TOCN/copper calcium titanate composite aerogel films as high-performance triboelectric materials for energy harvesting

High-performance dielectric film capacitors based on cellulose/Al2O3 nanosheets/PVDF composites

The design and preparation of novel renewable biomass-based dielectric composites have drawn great attention recently. Here, cellulose was dissolved in NaOH/urea aqueous solution, and Al₂O₃ nanosheets (AONS) synthesized by hydrothermal method were used as fillers. Then the regenerated cellulose (RC)-AONS dielectric composite films were prepared by regeneration, washing and drying. The two-dimensional AONS had a better effect on improving the dielectric constant and breakdown strength of the composites, so that the RC-AONS composite film with 5 wt% AONS content reached an energy density of 6.2 J/cm³ at 420 MV/m. Furthermore, in order to improve the dielectric energy storage properties of cellulose films in high humidity environment, the hydrophobic polyvinylidene fluoride (PVDF) was innovatively introduced to construct RC-AONS-PVDF composite films. The energy storage density of the prepared ternary composite films could reach 8.32 J/cm³ at 400 MV/m, which was 416 % improvement against that of the commercially biaxially oriented polypropylene (2 J/cm³), and could be cycled for >10,000 times under 200 MV/m. Concurrently, the water absorption of the composite film in humidity was effectively reduced. This work broadens the application prospect of biomass-based materials in the field of film dielectric capacitor.

Rational Design of Cellulosic Triboelectric Materials for Self-Powered Wearable Electronics

With the rapid development of the Internet of Things and flexible electronic technologies, there is a growing demand for wireless, sustainable, multifunctional, and independently operating self-powered wearable devices. Nevertheless, structural flexibility, long operating time, and wearing comfort have become key requirements for the widespread adoption of wearable electronics. Triboelectric nanogenerators as a distributed energy harvesting technology have great potential for application development in wearable sensing. Compared with rigid electronics, cellulosic self-powered wearable electronics have significant advantages in terms of flexibility, breathability, and functionality. In this paper, the research progress of advanced cellulosic triboelectric materials for self-powered wearable electronics is reviewed. The interfacial characteristics of cellulose are introduced from the top-down, bottom-up, and interfacial characteristics of the composite material preparation process. Meanwhile, the modulation strategies of triboelectric properties of cellulosic triboelectric materials are presented. Furthermore, the design strategies of triboelectric materials such as surface functionalization, interfacial structure design, and vacuum-assisted self-assembly are systematically discussed. In particular, cellulosic self-powered wearable electronics in the fields of human energy harvesting, tactile sensing, health monitoring, human-machine interaction, and intelligent fire warning are outlined in detail. Finally, the current challenges and future development directions of cellulosic triboelectric materials for self-powered wearable electronics are discussed.

Investigating the thermal conductivity and flame-retardant properties of BN/MoS2/PCNF composite film containing low BN and MoS2 nanosheets loading

Cellulose has attracted considerable attention as a potential substitute for plastics. However, the flammability and high thermal insulation properties of cellulose contradict the unique requirements for highly integrated and miniaturized electronics i.e., rapid thermal dissipation and efficient flame retardancy. In this work, cellulose was first phosphorylated to achieve intrinsic flame-retardant properties, and subsequently treated with MoS₂ and BN, ensuring efficient dispersion throughout the material. Via chemical crosslinking, a sandwich-like unit was formed, in the order of BN, MoS₂, and phosphorylated cellulose nanofibers (PCNF). The sandwich-like units were further self-assembled, layer-by-layer, to successfully create BN/MoS₂/PCNF composite films exhibiting excellent thermal conductivity and flame retardancy, and comprised a low MoS₂ and BN loading. The thermal conductivity of the BN/MoS₂/PCNF composite film containing 5 wt% BN nanosheets was higher than that of neat PCNF film. The combustion characterization of BN/MoS₂/PCNF composite films revealed highly desirable properties that were far more superior than the BN/MoS₂/TCNF (TCNF, TEMPO-oxidized cellulose nanofibers) composite films. Moreover, the toxic volatiles that escaped from flaming BN/MoS₂/PCNF composite films were significantly reduced compared to that of the BN/MoS₂/TCNF composite film alternative. The thermal conductivity and flame retardancy of BN/MoS₂/PCNF composite films have promising application prospects in highly integrated and eco-friendly electronics.