Structure of a novel Co-based heterogeneous catalyst via Mn3(PO4)2 as a carrier to efficiently activate peroxymonosulfate for improving degradation of sulfonamides

Peroxymonosulfate activation by CuMn-LDH for the degradation of bisphenol A: Effect, mechanism, and pathway

The remediation of water contaminated with bisphenol A (BPA) has gained significant attention. In this study, a hydrothermal composite activator of Cu3Mn-LDH containing coexisting phases of cupric nitrate (Cu(NO3)2) and manganous nitrate (Mn(NO3)2) was synthesized. Advanced oxidation processes were employed as an effective approach for BPA degradation, utilizing Cu3Mn-LDH as the catalyst to activate peroxymonosulfate (PMS). The synthesis of the Cu3Mn-LDH material was characterized using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and transmission electron microscopy (TEM). According to the characterization data and screening experiments, Cu3Mn-LDH was selected as the best experimental material. Cu3Mn-LDH exhibits remarkable catalytic ability with PMS, demonstrating good degradation efficiency of BPA under neutral and alkaline conditions. With a PMS dosage of 0.25 g·L-1 and Cu3Mn-LDH dosage of 0.10 g·L-1, 10 mg·L-1 BPA (approximately 17.5 μM) can be completely degraded within 40 min, of which the TOC removal reached 95%. The reactive oxygen species present in the reaction system were analyzed by quenching experiments and EPR. Results showed that sulfate free radicals (SO4•-), hydroxyl free radicals (•OH), superoxide free radicals (•O2-), and nonfree radical mono-oxygen were generated, while mono-oxygen played a key role in degrading BPA. Cu3Mn-LDH exhibits excellent reproducibility, as it can still completely degrade BPA even after four consecutive cycles. The degradation intermediates of BPA were detected by GCMS, and the possible degradation pathways were reasonably predicted. This experiment proposes a nonradical degradation mechanism for BPA and analyzes the degradation pathways. It provides a new perspective for the treatment of organic pollutants in water.

Starch of oat derived nanostructured Fe/Mn bimetallic carbon materials for sulfamethoxazole degradation via peroxymonosulfate activation

Fe/Mn bimetallic carbon materials were synthesized by combining oat and urea, followed by and carbonization processes, the activity and mechanism of the obtained materials in activating peroxymonosulfate (PMS) for sulfamethoxazole (SMX) degradation were determined. Data suggested that the obtained material (CN@FeMn-10-800) showed the optimal performance for SMX degradation under the1:8:0.05:0.05 mass ratios of oat/urea/Fe/Mn. Around 91.2 % SMX (10 mg L-1) was removed under the conditions of 0.15 g L-1 CN@FeMn-10-800 and 0.20 g L-1 PMS. The CN@FeMn-10-800 showed great adaptability under different conditions, satisfactory activation repeatability and versatility. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) demonstrated that core-shell structure with rich porous of CN@FeMn-10-800 was achieved. Quenching test and electron paramagnetic resonance (EPR) indicated that surface bound oxygen and singlet oxygen (1O2) were the dominate reactive groups in this system. X-ray photoelectron spectroscopy (XPS) suggested that graphite N, Fe0, Fe3C and Mn(II) were the dominant active sites. Through the work, a simple strategy could be found to make high-value use of biomass and use it to effectively purified wastewater.