Impact of stem taper damage on the fracture strength of ceramic heads with adapter sleeves

Computer-based analysis of the taper connection strength of different revision head and adapter sleeve designs

OBJECTIVES

Ceramic revision heads, equipped with titanium adapter sleeves, are used in femoral head revision in total hip arthroplasty to avoid ceramic fracture due to the damaged taper.

METHODS

A finite element analysis of the taper connection strength of revision heads with varying head diameters combined with adapter sleeves of different lengths was conducted. The influence of various assembly forces, head diameter, and length of the adapter sleeves was evaluated. For two combinations, the pattern of contact pressure was evaluated when applying a simplified joint load (3 kN, 45° load angle). Experimental validation was conducted with 36 mm heads and adapter sleeves in size S, as well as 28 mm heads and adapter sleeves in size XL.

RESULTS

The pull-off force increased with higher assembly forces. Using larger head diameters and adapter sleeves led to decreased pull-off forces, a reduced contact surface, and less contact pressure. The contact pressure showed significant peaks and a diagonal pattern under 45° angle loading when assembly forces were less than 4 kN, and larger adapter sleeves were utilized.

CONCLUSION

A sufficient assembly force should be ensured intraoperatively, especially with an increasing head diameter and adapter sleeve size, as lower assembly forces might lead to reduced taper connection strength.

Catastrophic intraoperative failure of a ceramic femoral head

Approximately 17 years after a primary metal-on-metal total hip arthroplasty, a 59-year-old female developed pain, swelling, and weakness in her right hip accompanied by laboratory findings and imaging suggestive of an adverse local tissue reaction. Acetabular revision was performed to upsize the femoral head and improve hip stability. Upon impaction of the new, non-option ceramic femoral head onto the unsleeved retained stem, the head split into two pieces without fragmentation. The surgery was completed using a cobalt-chromium head, which was impacted without issue onto the stem’s taper. Although BIOLOX delta femoral heads do not require titanium sleeves, we believe that careful consideration should be given to their use in revision total hip arthroplasty with ceramic heads, regardless of the extent of trunnion damage noted intraoperatively.

Influence of Different Damage Patterns of the Stem Taper on Fixation and Fracture Strength of Ceramic Ball Heads for Total Hip Replacement

Background

Modularity finds frequent application in total hip replacement, allowing a preferable individual configuration and a simplified revision by retaining the femoral stem and replacing the prosthetic head. However, micromotions within the interface between the head and the stem taper can arise, resulting in the release of wear debris and corrosion products. The aim of our experimental study was to evaluate the influence of different taper damages on the fixation and fracture stability of ceramic femoral heads, after static and dynamic implant loading.

Methods

Ceramic ball heads (36 mm diameter) and 12/14 stem tapers made of titanium with various mild damage patterns (intact, scratched, and truncated) were tested. The heads were assembled on the taper with a quasistatic load of 2 kN and separated into a static and a dynamic group afterwards. The dynamic group (n = 18) was loaded over 1.5 million gait cycles in a hip wear simulator (ISO 14242-1). In contrast, the static group (n = 18) was not mechanically loaded after assembly. To determine the taper stability, all heads of the dynamic and static groups were either pulled off (ASTM 2009) or turned off (ISO 7206-16). A head fracture test (ISO 7206-10) was also performed. Subsequent to the fixation stability tests, the taper surface was visually evaluated in terms of any signs of wear or corrosion after the dynamic loading.

Results

In 10 of the 18 cases, discoloration of the taper was determined after the dynamic loading and subsequent cleaning, indicating the first signs of corrosion. Pull-off forces as well as turn-off moments were increased between 23% and 54% after the dynamic loading compared to the unloaded tapers. No significant influence of taper damage was determined in terms of taper fixation strength. However, the taper damage led to a decrease in fracture strength by approximately 20% (scratched) and 40% (truncated), respectively.

Conclusion

The results suggest that careful handling and accurate manufacturing of the stem taper are crucial for the ceramic head fracture strength, even though a mild damage showed no significant influence on taper stability. Moreover, our data indicate that a further seating of the prosthetic head may occur during daily activities, when the resulting hip force increases the assembly load.

Adapter sleeves are essential for ceramic heads in hip revision surgery

BACKGROUND

Removing a head during isolated acetabular revision surgery can cause damage to the stem taper surface from extraction tool contact. Implanting a ceramic head on the damaged stem taper might elevate the fracture risk, which can be mitigated with the use of titanium adapter sleeves. The aim of this study was to investigate whether the improved fracture strength of modern generation ceramic heads allows the direct implantation on damaged stem tapers without an adapter sleeve.

METHODS

Finite element models of taper junctions with and without adapter sleeve were generated. Different stem taper damages were modelled to investigate the influence on the ceramic head fracture load under axial compression.

FINDINGS

Heads without adapter sleeves exhibited slightly higher or equal fracture strengths compared with sleeved heads for most scenarios. However, a small metal elevation on the stem taper caused a drastic decrease of the fracture strength if no adapter sleeve was used (-96%). The sleeved head was not influenced by the metal elevation damage.

INTERPRETATION

Adapter sleeves are essential to ensure patient safety and prosthesis longevity whenever implanting ceramic heads on used stem tapers.