Regulation of mixed Ag valence state by non-thermal plasma for complete oxidation of formaldehyde

Synergically regulated silver species and surface oxygen on manganese oxide for promoted activity of formaldehyde oxidation

Formaldehyde (HCHO) is a common indoor pollutant that is detrimental to human health. Its efficient removal has become an urgent demand to reduce the public health risk. In this work, Ag-MnOx-based catalysts were prepared and activated under different atmosphere (i.e., air, hydrogen (H2) and carbon monoxide (CO)) for efficient oxidation of HCHO. The catalyst activated with CO (Ag/Mn-CO) displayed the highest activity among the tested samples with 90% conversion at 100°C under a gas space velocity of 75,000 mL/(gcat·hr). Complementary characterizations demonstrate that CO reduction treatment resulted in synergically regulated content of surface oxygen on support to adsorb/activate HCHO and size of Ag particle to dissociate oxygen to oxidize the adsorbed HCHO. In contrast, other catalysts lack for either abundant surface oxygen species or metallic silver with the appropriate particle size, so that the integrate activity is limited by one specific reaction step. This study contributes to elucidating the mechanisms regulating the oxidation activity of Ag-based catalysts.

Novel synergistically effects of palladium-iron bimetal and manganese carbonate carrier for catalytic oxidation of formaldehyde at room temperature

The elimination of formaldehyde at room temperature holds immense potential for various applications, and the incorporation of a catalyst rich in surface hydroxyl groups and oxygen significantly enhances its catalytic activity towards formaldehyde oxidation. By employing a coprecipitation method, we successfully achieved a palladium domain confined within the manganese carbonate lattice and doped with iron. This synergistic effect between highly dispersed palladium and iron greatly amplifies the concentration of surface hydroxyl groups and oxygen on the catalyst, thereby enabling complete oxidation of formaldehyde at ambient conditions. The proposed method facilitates the formation of domain-limited palladium within the MnCO3 lattice, thereby enhancing the dispersion of palladium and facilitating its partial incorporation into the MnCO3 lattice. Consequently, this approach promotes increased exposure of active sites and enhances the catalyst's capacity for oxygen activation. The co-doping of iron effectively splits the doping sites of palladium to further enhance its dispersion, while simultaneously modifying the electronic modification of the catalyst to alter formaldehyde's adsorption strength on it. Manganese carbonate exhibits superior adsorption capability for activated surface hydroxyl groups due to the presence of carbonate. In situ infrared testing revealed that dioxymethylene and formate are primary products resulting from catalytic oxidation of formaldehyde, with catalyst surface oxygen and hydroxyl groups playing a crucial role in intermediate product decomposition and oxidation. This study provides novel insights for designing palladium-based catalysts.

Adsorptivity and kinetics for low concentration of gaseous formaldehyde on bamboo-based activated carbon loaded with ammonium acetate particles

The highly promising formaldehyde (HCHO)-removing materials are essential for eliminating interior pollution to safeguard the public's health with increasing indoor HCHO contamination situations being recorded on a global scale. In the paper, bamboo charcoal (BC) was activated with boric acid to prepare bamboo-based activated carbon (BAC), and then impregnated with ammonium acetate solution to successfully develop porous adsorbent with ammonium acetate particles (N/BAC), which was applied to remove low concentration of HCHO at room temperature. The adsorption performance for HCHO was systematically investigated while the surface chemical properties and microstructure of the as-prepared adsorbents were described and analyzed. The specific surface area, total pore volume and microporous volume of N/BAC sample were 240.09 m²/g, 0.27 cm³/g and 0.12 cm³/g, which increased by 42.40 m²/g, 0.15 cm³/g and 0.03 cm³/g compared with BAC sample, respectively. The specific surface area and the microporous volume, as well as the content of oxygen- and nitrogen-containing functional groups of N/BAC sample were augmented by contrast with other samples, and numerous ammonium acetate particles were present on the surface. Precisely because of this, the N/BAC sample exhibited a high removal rate of 98.89%, which was 18.38% greater than that of BAC sample. A superior correlation coefficient (0.9999) from the experimental values of the kinetics and the fitted values of the pseudo-second-order kinetic model demonstrated that the adsorption process of HCHO on N/BAC sample was physical-chemical combined adsorption. The adsorption of HCHO on N/BAC sample was investigated under different humidity, and the results showed that the adsorbent yet had excellent adsorption capacity (87.93%) under RH 75%. Moreover, the N/BAC sample was renewable, and the removal rate still reached 82.81% after five cycles of regeneration. Therefore, the as-prepared adsorbent is an effective, economical and sustainable material, and could be used to remove HCHO from real contaminated indoor air.