Transient response method for characterization of active sites in HZSM-5 with low content of iron during N2O decomposition

N2O Decomposition over Fe-ZSM-5: A Systematic Study in the Generation of Active Sites

We have carried out a systematic investigation of the critical activation parameters (i.e., final temperature (673–1273 K), atmosphere (He vs. O₂/He), and final isothermal hold (1 min–15 h) on the generation of “α-sites”, responsible for the direct N₂O decomposition over Fe-ZSM-5 (Fe content = 1200–2300 ppm). The concentration of α-sites was determined by (ia) transient response of N₂O and (ib) CO at 523 K, and (ii) temperature programmed desorption (TPD) following nitrous oxide decomposition. Transient response analysis was consistent with decomposition of N₂O to generate (i) “active” α-oxygen that participates in the low-temperature CO→CO₂ oxidation and (ii) “non-active” oxygen strongly adsorbed that is not released during TPD. For the first time, we were able to quantify the formation of α-sites, which requires a high temperature (>973) treatment of Fe-ZSM-5 in He over a short period of time (<1 h). In contrast, prolonged high temperature treatment (1273 K) and the presence of O₂ in the feed irreversibly reduced the amount of active sites.

Theoretical Study of N2O Reduction by CO in Fe-BEA Zeolite

Quantum mechanical (QM) and QM/molecular mechanics (MM) studies of the full catalytic cycle of N(2)O reduction by CO in Fe-BEA zeolite, that is, oxidation of BEA-Fe by N(2)O and reduction of BEA-Fe-alphaO by CO, is presented. A large QM cluster, representing half of the channel of the BEA zeolite, is used. The contribution of the MM embedding to the calculated activation energies is found to be negligible. The minimum-energy paths for N(2)O decomposition and reduction with CO are calculated using the nudged elastic band (NEB) method. Calculated and experimental activation energies are in good agreement. The two possible orientations for the gaseous molecules adsorbing on the Fe site that are found lead to different activation energies.

Nitrous Oxide Decomposition over Fe-ZSM-5 in the Presence of Nitric Oxide: A Comprehensive DFT Study

A number of experimental studies have shown recently that ppm-level additions of nitric oxide (NO) enhance the rate of nitrous oxide (N(2)O) decomposition catalyzed by Fe-ZSM-5 at low temperatures. In the present work, the NO-assisted N(2)O decomposition over mononuclear iron sites in Fe-ZSM-5 was studied on a molecular level using density functional theory (DFT) and transition-state theory. A reaction network consisting of over 100 elementary reactions was considered. The structure and energies of potential-energy minima were determined for all stable species, as were the structures and energies of all transition states. Reactions involving changes in spin potential-energy surfaces were also taken into account. In the absence of NO and at temperatures below 690 K, most active single iron sites (Z(-)[FeO](+)) are poisoned by small concentrations of water in the gas phase; however, in the presence of NO, these poisoned sites are converted into a novel active iron center (Z(-)[FeOH](+)). These latter sites are capable of promoting the dissociation of N(2)O into a surface oxygen atom and gas-phase N(2). The surface oxygen atom is removed by reaction with NO or nitrogen dioxide (NO(2)). N(2)O dissociation is the rate-limiting step in the reaction mechanism. At higher temperatures, water desorbs from inactive iron sites and the reaction mechanism for N(2)O decomposition becomes independent of NO, reverting to the reaction mechanism previously reported by Heyden et al. [J. Phys. Chem. B 2005, 109, 1857].

Role of Adsorbed NO in N2O Decomposition over Iron-Containing ZSM-5 Catalysts at Low Temperatures

Transient response and temperature-programmed desorption/reaction (TPD/TPR) methods were used to study the formation of adsorbed NO(x) from N2O and its effect during N2O decomposition to O2 and N2 over FeZSM-5 catalysts at temperatures below 653 K. The reaction proceeds via the atomic oxygen (O)(Fe) loading from N2O on extraframework active Fe(II) sites followed by its recombination/desorption as the rate-limiting step. The slow formation of surface NO(x,ads) species was observed from N2O catalyzing the N2O decomposition. This autocatalytic effect was assigned to the formation of NO(2,ads) species from NO(ads) and (O)(Fe) leading to facilitation of (O)(Fe) recombination/desorption. Mononitrosyl Fe2+(NO) and nitro (NO(2,ads)) species were found by diffuse reflectance infrared fourier transform spectroscopy (DRIFTS) in situ at 603 K when N2O was introduced into NO-containing flow passing through the catalyst. The presence of NO(x,ads) does not inhibit the surface oxygen loading from N2O at 523 K as observed by transient response. However, the reactivity of (O)(Fe) toward CO oxidation at low temperatures (<523 K) is drastically diminished. Surface NO(x) species probably block the sites necessary for CO activation, which are in the vicinity of the loaded atomic oxygen.

Formation of the Surface NO during N2O Interaction at Low Temperature with Iron-Containing ZSM-5

Interaction of N2O at low temperatures (473-603 K) with Fe-ZSM-5 zeolites (Fe, 0.01-2.1 wt %) activated by steaming and/or thermal treatment in He at 1323 K was studied by the transient response method and temperature-programmed desorption (TPD). Diffuse reflectance infrared fourier transform spectroscopy (DRIFTS) of NO adsorbed at room temperature as a probe molecule indicated heterogeneity of surface Fe(II) sites. The most intensive bands were found at 1878 and 1891 cm(-1), characteristic of two types mononitrosyl species assigned to Fe2+(NO) involved in bi- and oligonuclear species. Fast loading of atomic oxygen from N2O on the surface and slower formation of adsorbed NO species were observed. The initial rate of adsorbed NO formation was linearly dependent on the concentration of active Fe sites assigned to bi- and oligonuclear species, evolving oxygen in the TPD at around 630-670 K. The maximal coverage of a zeolite surface by NO was estimated from the TPD of NO at approximately 700 K. This allowed the simulation of the dynamics of the adsorbed NO formation at 523 K, which was consistent with the experiments. The adsorbed NO facilitated the atomic oxygen recombination/desorption, the rate determining step during N2O decomposition to O2 and N2, taking place at temperatures > or =563 K.