Enhancement of leaching copper by organic agents from waste printed circuit boards in a sulfuric acid solution

A clean and efficient route for extraction of vanadium from vanadium slag by electro-oxidation combined with ultrasound cavitation

Extracting vanadium (V) from vanadium slag (VS) by the traditional roasting-leaching process has disadvantages of high energy consumption and high poisonous gases emission. In this work, a green and efficient route was developed to extract V from VS without roasting by electro-oxidation combined with ultrasound cavitation (EOUC) intensification in sulfuric acid solution. The leaching parameters (e.g., leaching temperature, sulfuric acid concentration, anodic current density, ultrasound power, liquid to solid ratio, leaching time and particle size) were optimized. The leaching mechanism was explored by comparing the leaching behavior and mineralogical evolution of the direct sulfuric acidic leaching (DSL), electro-oxidation-assisted sulfuric acidic leaching (EOSL), ultrasound cavitation-assisted sulfuric acidic leaching (UCSL) and EOUC methods. The results show that introducing electric field strengthens the ultrasound cavitation effect on slag particles in sulfuric acid solution. Under the optimum parameter of EOUC method, the leaching rate of V from VS is as high as 94.64 %. Using EOUC method can open the silicate-wrapped structure of the spinel, increase pore volume of VS from 0.00127 cm3 g-1 to 0.01124 cm3 g-1, decrease slag particle size from 26.8 μm to 16.4 μm and improve specific surface area from 0.508 m2 g-1 to 10.855 m2 g-1, which significantly accelerate V leaching process. The exposed spinel was oxidized by both electrochemical route and chemical route, forming a mixture of V3+ ion and VO2+ ion after leaching.

Review on the gentle hydrometallurgical treatment of WPCBs: Sustainable and selective gradient process for multiple valuable metals recovery

The metal resource crisis and the inherent need for a low-carbon circular economy have driven the rapid development of e-waste recycling technology. High-value waste printed circuit boards (WPCBs) are an essential component of e-waste. However, WPCBs are considered hazardous to the ecosystem due to the presence of heavy metals and brominated organic polymers. Therefore, achieving the recycling of metals in WPCBs is not only a strategic requirement for building a green ecological civilization but also an essential guarantee for achieving a safe supply of mineral resources. This review systematically analyzes the hydrometallurgical technology of metals in WPCBs in recent years. Firstly, the different unit operations of pretreatment in the hydrometallurgical process, which contain disassembly, crushing, and pre-enrichment, were analyzed. Secondly, environmentally friendly hydrometallurgical leaching systems and high-value product regeneration technologies used in recent years to recover metals from WPCBs were evaluated. The leaching techniques, including cyanidation, halide, thiourea, and thiosulfate for precious metals, and inorganic acid, organic acid, and other leaching methods for base metals such as copper and nickel in WPCBs, were outlined, and the leaching performance and greenness of each leaching system were summarized and analyzed. Eventually, based on the advantages of each leaching system and the differences in chemical properties of metals in WPCBs, an integrated and multi-gradient green process for the recovery of WPCBs was proposed, which provides a sustainable pathway for the recovery of metals in WPCBs. This paper provides a reference for realizing the gradient hydrometallurgical recovery of metals from WPCBs to promote the recycling metal resources.