A brief review of bio-tribology in cardiovascular devices

Design, preparation, and characterization of lubricating polymer brushes for biomedical applications

The lubrication modification of biomedical devices significantly enhances the functionality of implanted interventional medical devices, thereby providing additional benefits for patients. Polymer brush coating provides a convenient and efficient method for surface modification while ensuring the preservation of the substrate's original properties. The current research has focused on a "trial and error" method to finding polymer brushes with superior lubricity qualities, which is time-consuming and expensive, as obtaining effective and long-lasting lubricity properties for polymer brushes is difficult. This review summarizes recent research advances in the biomedical field in the design, material selection, preparation, and characterization of lubricating and antifouling polymer brushes, which follow the polymer brush development process. This review begins by examining various approaches to polymer brush design, including molecular dynamics simulation and machine learning, from the fundamentals of polymer brush lubrication. Recent advancements in polymer brush design are then synthesized and potential avenues for future research are explored. Emphasis is placed on the burgeoning field of zwitterionic polymer brushes, and highlighting the broad prospects of supramolecular polymer brushes based on host-guest interactions in the field of self-repairing polymer brush applications. The review culminates by providing a summary of methodologies for characterizing the structural and functional attributes of polymer brushes. It is believed that a development approach for polymer brushes based on "design-material selection-preparation-characterization" can be created, easing the challenge of creating polymer brushes with high-performance lubricating qualities and enabling the on-demand creation of coatings. STATEMENT OF SIGNIFICANCE: Biomedical devices have severe lubrication modification needs, and surface lubrication modification by polymer brush coating is currently the most promising means. However, the design and preparation of polymer brushes often involves "iterative testing" to find polymer brushes with excellent lubrication properties, which is both time-consuming and expensive. This review proposes a polymer brush development process based on the "design-material selection-preparation-characterization" strategy and summarizes recent research advances and trends in the design, material selection, preparation, and characterization of polymer brushes. This review will help polymer brush researchers by alleviating the challenges of creating polymer brushes with high-performance lubricity and promises to enable the on-demand construction of polymer brush lubrication coatings.

Influence of Surface Texturing on the Dry Tribological Properties of Polymers in Medical Devices

There is a constant need to improve patient comfort and product performance associated with the use of medical devices. Efforts to optimise the tribological characteristics of medical devices usually involve modifying existing devices without compromising their main design features and functionality. This article constitutes a state-of-the-art review of the influence of dry friction on polymeric components used in medical devices, including those having microscale surface features. Surface tribology and contact interactions are discussed, along with alternative forms of surface texturing. Evident gaps in the literature, and areas warranting future research are highlighted; these include friction involving polymer Vs polymer surfaces, information regarding which topologies and feature spacings provide the best performing textured surfaces, and design guidelines that would assist manufacturers to minimise or maximise friction under non-lubricated conditions.

Compression of the vascular wall to create a friction fit in a vascular anastomotic coupler

A previously reported microvascular coupler was shown to effectively create vascular anastomoses, but was too large for practical clinical use. To safely reduce coupler size, certain failure modes needed to be better understood. The coupler functions, in part, by compressing the vessel wall between two concentric rings, creating a friction fit that anchors the device to the vessel. This work investigates the relationship between vessel wall compression and resulting friction fit strength to ensure reducing coupler size will not unduly increase the risk that this friction fit might fail. Vascular walls were compressed to a specified strain and the tensile force required to overcome the resulting friction was measured. Experiments were conducted with various vessel types (Porcine common carotid artery, splenic artery, and jugular vein), across a range of compressive strains (55-95%), and by using either PEEK or HDPE to compress the vessel. Tensile force was increased at a rate of 5 g/min or held constant for 24 h. For experiments with incrementally increasing force, the force at failure varied with compressive strain via a power function. At 70% compression, PEEK produced 4.6 times stronger friction fits than HDPE, and common carotid arteries and splenic arteries produced 1.8 and 1.3 times stronger fits than jugular veins respectively. For experiments where tensile force was applied for 24 h, much lower forces were required to overcome friction. These results were compared to friction fit failure in a coupler prototype and it was found that the prototypes failed at just 30% of the force required to cause vessel slip under the other test conditions. These results were used to develop a model that predicts the probability of device failure via vessel slipping (one design, smaller than previously reported, was estimated to fail at maximum in vivo axial stress once in 500 anastomoses, a potentially safe level of risk).

A review study on blood in human coronary artery: Numerical approach

Computational fluid dynamics (CFD) study of blood flow in human coronary artery is one of the emerging fields of Biomed- ical engineering. In present review paper, Finite Volume Method with governing equations and boundary conditions are briefly discussed for different coronary models. Many researchers have come up with astonishing results related to the various factors (blood viscosity, rate of blood flow, shear stress on the arterial wall, Reynolds number, etc.) affecting the hemodynamic of blood in the right/left coronary artery. The aim of this paper is to present an overview of all those work done by the researchers to justify their work related to factors which hampers proper functioning of heart and lead to Coronary Artery Disease (CAD). Governing equations like Navier-stokes equations, continuity equations etc. are widely used and are solved using CFD solver to get a clearer view of coronary artery blockage. Different boundary conditions and blood properties published in the last ten years are summarized in the tabulated form. This table will help new researchers to work on this area.

Characterizing fretting damage in different test media for cardiovascular device durability testing

In vitro durability tests of cardiovascular devices are often used to evaluate the potential for fretting damage during clinical use. Evaluation of fretting damage is important because severe fretting can concentrate stress and lead to the loss of structural integrity. Most international standards call for the use of phosphate buffered saline (PBS) for such tests although there has been little evidence to date that the use of PBS is appropriate in terms of predicting the amount of fretting damage that would occur in vivo. In order to determine an appropriate test media for in vitro durability tests where fretting damage is being evaluated, we utilized an in vitro test that is relevant to cardiovascular devices both in terms of dimensions and materials (nitinol, cobalt-chromium, and stainless steel) to characterize fretting damage in PBS, deionized water (DIW), and heparinized porcine blood. Overall, tests conducted in blood were found to have increased levels of fretting damage over tests in DIW or PBS, although the magnitude of this difference was smaller than the variability for each test media. Tests conducted in DIW and PBS led to mostly similar amounts of fretting damage with the exception of one material combination where DIW had greatly reduced damage compared to PBS and blood. Differences in fretting damage among materials were also observed with nitinol having less fretting damage than stainless steel or cobalt-chromium. In general, evaluating fretting damage in PBS or DIW may be appropriate although caution should be used when selecting test media and interpreting results given some of the differences observed across different materials.