In vitro mineralisation of grafted ePTFE membranes carrying carboxylate groups

Elastomeric, bioadhesive and pH-responsive amphiphilic copolymers based on direct crosslinking of poly(glycerol sebacate)-co-polyethylene glycol

Poly(glycerol sebacate) (PGS), a synthetic biorubber, is characterised by its biocompatibility, high elasticity and tunable mechanical properties; however, its inherent hydrophobicity and insolubility in water make it unsuitable for use in advanced biomaterials like hydrogels fabrication. Here, we developed new hydrophilic PGS-based copolymers that enable hydrogel formation through use of two different types of polyethylene glycol (PEG), polyethylene glycol (PEG2) or glycerol ethoxylate (PEG3), combined at different ratios. A two-step polycondensation reaction was used to produce poly(glycerol sebacate)-co-polyethylene glycol (PGS-co-PEG) copolymers that were then crosslinked thermally without the use of initiators or crosslinkers, resulting in PGS-co-PEG2 and PGS-co-PEG3 amphiphilic polymers. It has been illustrated that the properties of PGS-co-PEG copolymers can be controlled by altering the type and amount of PEG. PGS-co-PEG copolymers containing PEG ≥ 40% showed high swelling, flexibility, stretching, bioadhesion and biocompatibility, and good enzymatic degradation and mechanical properties. Also, the addition of PEG created hydrogels that demonstrated pH-responsive behaviours, which can be used for bioapplications requiring responding to physicochemical dynamics. Interestingly, PGS-co-40PEG2 and PGS-co-60PEG3 had the highest shear strengths, 340.4 ± 49.7 kPa and 336.0 ± 35.1 kPa, and these are within the range of commercially available sealants or bioglues. Due to the versatile multifunctionalities of these new copolymer hydrogels, they can have great potential in soft tissue engineering and biomedicine.

In vitro mineralization of dual grafted polytetrafluoroethylene membranes

The modification of biomaterials by radiation induced grafting is a promising method to improve their bioactivity. Successful introduction of carboxyl and amine functional groups on the surface of a polytetrafluoroethylene membrane was achieved by grafting of acrylic acid (AA) and 2-aminoethyl methacrylate hydrochloride (AEMA) using simultaneous gamma irradiation grafting. Chemical characterization by attenuated total reflectance Fourier transform infrared spectroscopy and x-ray photoelectron spectroscopy confirmed the presence of amine and carboxylate functionalities and indicated that all protonated amines formed ion pairs with carboxyl groups, but not all carboxyl are involved in ion pairing. It was found that the irradiation doses (2, 5, or 10 kGy) affected the grafting outcome only when sulfuric acid (0.5 or 0.9 M) was added as a polymerization enhancer. The use of the inorganic acid successfully enhanced the total graft yield (GY), but the changes in the graft extent (GE) were not conclusive. Dual functional films were produced by either a one- or a two-step process. Generally, higher GY and GE values were observed for the samples produced by the two-step grafting of AA and AEMA. The in vitro mineralization in 1.5× simulated body fluid (SBF) induced the formation of carbonated hydroxyapatite as verified by FITR. All samples showed an increase in weight after mineralization with significantly larger increases observed for the samples which had the 1.5× SBF changed every third day compared to every seventh. For the dual functional samples, it was found that the sample grafted by the one-step method shows a significantly higher increase in weight despite a much lower GY compared to the sample prepared by the two-step method and this was attributed to the different architecture of grafted chains.