Hydrogen peroxide improving crystallinity of TiO2 nanoparticle in layer compound

Temperature-dependent breakdown of hydrogen peroxide-treated ZnO and TiO2 nanoparticle agglomerates

Metal oxide nanoparticles (MONPs) are used in a variety of applications including drug formulations, paint, sensors and biomedical devices due to their unique physicochemical properties. One of the major problems with their widespread implementation is their uncontrolled agglomeration. One approach to reduce agglomeration is to alter their surface chemistry with a proper functionality in an environmentally friendly way. In this study, the influence of hydrogen peroxide (H2O2) treatment on the dispersion of ZnO and TiO2 nanoparticle (NP) agglomerates as a function of temperature is studied. The H2O2 treatment of the MONPs increases the density of hydroxyl (-OH) groups on the NP surface, as verified with FTIR spectroscopy. The influence of heating on the dispersion of H2O2-treated ZnO and TiO2 NPs is investigated using dynamic light scattering. The untreated and H2O2-treated ZnO and TiO2 NP suspensions were heated from 30 °C to 90 °C at 5 °C intervals to monitor the breakdown of large aggregates into smaller aggregates and individual nanoparticles. It was shown that the combined effect of hydroxylation and heating enhances the dispersion of ZnO and TiO2 NPs in water.

Investigation on transition crystal of ordinary rutile TiO2 powder and its sonocatalytic activity

The transition crystal TiO(2) sonocatalyst was prepared utilizing the method of ultrasonic irradiation in hydrogen peroxide solution. The sonocatalytic activity of the transition crystal TiO(2) powder was validated through the degradation of methyl orange in aqueous solution by ultrasonic irradiation. The results show that the sonocatalytic activity of the transition crystal TiO(2) powder is obviously higher than that of pure rutile and anatase TiO(2) powders as well as mixed rutile and anatase TiO(2) powders according to the proportion of corresponding transition crystal TiO(2) catalyst. The degradation ratio of methyl orange in the presence of the transition crystal TiO(2) catalyst surpasses 75% within 80 min ultrasonic irradiation, while the degradation ratios are 55.93%, 51.68% and 40.88%, respectively, for rutile, mixed and anatase TiO(2) powders.

Photocatalytic remediation of gamma-hexachlorocyclohexane contaminated soils using TiO2 and montmorillonite composite photocatalyst

TiO2 and montmorillonite composite photocatalysts were prepared and applied in degrading gamma-hexachlorocyclohexane (gamma-HCH) in soils. After being spiked with gamma-HCH, soil samples loaded with the composite photocatalysts were exposed to UV-light irradiation. The results indicated that the photocatalytic activities of the composite photocatalysts varied with the content of TiO2 in the order of 10% < 70% < 50% < 30%. Moreover, the photocatalytic activity of the composite photocatalysts with TiO2 content 30% was higher than that of the pure P25 with the same mass of TiO2. The strong adsorption capacity of the composite photocatalysts and quantum size effect may contribute to its increased photocatalytic activities. In addition, effect of dosage of composite photocatalysts and soil pH on gamma-HCH photodegradation was investigated. Pentachlorocyclohexene, trichlorocyclohexene, and dichlorobenzene were detected as photodegradation intermediates, which were gradually degraded with the photodegradation evolution.