Correlation between signalment and the biphasic hyperelastic mechanical properties of equine articular cartilage

Comparison Between the Hyperelastic Behavior of Fresh and Frozen Equine Articular Cartilage in Various Joints

Fresh and frozen cartilage samples of the fetlock, carpus, and stifle were collected from 12 deceased horses. Half were measured immediately following extraction, and half were frozen for seven days and then measured. Seven indentations (various normalized displacements) were implemented with an indention rate of 0.1 mm/s. Solid phase aggregate modulus (Es), hyperelastic material constant (α), and fluid load fraction (F') of equine articular cartilage were assessed using the Ogden hyperelastic model. The properties were statistically compared in various joints (fetlock, carpus, and stifle), and between fresh and frozen samples using various statistical models. There was no statistical difference between the fetlock and carpus in the aggregate modulus (p = 0.5084), while both were significantly different from the stifle (fetlock: p = 0.0017 and carpus: p = 0.0406). For the hyperelastic material constant, no statistical differences between joints were observed (p = 0.3310). For the fluid load fraction, the fetlock and stifle comparison showed a difference (p = 0.0333), while the carpus was not different from the fetlock (p = 0.1563) or stifle (p = 0.3862). Comparison between the fresh and frozen articular cartilage demonstrated no significant difference among the joints in the three material properties: p = 0.9418, p = 0.7031, and p = 0.9313 for the aggregate modulus, the hyperelastic material constant, and the fluid load fraction, respectively.

A Comparison of Friction Measurements of Intact Articular Cartilage in Contact with Cartilage, Glass, and Metal

The goal of this study was to develop a method of friction testing utilizing cartilage counter surfaces with a complete subchondral bone plate and compare the results to the cartilage on glass and metal (steel) counter surfaces. Articular cartilage surfaces with the underlying subchondral bone intact were not isolated through plug removal. Friction testing was completed using a tribometer (n=16). The coefficient of friction (COF) was measured between the proximal articular surfaces of the second carpal bone when brought into contact with the articular surface of the distal radial facet. The COF of the distal radial facet was obtained with glass and metal counter surfaces. Cartilage-cartilage interfaces yielded the lowest COF when a normal force of 5N and 10N was applied. No statistically significant increase in COF was noted for any combination when an increased normal force was applied (10N), although an increase was observed when glass and metal was in contact with cartilage. COF significantly increased when comparing the cartilage counter surface to metal under an applied load of 5N (p=0.0002). When a 10N load was applied, a significant increase in the COF was observed when comparing the cartilage counter surface to both the glass and metal counter surfaces (p=0.0123 and p < 0.0001 respectively). Results have shown that the described methodology was accurate, repeatable, and emulates physiologic conditions when determining the friction coefficient. The determined COF of cartilage against cartilage is significantly lower than cartilage against metal or glass.