Electrokinetic preconcentration of magnetite core – carboxylic shell nanoparticles by capillary electrophoresis

Electroosmotic flow modulation for improved electrokinetic preconcentration: Application to capillary electrophoresis of fluorescent magnetic nanoparticles

It is reported in this study a new approach for modulation and even suppression of the electroosmotic flow (EOF) to achieve better electrokinetic preconcentration in capillary electrophoresis. This is based on the augmentation of the buffer's concentrations to very high levels (more than a thousand of mM) without recourse to any dynamic/permanent coating nor viscous gel. The use of large weakly charged molecules as background electrolyte's constituents allows working at extreme concentration ranges without penalty of high electric currents and Joule heating. By this way, the electroosmotic mobility could be modulated over a wide range (2-60 × 10^-5 cm² V^-1 s^-1 under alkaline conditions), and suppressed to levels equivalent to those obtained with several neutral coatings. The highest buffer concentrations, and the lowest EOF magnitudes, accordingly, were achieved with diethanolamine/3-(Cyclohexylamino)-1-propanesulfonic acid (ionic strength (IS) of 250 mM, pH 9.5), Tris(hydroxymethyl)aminomethane (Tris)/2-(Cyclohexylamino)ethanesulfonic acid (CHES) (IS of 280 mM, pH 8.7) and triethanolamine/2-(Cyclohexylamino)ethanesulfonic acid (IS of 250 mM, pH 8.5). For demonstration, this new approach was applied for sensitive determination of core-shell magnetic nanoparticles (CSMNPs) having high potential for healthcare applications such as imaging agents for diagnostics and controllable cargos for nanomedicine. Different profiles were achieved for purpose-made and commercial magnetic nanoparticles using CE coupled with light-emitting-diode induced fluorescence (LEDIF) detection. The best performance for EOF-assisted preconcentration and CE-LEDIF of CSMNPs was achieved with these nanoparticles prepared in TRIS/CHES (IS 10 mM, pH 8.4) for preconcentration, and separation under BGE of TRIS/CHES (IS 100 mM, pH 8.4). Compared to the conventional capillary electrophoresis (CE-UV) method for characterization of magnetic nanoparticles, our proposed approach with fluorescent detection and EOF-assisted preconcentration offers almost 350-fold sensitivity improvement. Furthermore, our scheme can be used for monitoring the interaction between CSMNPs and target pharmaceutical molecules, serving for drug delivery development. A preliminary study with two antibiotics using this approach revealed that kanamycin interacts better with the target nanoparticles than amikacin.

The on-line preconcentration of nanoparticles in electromigration techniques

Electromigration techniques have recently emerged as an alternative analytical tool for nanoparticles characterization. Due to the high throughput capability and separation efficiency their application for detection/quantification of nanomaterials in samples of various origin has attracted much attention. While the electromigration techniques are known to suffer from insufficient detection sensitivity, a number of papers investigating on-line preconcentration of nanoparticles in capillary electrophoresis was addressed to the issue. In this work the available literature on nanoparticles stacking in electrodriven separation techniques was reviewed. The discussion was supported by theoretical background. A special emphasis was put on the stability of nanoparticles dispersion during electrophoretic process. The considerations on future perspectives were included in final remarks.

Inline Coupling of Electrokinetic Preconcentration Method to Taylor Dispersion Analysis for Size-Based Characterization of Low-UV-Absorbing Nanoparticles

The inline coupling of the field-amplified sample injection (FASI) to Taylor dispersion analysis (TDA) was used to characterize low-UV absorbing carboxylated silica nanoparticles (cNPs). The hydrodynamic diameters (D_h) were measured by using a commercial capillary electrophoresis instrument. The proposed methodology did not require any complicated instruments or chromophoric dye to increase the detection sensitivity. A practical method based on a half-Gaussian fitting was proposed for the data processing. The results obtained by this method were compared with those derived from dynamic light scattering (DLS) and transmission electron microscopy (TEM) analyses. From these results, it appeared that the size derived by TDA is in excellent agreement with those measured by DLS and TEM, as demonstrated by stable nanoparticles with narrow size distributions. Intermediate precision relative standard deviations less than 5% were obtained by FASI-TDA. The effect of the FASI-induced cNP peak dispersion on the reliability of the results was discussed in detail.