, a minimum of 22% (35/162) of hips had a cobalt level more than 1 ppb, consistent with MACC. Symptoms and adverse local tissue reactions are each present about one-half of the time, and 59% of those with documented MACC have undergone revision.

Outcomes Following Revision for Mechanically Assisted Crevice Corrosion in a Single Femoral Design

BACKGROUND

Mechanically assisted crevice corrosion (MACC) is a described complication following metal-on-polyethylene (MoP) total hip arthroplasty (THA). The literature regarding outcomes following revision for MACC suggests that complication rates are high. The purpose of this investigation is to add to this literature with the largest reported series to date.

METHODS

This is a retrospective cohort study of 552 consecutive patients who underwent 621 MoP primary THAs. We identified patients who subsequently underwent revision THA for a diagnosis of MACC. All patients were implanted with the same implant combination (Accolade I stem/cobalt-chromium low friction ion treatment femoral head). Patient demographic, surgical, and laboratory data were collected. Follow-up was calculated from the revision surgery and Hip Disability and Osteoarthritis Outcome Score Joint Replacement and hip subjective values (HSV) were examined at final follow-up. Descriptive statistics were performed.

RESULTS

The revision rate for MACC was 11.6% and mean time to revision was 6.6 (±2.4) years. Revised patients (n = 69) had a mean preoperative serum cobalt-chromium ratio of 3.5 (±2.4). There were 8 cases of gross trunnion failure. At mean 3.2 (±1.9) years following revision, the overall major complication rate was 11.6% with a 5.8% reoperation rate. At final follow-up, mean Hip Disability and Osteoarthritis Outcome Score Joint Replacement scores were 83.2 (±15.6) and mean hip subjective value was 77.6 (±17.4). Revision resulted in significant increases in both parameters (P < .001).

CONCLUSION

The incidence of MACC in MoP THA is likely higher than previously reported, particularly for certain implant combinations. Revision surgery for MACC can achieve good outcomes but a high clinical suspicion with early detection and revision is likely key to success.

Barbed sutures reduce arthrotomy closure duration compared to interrupted conventional sutures for total knee arthroplasty: a randomized controlled trial

BACKGROUND

The broad aim of this study was to compare the safety and efficacy of using barbed sutures versus standard-of-care sutures for closure of arthrotomy during total knee arthroplasty. Specifically, we compared the duration of arthrotomy closure, the number of sutures utilized for arthrotomy closure, and 90-day outcomes, including wound-related readmission, reoperation, and complications.

MATERIALS AND METHODS

A total of 60 patients undergoing primary total knee arthroplasty were enrolled in a prospective, blinded trial and randomized to receive either running closure of the arthrotomy with barbed sutures (n = 30) or interrupted closure with standard-of-care sutures (n = 30).

RESULTS

Arthrotomy closure time was significantly shorter in the barbed suture group (3 min ± 2 min) versus the standard-of-care group (13 min ± 5 min, p < 0.001). The average suture utilization for arthrotomy closure was 1 suture (range 1-2) versus 3 sutures (range 2-4) in the standard-of-care group (p < 0.001). The overall number of wound-related complications in the barbed suture group was 3/30 (10%) versus 3/30 (10%) in the standard-of-care group (p = 1.00). There was one dehiscence 1/30 (3%) in the standard-of-care group versus zero in the barbed suture group (p = 1.00). The rate of superficial surgical site infection was 1/30 (3%) in barbed suture versus zero in the standard-of-care groups (p = 1.00).

CONCLUSION

These results suggest barbed suture utilization may be faster and more resource-efficient than the use of standard-of-care sutures for arthrotomy closure in primary total knee arthroplasty without increased complications. CLINICALTRIALS.

GOV IDENTIFIER

NCT03285529.