Different effect of Y (Y = Cu, Mn, Fe, Ni) doping on Co3O4 derived from Co-MOF for toluene catalytic destruction

MOF-Derived ZrO2-Supported Bimetallic Pd-Ni Catalyst for Selective Hydrogenation of 1,3-Butadiene

A series of MOF-derived ZrO2-supported Pd-Ni bimetallic catalysts (PdNi/UiO-67-CTAB(n)-A500) were prepared by co-impregnation and pyrolysis at 500 °C under air atmosphere using UiO-67-CTAB(n) (CTAB: cetyltrimethylammonium bromide; n: the concentration of CTAB; n = 0, 3, 8, 13, 18) as a sacrificial template. The catalytic activity of PdNi/UiO-66-CTAB(n)-A500 in 1,3-butadiene hydrogenation was found to be dependent on the crystal morphology of the UiO-67 template. The highest activity was observed over the PdNi/UiO-67-CTAB(3)-A500 catalyst which was synthesized using UiO-67-CTAB(3) with uniform octahedral morphology as the template for the 1,3-butadiene selective hydrogenation. The 1,3-butadiene conversion and total butene selectivity were 98.4% and 44.8% at 40 °C within 1 h for the PdNi/UiO-67-CTAB(3)-A500 catalyst, respectively. The catalyst of PdNi/UiO-67-CTAB(3)-A500 can be regenerated in flowing N2 at 200 °C. Carbon deposited on the surface of the catalyst was the main reason for its deactivation. This work is valuable for the high-efficiency bimetallic catalyst's development on the selective hydrogenation of 1,3-butadiene.

Synergistic oxidation of toluene through bimetal/cordierite monolithic catalysts with ozone

Toluene treatment has received extensive attention, and ozone synergistic catalytic oxidation was thought to be a potential method to degrade VOCs (violate organic compounds) due to its low reaction temperature and high catalytic efficiency. A series of bimetal/Cord monolithic catalysts were prepared by impregnation with cordierite, including MnxCu5-x/Cord, MnxCo5-x/Cord and CuxCo5-x/Cord (x = 1, 2, 3, 4). Analysis of textural properties, structures and morphology characteristics on the prepared catalysts were conducted to evaluate their performance on toluene conversion. Effects of active component ratio, ozone addition and space velocity on the catalytic oxidation of toluene were investigated. Results showed that MnxCo5-x/Cord was the best among the three bimetal catalysts, and toluene conversion and mineralization rates reached 100 and 96% under the condition of Mn2Co3/Cord with 3.0 g/m3 O3 at the space velocity of 12,000 h-1. Ozone addition in the catalytic oxidation of toluene by MnxCo5-x/Cord could efficiently avoid the 40% reduction of the specific surface area of catalysts, because it could lower the optimal temperature from 300 to 100 °C. (Co/Mn)(Co/Mn)2O4 diffraction peaks in XRD spectra indicated all the four MnxCo1-x/Cord catalysts had a spinel structure, and diffraction peak intensity of spinel reached the largest at the ratio of Mn:Co = 2:3. Toluene conversion rate increased with rising ozone concentration because intermediate products generated by toluene degradation might react with excess ozone to generate free radicals like ·OH, which would improve the toluene mineralization rate of Mn2Co3/Cord catalyst. This study would provide a theoretical support for its industrial application.

Recent advances of metal-organic framework-based and derivative materials in the heterogeneous catalytic removal of volatile organic compounds

Since the environmental hazards of volatile organic compounds (VOCs) are well known, heterogeneous catalysis has become one of the most popular methods to treat VOCs due to its environmental friendliness and simplicity of operation. Although a large number of reports have reviewed the application of catalytic oxidation for the degradation of VOCs, relatively few reports are based on this direction of metal organic frameworks (MOFs) and MOF derivatives. Herein, this paper reviews the recent applications of heterogeneous catalytic technologies in the degradation of VOCs, including photocatalysis, thermal catalysis and other catalytic approaches. The applications of MOFs and their derivatives in VOCs degradation, such as the progress of MOF-derived metal oxides in the treatment of toluene, were highlighted. The mechanisms of VOCs degradation by different catalytic approaches were systematically presented. Finally, we presented the views and directions of VOCs treatment technology development. We hope that this reaction type-oriented review will provide important insights into MOFs and MOF-derived materials for VOCs pollution control.